Industrial Laminates/Norplex NP660 Paper Base Laminate

Category Polymer , Thermoset , Phenolic
Manufacturer Industrial Laminates/Norplex
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Industrial Laminates/Norplex NP660 Paper Base Laminate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Lower cost paper phenolic NEMA Grade XP. Uses natural kraft paper without pigmented cover sheet. Warm to hot punching. UL listed. Thickness Tested: 0.062", 0.125" & 0.500"
Physical Properties Metric English Comments
Specific Gravity 1.30 - 1.40 g/cc

@Thickness 1.57 mm
 1.30 - 1.40 g/cc

@Thickness 0.0620 in
 ASTM D792
Moisture Absorption at Equilibrium 3.5 %

@Thickness 1.57 mm
 3.5 %

@Thickness 0.0620 in
 ASTM D229
Mechanical Properties Metric English Comments
Hardness, Rockwell M 90 - 110

@Thickness 1.57 mm
 90 - 110

@Thickness 0.0620 in
 ASTM D785
Tensile Strength, Yield 110 MPa

@Thickness 1.57 mm
 16000 psi

@Thickness 0.0620 in
 CW; ASTM D638
138 MPa

@Thickness 1.57 mm
 20000 psi

@Thickness 0.0620 in
 LW; ASTM D638
Modulus of Elasticity 9.65 GPa

@Thickness 1.57 mm
 1400 ksi

@Thickness 0.0620 in
 CW; ASTM D229
13.1 GPa

@Thickness 1.57 mm
 1900 ksi

@Thickness 0.0620 in
 LW; ASTM D229
Flexural Strength 152 MPa

@Thickness 1.57 mm
 22000 psi

@Thickness 0.0620 in
 CW; ASTM D790
200 MPa

@Thickness 1.57 mm
 29000 psi

@Thickness 0.0620 in
 LW; ASTM D790
Compressive Strength 338 MPa

@Thickness 12.7 mm
 49000 psi

@Thickness 0.500 in
 ASTM D695
Shear Strength 96.5 MPa

@Thickness 15.7 mm
 14000 psi

@Thickness 0.620 in
 ASTM D732
Izod Impact, Unnotched 0.374 J/cm

@Thickness 12.7 mm
 0.700 ft-lb/in

@Thickness 0.500 in
 CW, Cond E-48/50; ASTM D256
0.400 J/cm

@Thickness 12.7 mm
 0.750 ft-lb/in

@Thickness 0.500 in
 LW, Cond E-48/50; ASTM D256
Thermal Properties Metric English Comments
CTE, linear 17.0 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
 9.44 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
 x-axis; IPC-TM 650-2.4.24
CTE, linear, Transverse to Flow 13.0 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
 7.22 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
 x-axis; IPC-TM 650-2.4.24
Maximum Service Temperature, Air 130 °C
266 °F
Flammability, UL94 HB

@Thickness 1.57 mm
 HB

@Thickness 0.0620 in
Electrical Properties Metric English Comments
Dielectric Constant 5.45

@Thickness 1.57 mm
 5.45

@Thickness 0.0620 in
 Permittivity, Cond D-24/23; ASTM D150
Dielectric Strength 11.8 kV/mm

@Thickness 1.57 mm
 300 kV/in

@Thickness 0.0620 in
 Cond D-48/50; ASTM D229 S.T.
19.7 kV/mm

@Thickness 1.57 mm
 500 kV/in

@Thickness 0.0620 in
 Cond A; ASTM D229 S.T.
Dielectric Breakdown 10000 V

@Thickness 1.57 mm
 10000 V

@Thickness 0.0620 in
 Cond D-48/50; ASTM D229 S/S
47000 V

@Thickness 1.57 mm
 47000 V

@Thickness 0.0620 in
 Cond A; ASTM D229 S/S
Dissipation Factor 0.45

@Thickness 1.57 mm
 0.45

@Thickness 0.0620 in
 Cond D-24/23; ASTM D150
Arc Resistance 60 sec

@Thickness 3.17 mm
 60 sec

@Thickness 0.125 in
 ASTM D495
Comparative Tracking Index 150 V

@Thickness 3.17 mm
 150 V

@Thickness 0.125 in
 ASTM D3638
Descriptive Properties Value Comments
Bond Strength 1100 lb
0.5", ASTM D229
Color Natural, Black