- Lanxess Durethan® DP 2-2240/15 H2.0 901510 Nylon 66, 15% Glass Fiber
Lanxess Durethan® DP 2-2240/15 H2.0 901510 Nylon 66, 15% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® DP 2-2240/15 H2.0 901510 Nylon 66, 15% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 66, 15% glass fibers, blow molding, heat-aging stabilized, hydrolysis stabilizedInformation provided by LANXESS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.236 g/cc | 1.236 g/cc | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0012 cm/cm | 0.0012 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.015 cm/cm | 0.015 in/in | 60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4 | |
| Linear Mold Shrinkage, Transverse | 0.00 cm/cm | 0.00 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.0048 cm/cm | 0.0048 in/in | 60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 80.0 MPa | 11600 psi | cond.; ISO 527-1, -2; 5 mm/min |
| 130 MPa | 18900 psi | d.a.m.; ISO 527-1, -2; 5 mm/min | |
| Elongation at Break | 4.3 % | 4.3 % | d.a.m.; ISO 527-1, -2; 5 mm/min |
| 16 % | 16 % | cond.; ISO 527-1, -2; 5 mm/min | |
| Tensile Modulus | 3.40 GPa | 493 ksi | cond.; ISO 527-1, -2; 1 mm/min |
| 6.30 GPa | 914 ksi | d.a.m.; ISO 527-1, -2; 1 mm/min | |
| Flexural Strength | 100 MPa @Strain 7.30 % |
14500 psi @Strain 7.30 % |
cond., 2 mm/min; ISO 178-A |
| 205 MPa @Strain 6.00 % |
29700 psi @Strain 6.00 % |
d.a.m., 2 mm/min; ISO 178-A | |
| Flexural Yield Strength | 75.0 MPa @Strain 3.50 % |
10900 psi @Strain 3.50 % |
cond., 2 mm/min; ISO 178-A |
| 175 MPa @Strain 3.50 % |
25400 psi @Strain 3.50 % |
d.a.m., 2 mm/min; ISO 178-A | |
| Flexural Modulus | 2.60 GPa | 377 ksi | cond., 2 mm/min; ISO 178-A |
| 5.40 GPa | 783 ksi | d.a.m., 2 mm/min; ISO 178-A | |
| Izod Impact, Notched (ISO) | <= 10.0 kJ/m² | <= 4.76 ft-lb/in² | d.a.m.; ISO 180-1A |
| 10.0 kJ/m² | 4.76 ft-lb/in² | cond.; ISO 180-1A | |
| Izod Impact, Unnotched (ISO) | 42.0 kJ/m² @Temperature -30.0 °C |
20.0 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 180-1U |
| 55.0 kJ/m² @Temperature 23.0 °C |
26.2 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 180-1U | |
| 75.0 kJ/m² @Temperature 23.0 °C |
35.7 ft-lb/in² @Temperature 73.4 °F |
cond.; ISO 180-1U | |
| Charpy Impact Unnotched | 4.50 J/cm² @Temperature -30.0 °C |
21.4 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 179-1eU |
| 6.00 J/cm² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 179-1eU | |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 179-1eA |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 179-1eA | |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
cond.; ISO 179-1eA | |
| 1.20 J/cm² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
cond.; ISO 179-1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
22.2 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| CTE, linear, Transverse to Flow | 100 µm/m-°C @Temperature 23.0 - 55.0 °C |
55.6 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| Melting Point | 262 °C | 504 °F | 10°C/min; ISO 11357-1, -3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 245 °C | 473 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 225 °C | 437 °F | ISO 75-1, -2 |
| Vicat Softening Point | 255 °C @Load 5.10 kg |
491 °F @Load 11.2 lb |
120°C/hour; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
||
| Glow Wire Test | 650 °C @Diameter 2.00 mm |
1200 °F @Diameter 0.0787 in |
GWFI; IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+11 ohm | 1.00e+11 ohm | d.a.m.; IEC 60093 |
| Comparative Tracking Index | 375 V | 375 V | d.a.m.; Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | |
| 290 °C | 554 °F | for test specimens; ISO 294 | |
| Mold Temperature | 80.0 °C | 176 °F | for test specimens; ISO 294 |
| 80.0 - 120 °C | 176 - 248 °F | ||
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2 - 6 hour | 2 - 6 hour | |
| Moisture Content | 0.030 - 0.12 % | 0.030 - 0.12 % | residual; Karl Fischer Test |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shortname | ISO 1874-PA 66, BHRW, 14-060, GF15 |
Users viewing this material also viewed the following:
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 3.0 PHR MBT
- Lehmann & Voss LUVOCOM® 80-7666/GY Polyacetal-copolymer, with glass fiber and PTFE
- Gwent Electronic Materials P2121112P7 Acid Vapor Plasma Modified Multiwalled Carbon Nanotubes
- SABIC Innovative Plastics LNP LUBRICOMP DL003EXJ PC
- SABIC Innovative Plastics Valox® SLWM2105 PBT+PC (Asia Pacific)
- A. Schulman POLYBATCH™ Canyon 10277U/4 Concentrate Based In LLDPE
- Toyobo PELPRENE™ P55U Polyester TPE, Weather-resistant
- 3M Scotch® 827 Pouch Tape
Copyright © lookpolymers.com All Rights Reserved