Toyobo GLAMIDE® T-808-02 Nylon-6

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced, Flame Retardant
Manufacturer Toyobo
Trade Name GLAMIDE®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Toyobo GLAMIDE® T-808-02 Nylon-6.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing and a specific grade approved as UL94V-0 class is provided, and it exhibits excellent chemical resistance and oil resistance. Grade T-808-02 is a flame resistant, aromatic Nylon-6. It is non-bleeding and of non-halogen origin.
Physical Properties Metric English Comments
Specific Gravity 1.18 g/cc
1.18 g/cc
Absolute Drying; ASTM-D792
Water Absorption 1.3 %
1.3 %
Absolute Drying; ASTM-D570
Moisture Absorption at Equilibrium 3.0 %
3.0 %
Absolute Drying; ASTM-D570
Linear Mold Shrinkage 0.0040 - 0.0080 cm/cm

@Thickness 1.00 mm
 0.0040 - 0.0080 in/in

@Thickness 0.0394 in
 Absolute Drying
0.010 - 0.013 cm/cm

@Thickness 3.00 mm
 0.010 - 0.013 in/in

@Thickness 0.118 in
 Absolute Drying
Melt Flow 40 g/10 min
40 g/10 min
Mechanical Properties Metric English Comments
Hardness, Rockwell R 120
120
Absolute Drying; ASTM-D785
Tensile Strength, Ultimate 20.0 MPa

@Temperature 80.0 °C
 2900 psi

@Temperature 176 °F
 Practical Use (Water Absorption 3.0%); ASTM-D638
32.0 MPa

@Temperature 80.0 °C
 4640 psi

@Temperature 176 °F
 Absolute Drying; ASTM-D638
40.0 MPa

@Temperature 23.0 °C
 5800 psi

@Temperature 73.4 °F
 Practical Use (Water Absorption 3.0%); ASTM-D638
75.0 MPa

@Temperature 23.0 °C
 10900 psi

@Temperature 73.4 °F
 Absolute Drying; ASTM-D638
90.0 MPa

@Temperature -40.0 °C
 13100 psi

@Temperature -40.0 °F
 Practical Use (Water Absorption 3.0%); ASTM-D638
100 MPa

@Temperature -40.0 °C
 14500 psi

@Temperature -40.0 °F
 Absolute Drying; ASTM-D638
Elongation at Break 6.0 %
6.0 %
Absolute Drying; ASTM-D638
15 %
15 %
Practical Use (Water Absorption 3.0%); ASTM-D638
Flexural Strength 26.0 MPa

@Temperature 80.0 °C
 3770 psi

@Temperature 176 °F
 Practical Use (Water Absorption 3.0%); ASTM-D790
42.0 MPa

@Temperature 80.0 °C
 6090 psi

@Temperature 176 °F
 Absolute Drying; ASTM-D790
45.0 MPa

@Temperature 23.0 °C
 6530 psi

@Temperature 73.4 °F
 Practical Use (Water Absorption 3.0%); ASTM-D790
100 MPa

@Temperature 23.0 °C
 14500 psi

@Temperature 73.4 °F
 Absolute Drying; ASTM-D790
120 MPa

@Temperature -40.0 °C
 17400 psi

@Temperature -40.0 °F
 Practical Use (Water Absorption 3.0%); ASTM-D790
145 MPa

@Temperature -40.0 °C
 21000 psi

@Temperature -40.0 °F
 Absolute Drying; ASTM-D790
Flexural Modulus 0.500 GPa

@Temperature 80.0 °C
 72.5 ksi

@Temperature 176 °F
 Practical Use (Water Absorption 3.0%); ASTM-D790
1.00 GPa

@Temperature 80.0 °C
 145 ksi

@Temperature 176 °F
 Absolute Drying; ASTM-D790
1.30 GPa

@Temperature 23.0 °C
 189 ksi

@Temperature 73.4 °F
 Practical Use (Water Absorption 3.0%); ASTM-D790
3.30 GPa

@Temperature 23.0 °C
 479 ksi

@Temperature 73.4 °F
 Absolute Drying; ASTM-D790
5.10 GPa

@Temperature -40.0 °C
 740 ksi

@Temperature -40.0 °F
 Practical Use (Water Absorption 3.0%); ASTM-D790
5.50 GPa

@Temperature -40.0 °C
 798 ksi

@Temperature -40.0 °F
 Absolute Drying; ASTM-D790
Compressive Strength 80.0 MPa
11600 psi
Absolute Drying; ASTM-D695
Izod Impact, Notched 0.300 J/cm

@Temperature -40.0 °C
 0.562 ft-lb/in

@Temperature -40.0 °F
 Absolute Drying; ASTM-D256
0.430 J/cm

@Temperature 23.0 °C
 0.806 ft-lb/in

@Temperature 73.4 °F
 Absolute Drying; ASTM-D256
0.450 J/cm

@Temperature -40.0 °C
 0.843 ft-lb/in

@Temperature -40.0 °F
 Practical Use (Water Absorption 3.0%); ASTM-D256
1.75 J/cm

@Temperature 23.0 °C
 3.28 ft-lb/in

@Temperature 73.4 °F
 Practical Use (Water Absorption 3.0%); ASTM-D256
Thermal Properties Metric English Comments
CTE, linear 70.0 µm/m-°C
38.9 µin/in-°F
Absolute Drying; ASTM-D696
Deflection Temperature at 0.46 MPa (66 psi) 190 °C
374 °F
Absolute Drying; ASTM-D648
Deflection Temperature at 1.8 MPa (264 psi) 84.0 °C
183 °F
Absolute Drying; ASTM-D648
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+8 - 1.00e+9 ohm-cm
1.00e+8 - 1.00e+9 ohm-cm
Practical Use (Water Absorption 3.0%); ASTM-D257
1.00e+12 ohm-cm
1.00e+12 ohm-cm
Absolute Drying; ASTM-D257
Dielectric Constant 5.2

@Frequency 1000 Hz
 5.2

@Frequency 1000 Hz
 Absolute Drying; ASTM-D150
Dielectric Strength 17.0 kV/mm

@Thickness 2.00 mm
 432 kV/in

@Thickness 0.0787 in
 Practical Use (Water Absorption 3.0%); ASTM-D149
25.0 kV/mm

@Thickness 2.00 mm
 635 kV/in

@Thickness 0.0787 in
 Absolute Drying; ASTM-D149
Dissipation Factor 0.080

@Frequency 1000 Hz
 0.080

@Frequency 1000 Hz
 Absolute Drying; ASTM-D150
Arc Resistance 105 sec
105 sec
Practical Use (Water Absorption 3.0%); ASTM-D495
120 sec
120 sec
Absolute Drying; ASTM-D495
Comparative Tracking Index >= 600 V
>= 600 V
IEC Method
Processing Properties Metric English Comments
Melt Temperature 240 - 260 °C
464 - 500 °F
Mold Temperature 80.0 °C
176 °F
Injection Pressure 30.0 - 45.0 MPa
4350 - 6530 psi