Industrial Laminates/Norplex NP611 Paper Base Laminate

Category Polymer , Thermoset , Phenolic
Manufacturer Industrial Laminates/Norplex
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Industrial Laminates/Norplex NP611 Paper Base Laminate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Hot punching general-purpose phenolic grade. Mechanical properties approach those of NP610 with improved electrical properties and moisture resistance.Thickness Tested: 0.062", 0 125" and 0.500".
Physical Properties Metric English Comments
Specific Gravity 1.32 - 1.38 g/cc

@Thickness 1.57 mm
 1.32 - 1.38 g/cc

@Thickness 0.0620 in
 ASTM D792
Moisture Absorption at Equilibrium 2.2 %

@Thickness 1.57 mm
 2.2 %

@Thickness 0.0620 in
 ASTM D229
Mechanical Properties Metric English Comments
Hardness, Rockwell M 90 - 110

@Thickness 1.57 mm
 90 - 110

@Thickness 0.0620 in
 ASTM D785
Tensile Strength, Yield 93.1 MPa

@Thickness 1.57 mm
 13500 psi

@Thickness 0.0620 in
 CW; ASTM D638
124 MPa

@Thickness 1.57 mm
 18000 psi

@Thickness 0.0620 in
 LW; ASTM D638
Modulus of Elasticity 6.21 GPa

@Thickness 1.57 mm
 900 ksi

@Thickness 0.0620 in
 CW; ASTM D229
8.27 GPa

@Thickness 1.57 mm
 1200 ksi

@Thickness 0.0620 in
 LW; ASTM D229
Flexural Strength 152 MPa

@Thickness 1.57 mm
 22000 psi

@Thickness 0.0620 in
 CW; ASTM D790
200 MPa

@Thickness 1.57 mm
 29000 psi

@Thickness 0.0620 in
 LW; ASTM D790
Compressive Strength 310 MPa

@Thickness 12.7 mm
 45000 psi

@Thickness 0.500 in
 ASTM D695
Shear Strength 84.1 MPa

@Thickness 15.7 mm
 12200 psi

@Thickness 0.620 in
 ASTM D732
Izod Impact, Unnotched 0.320 J/cm

@Thickness 12.7 mm
 0.600 ft-lb/in

@Thickness 0.500 in
 CW, Cond E-48/50; ASTM D256
0.374 J/cm

@Thickness 12.7 mm
 0.700 ft-lb/in

@Thickness 0.500 in
 LW, Cond E-48/50; ASTM D256
Thermal Properties Metric English Comments
CTE, linear 13.0 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
 7.22 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
 x-axis; IPC-TM 650-2.4.24
CTE, linear, Transverse to Flow 17.0 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
 9.44 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
 x-axis; IPC-TM 650-2.4.24
Maximum Service Temperature, Air 130 °C
266 °F
Flammability, UL94 HB

@Thickness 1.57 mm
 HB

@Thickness 0.0620 in
Electrical Properties Metric English Comments
Dielectric Strength 23.6 kV/mm

@Thickness 1.57 mm
 600 kV/in

@Thickness 0.0620 in
 Cond A; ASTM D229 S.T.
Dielectric Breakdown 50000 V

@Thickness 1.57 mm
 50000 V

@Thickness 0.0620 in
 Cond A; ASTM D229 S/S
Arc Resistance 75 sec

@Thickness 3.17 mm
 75 sec

@Thickness 0.125 in
 ASTM D495
Comparative Tracking Index 180 V

@Thickness 3.17 mm
 180 V

@Thickness 0.125 in
 ASTM D3638
Descriptive Properties Value Comments
Bond Strength 1100 lb
0.5", ASTM D229
Color Natural, Black, Chocolate