Toyobo GLAMIDE® T-401 Nylon-6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled |
| Manufacturer | Toyobo |
| Trade Name | GLAMIDE® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo GLAMIDE® T-401 Nylon-6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing and a specific grade approved as UL94V-0 class is provided, and it exhibits excellent chemical resistance and oil resistance. Grade T-401 is a GF reinforced Nylon-6. It contains 20% GF.20
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.29 g/cc | 1.29 g/cc | Absolute Drying; ASTM-D792 |
| Filler Content | 20 % | 20 % | |
| Water Absorption | 1.4 % | 1.4 % | Absolute Drying; ASTM-D570 |
| Moisture Absorption at Equilibrium | 2.8 % | 2.8 % | Absolute Drying; ASTM-D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm @Thickness 1.00 mm |
0.0020 - 0.0050 in/in @Thickness 0.0394 in |
Absolute Drying |
| 0.0050 - 0.0080 cm/cm @Thickness 3.00 mm |
0.0050 - 0.0080 in/in @Thickness 0.118 in |
Absolute Drying | |
| Melt Flow | 22 g/10 min | 22 g/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | Absolute Drying; ASTM-D785 |
| Tensile Strength, Ultimate | 38.0 MPa @Temperature 80.0 °C |
5510 psi @Temperature 176 °F |
Practical Use (Water Absorption 2.8%); ASTM-D638 |
| 53.0 MPa @Temperature 80.0 °C |
7690 psi @Temperature 176 °F |
Absolute Drying; ASTM-D638 | |
| 70.0 MPa @Temperature 23.0 °C |
10200 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 2.8%); ASTM-D638 | |
| 125 MPa @Temperature 23.0 °C |
18100 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D638 | |
| 130 MPa @Temperature -40.0 °C |
18900 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 2.8%); ASTM-D638 | |
| 150 MPa @Temperature -40.0 °C |
21800 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D638 | |
| Elongation at Break | 3.8 % | 3.8 % | Absolute Drying; ASTM-D638 |
| 6.0 % | 6.0 % | Practical Use (Water Absorption 2.8%); ASTM-D638 | |
| Flexural Strength | 58.0 MPa @Temperature 80.0 °C |
8410 psi @Temperature 176 °F |
Practical Use (Water Absorption 2.8%); ASTM-D790 |
| 100 MPa @Temperature 23.0 °C |
14500 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 2.8%); ASTM-D790 | |
| 110 MPa @Temperature 80.0 °C |
16000 psi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 115 MPa @Temperature -40.0 °C |
16700 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 2.8%); ASTM-D790 | |
| 180 MPa @Temperature 23.0 °C |
26100 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 240 MPa @Temperature -40.0 °C |
34800 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Flexural Modulus | 2.40 GPa @Temperature 80.0 °C |
348 ksi @Temperature 176 °F |
Practical Use (Water Absorption 2.8%); ASTM-D790 |
| 2.90 GPa @Temperature 80.0 °C |
421 ksi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 3.20 GPa @Temperature 23.0 °C |
464 ksi @Temperature 73.4 °F |
Practical Use (Water Absorption 2.8%); ASTM-D790 | |
| 6.30 GPa @Temperature 23.0 °C |
914 ksi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 6.60 GPa @Temperature -40.0 °C |
957 ksi @Temperature -40.0 °F |
Practical Use (Water Absorption 2.8%); ASTM-D790 | |
| 8.00 GPa @Temperature -40.0 °C |
1160 ksi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Compressive Strength | 120 MPa | 17400 psi | Absolute Drying; ASTM-D695 |
| Izod Impact, Notched | 0.450 J/cm @Temperature -40.0 °C |
0.843 ft-lb/in @Temperature -40.0 °F |
Absolute Drying; ASTM-D256 |
| 0.600 J/cm @Temperature -40.0 °C |
1.12 ft-lb/in @Temperature -40.0 °F |
Practical Use (Water Absorption 2.8%); ASTM-D256 | |
| 0.700 J/cm @Temperature 23.0 °C |
1.31 ft-lb/in @Temperature 73.4 °F |
Absolute Drying; ASTM-D256 | |
| 1.90 J/cm @Temperature 23.0 °C |
3.56 ft-lb/in @Temperature 73.4 °F |
Practical Use (Water Absorption 2.8%); ASTM-D256 | |
| Taber Abrasion, mg/1000 Cycles | 10 | 10 | CS-17, Absolute Drying; ASTM-D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 µm/m-°C | 16.7 µin/in-°F | Absolute Drying; ASTM-D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 217 °C | 423 °F | Absolute Drying; ASTM-D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | Absolute Drying; ASTM-D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+9 ohm-cm | 1.00e+9 ohm-cm | Practical Use (Water Absorption 2.8%); ASTM-D257 |
| 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | Absolute Drying; ASTM-D257 | |
| Dielectric Constant | 4.0 @Frequency 1000 Hz |
4.0 @Frequency 1000 Hz |
Absolute Drying; ASTM-D150 |
| Dielectric Strength | 17.0 kV/mm @Thickness 2.00 mm |
432 kV/in @Thickness 0.0787 in |
Practical Use (Water Absorption 2.8%); ASTM-D149 |
| 23.0 kV/mm @Thickness 2.00 mm |
584 kV/in @Thickness 0.0787 in |
Absolute Drying; ASTM-D149 | |
| Dissipation Factor | 0.010 @Frequency 1000 Hz |
0.010 @Frequency 1000 Hz |
Absolute Drying; ASTM-D150 |
| Arc Resistance | 90 sec | 90 sec | Practical Use (Water Absorption 2.8%); ASTM-D495 |
| 100 sec | 100 sec | Absolute Drying; ASTM-D495 | |
| Comparative Tracking Index | 550 V | 550 V | IEC Method |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 280 °C | 500 - 536 °F | |
| Mold Temperature | 60.0 °C | 140 °F | |
| Injection Pressure | 30.0 - 55.0 MPa | 4350 - 7980 psi |