Industrial Laminates/Norplex NP600 Paper Base Laminate

Category	Polymer , Thermoset , Phenolic
Manufacturer	Industrial Laminates/Norplex
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Industrial Laminates/Norplex NP600 Paper Base Laminate.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: A paper-base laminate with low phenolic resin content for hard, flat surfaces. This material is most commonly used for drill entry material in the PCB industry. Thickness Tested: 0.062", 0.125"and 0.500"

Physical Properties	Metric	English	Comments
Specific Gravity	1.30 - 1.35 g/cc @Thickness 1.57 mm	1.30 - 1.35 g/cc @Thickness 0.0620 in	ASTM D792
Moisture Absorption at Equilibrium	8.0 % @Thickness 1.57 mm	8.0 % @Thickness 0.0620 in	ASTM D229

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell M	80 - 100 @Thickness 1.57 mm	80 - 100 @Thickness 0.0620 in	ASTM D785
Tensile Strength, Yield	89.6 MPa @Thickness 1.57 mm	13000 psi @Thickness 0.0620 in	CW; ASTM D638
	117 MPa @Thickness 1.57 mm	17000 psi @Thickness 0.0620 in	LW; ASTM D638
Flexural Strength	152 MPa @Thickness 1.57 mm	22000 psi @Thickness 0.0620 in	CW; ASTM D790
	172 MPa @Thickness 1.57 mm	25000 psi @Thickness 0.0620 in	LW; ASTM D790
Compressive Strength	241 MPa @Thickness 12.7 mm	35000 psi @Thickness 0.500 in	ASTM D695
Izod Impact, Unnotched	0.267 J/cm @Thickness 12.7 mm	0.500 ft-lb/in @Thickness 0.500 in	CW, Cond E-48/50; ASTM D256
	0.294 J/cm @Thickness 12.7 mm	0.550 ft-lb/in @Thickness 0.500 in	LW, Cond E-48/50; ASTM D256

Thermal Properties	Metric	English	Comments
Flammability, UL94	HB @Thickness 1.57 mm	HB @Thickness 0.0620 in

Electrical Properties	Metric	English	Comments
Dielectric Breakdown	3000 V @Thickness 1.57 mm	3000 V @Thickness 0.0620 in	Cond D-48/50; ASTM D229 S/S
	60000 V @Thickness 1.57 mm	60000 V @Thickness 0.0620 in	Cond A; ASTM D229 S/S

Descriptive Properties	Value	Comments
Color	Natural