- Victrex® ST™ ST45CA30 PolyEtherKetoneEtherKetoneKetone, 30% Carbon Fibre Reinforced
Victrex® ST™ ST45CA30 PolyEtherKetoneEtherKetoneKetone, 30% Carbon Fibre Reinforced
| Category | Polymer , Thermoplastic , Polyketone , Polyetherketoneetherketoneketone (PEKEKK), Carbon Fiber Filled |
| Manufacturer | Victrex |
| Trade Name | ST™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Victrex® ST™ ST45CA30 PolyEtherKetoneEtherKetoneKetone, 30% Carbon Fibre Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description:High performance thermoplastic material, 30% carbon fibre reinforced PolyEtherKetoneEtherKetoneKetone (PEKEKK), semi crystalline, granules for injection moulding, standard flow, colour black.Typical Application Areas:Applications for higher strength and stiffness at elevated temperatures in a static or dynamic system. Excellent wear resistance, low coefficient of friction, low coefficient of thermal expansion. Chemically resistant to aggressive environments.Information Provided by VICTREX®
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | Crystalline; ISO 1183 |
| Water Absorption at Saturation | 0.80 % @Temperature 100 °C |
0.80 % @Temperature 212 °F |
immersion; ISO 62-1 |
| Viscosity | 650000 cP @Temperature 420 °C |
650000 cP @Temperature 788 °F |
melt; ISO 11443 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | 360°C nozzle, 160°C tool; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | 415°C nozzle, 210°C tool; ISO 294-4 |
| Spiral Flow | 9.00 cm @Thickness 1.00 mm |
3.54 in @Thickness 0.0394 in |
415°C nozzle, 210°C tool |
| 41.0 cm @Thickness 3.00 mm |
16.1 in @Thickness 0.118 in |
415°C nozzle, 210°C tool |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 88 | 88 | ISO 868 |
| Tensile Strength at Break | 70.0 MPa @Temperature 275 °C |
10200 psi @Temperature 527 °F |
ISO 527 |
| 120 MPa @Temperature 175 °C |
17400 psi @Temperature 347 °F |
ISO 527 | |
| 180 MPa @Temperature 125 °C |
26100 psi @Temperature 257 °F |
ISO 527 | |
| 270 MPa @Temperature 23.0 °C |
39200 psi @Temperature 73.4 °F |
ISO 527 | |
| Elongation at Break | 1.7 % @Temperature 23.0 °C |
1.7 % @Temperature 73.4 °F |
ISO 527 |
| Tensile Modulus | 28.0 GPa @Temperature 23.0 °C |
4060 ksi @Temperature 73.4 °F |
ISO 527 |
| Flexural Strength | 100 MPa @Temperature 275 °C |
14500 psi @Temperature 527 °F |
ISO 178 |
| 190 MPa @Temperature 175 °C |
27600 psi @Temperature 347 °F |
ISO 178 | |
| 290 MPa @Temperature 125 °C |
42100 psi @Temperature 257 °F |
ISO 178 | |
| 400 MPa @Temperature 23.0 °C |
58000 psi @Temperature 73.4 °F |
ISO 178 | |
| Flexural Modulus | 23.5 GPa @Temperature 23.0 °C |
3410 ksi @Temperature 73.4 °F |
ISO 178 |
| Compressive Strength | 65.0 MPa @Temperature 250 °C |
9430 psi @Temperature 482 °F |
ISO 604 |
| 95.0 MPa @Temperature 200 °C |
13800 psi @Temperature 392 °F |
ISO 604 | |
| 210 MPa @Temperature 120 °C |
30500 psi @Temperature 248 °F |
ISO 604 | |
| 310 MPa @Temperature 23.0 °C |
45000 psi @Temperature 73.4 °F |
ISO 604 | |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A |
| Izod Impact, Unnotched (ISO) | 50.0 kJ/m² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
ISO 180/U |
| Charpy Impact Unnotched | 5.00 J/cm² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1U |
| Charpy Impact, Notched | 0.700 J/cm² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 40.0 µm/m-°C @Temperature <=162 °C |
22.2 µin/in-°F @Temperature <=324 °F |
Average below Tg; ISO 11359 |
| 95.0 µm/m-°C @Temperature >=162 °C |
52.8 µin/in-°F @Temperature >=324 °F |
Average above Tg; ISO 11359 | |
| CTE, linear, Parallel to Flow | 10.0 µm/m-°C @Temperature <=162 °C |
5.56 µin/in-°F @Temperature <=324 °F |
Below Tg; ISO 11359 |
| 13.0 µm/m-°C @Temperature >=162 °C |
7.22 µin/in-°F @Temperature >=324 °F |
Above Tg; ISO 11359 | |
| Thermal Conductivity | 0.960 W/m-K | 6.66 BTU-in/hr-ft²-°F | Average; ISO 22007-4 |
| 2.00 W/m-K | 13.9 BTU-in/hr-ft²-°F | Along flow; ISO 22007-4 | |
| Melting Point | 387 °C | 729 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 383 °C | 721 °F | ISO 75-f |
| Glass Transition Temp, Tg | 162 °C | 324 °F | Onset; ISO 11357 |
| 169 °C | 336 °F | Midpoint; ISO 11357 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1e+05 | 1e+05 | 1V; ASTM D4496 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | <= 100 °C | <= 212 °F | Hopper Temperature |
| Nozzle Temperature | 415 °C | 779 °F | |
| Mold Temperature | 200 - 230 °C | 392 - 446 °F | |
| Drying Temperature | 150 °C @Time 21600 sec |
302 °F @Time 6.00 hour |
|
| 180 °C @Time 10800 sec |
356 °F @Time 3.00 hour |