Polymer Property : Flexural Modulus = 7.90 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	7.90 GPa	1150 ksi
Plastcom SLOVAMID 66 GF 30 HI PA66, 30% glass fibre, improved strength FeaturesPA 66 for injection moulding, chemically strengthened with 30% glass fibre and with the content of thermoplastic kaoutchouc. Application: impacted mouldings and mouldings with high strength ..
Flexural Modulus	7.90 GPa	1150 ksi	ISO 178
NOVA Chemicals Dylark® 378P30 Glass Reinforced Engineering Resin Features: Ultra high modulus, High heat resistance, excellent adhesion to urethaneApplications: Instrument panel substrates, Brackets, Structural components
Flexural Modulus	7.90 GPa	1150 ksi	ISO 178
Nilit FRIANYL A63 KF30 M2 Nylon 6.6 for injection molding, 30% short glass fiber reinforced and 2% molybdenum disulphide lubricated Nylon 6.6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Flexural Modulus	7.90 GPa	1150 ksi	ISO 178
Nilit FRIANYL B63 HS-GV40 Nylon 6 for injection molding, 40% glass fiber reinforced Nylon 6 for injection molding, high impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Flexural Modulus	7.90 - 17.2 GPa	1150 - 2500 ksi	Average value: 13.9 GPa Grade Count:111
Overview of materials for Nylon 66, 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 50% Glass Fiber Filled". Specific grades with glass content between 45% and 54% are included. ..
Flexural Modulus	7.90 GPa	1150 ksi	ISO 178
Solvay TECHNYLÂ® A 21T2 V25 PA66, 25% glass fiber, DRY Description: Flame retardant polyamide 66, reinforced with 25% of glass fiber, heat stabilized, for injection molding.Available in: Asia Pacific, Europe, Latin America and North AmericaProduct Appl..
Flexural Modulus	7.90 GPa	1150 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP RFL36SXC PA 66 (Europe-Africa-Middle East) LNP* Lubricomp* RFL36SXC is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Heat Stabilized.
Flexural Modulus	7.90 GPa	1150 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP RFL36SXD PA 66 (Europe-Africa-Middle East) LNP* Lubricomp* RFL36SXD is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Heat Stabilized.
Flexural Modulus	7.90 GPa	1150 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP WFI18 PBT (Europe-Africa-Middle East) LNP* Lubricomp* WFI18 is a compound based on Polybutylene Terephalate resin containing Glass Fiber, Silicone.
Flexural Modulus	7.90 GPa	1150 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ValoxÂ® 4031 PBT (Europe-Africa-Middle East) VALOX 4031 is a 30% high strength glass fibre reinforced PBT injection moulding resin with excellent strength, stiffness and heat resistance. Applications: appliance handles, spotlights, electric mo..
Flexural Modulus	7.90 GPa	1150 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ValoxÂ® 771 PBT (Europe-Africa-Middle East) VALOX 771 is a 15% glass and 20% mineral filled, flame retarded injection moulding PBT resin.
Flexural Modulus	7.90 GPa	1150 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP STAT-KON SC004 PA 12 (Europe-Africa-Middle East) LNP* Stat-kon* SE004 is a compound based on Nylon 12 resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.
Flexural Modulus	7.90 GPa	1150 ksi	ISO 178
SABIC Innovative Plastics LNP THERMOCOMP BF004 SAN (Asia Pacific) LNP* Thermocomp* BF004 is a compound based on Styrene Acrylonitrile resin containing Glass Fiber.
Flexural Modulus	7.90 GPa	1150 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP QF0069 PA6.10 (Europe-Africa-Middle East) LNP* THERMOCOMP* QF0069 is a compound based on PA610 resin contaning Glass Fiber, Flame Retardant. Added features include: Flame retardant.
Flexural Modulus	7.90 GPa	1150 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP Thermocomp RFC16 PA 66 (Europe-Africa-Middle East) LNP* THERMOCOMP* RFC16 is a compound based on PA 66 resin containing Glass Fiber, Carbon Fiber. Added features include: Easy Molding.This data was supplied by SABIC-IP for the Europe-Africa-Middle..
Flexural Modulus	7.90 GPa	1150 ksi	ISO 178-93
Wellman Wellamid® GFT1675-N1 33% Glass Fiber Reinforced, Impact Modified Nylon 66 Description: Glass Fiber Reinforced, Impact Modified Nylon 66Information provided by Wellman.
Flexural Modulus	7.90 GPa	1150 ksi	ASTM-D790
Polyram RamTough PZ503 Polycarbonate, Flame Retardant Flame retardant polycarbonate for injection molding applicationsInformation provided by Polyram Ram On Ind.
Flexural Modulus	7.90 GPa	1150 ksi	ISO 178
Eurostar Star L PA6 30V D51 PA6, Glass Filled, Injection Molding Star L PA6 30V D51 is a PTFE Lubricated, Glass Fiber Reinforced, Polyamide 6 Injection Molding ResinInformation provided by Eurostar.
Flexural Modulus	7.90 GPa	1150 ksi	2 mm/min; ISO 178
Eurostar Staramide RFC16 PA66/6, Glass/Carbon Fiber Filled, Injection Molded RFC16 is a Glass Fiber and Carbon Fiber Reinforced Polyamide 66/Polyamide 6 Injection Molding Resin (also known as STAR C PA66 C 303VY Z3)Information provided by Eurostar.
Flexural Modulus	7.90 GPa	1150 ksi	ASTM D790
E-Polymers TEKAMID® TB120G30 , 30% Glass Fiber Reinforced PA6, DAM 30% Glass Fiber Reinforced, Good impact resistanceInformation provided by E-Polymers Co. Ltd.
Flexural Modulus	7.90 GPa	1150 ksi	ISO 178
BASF Ultramid® 66 H2 G/25-V0KB1 NAT 0046 PA66 (Dry) Information provided by BASF
Flexural Modulus	7.90 GPa	1150 ksi	ASTM D790
Ashley Polymers Ashlene® 630-33G Nylon 6, 33% Glass Reinforced Nylon 6, 33% glass reinforced resin.Data provided by the manufacturer
Flexural Modulus	7.90 GPa	1150 ksi	ASTM D790
Ashley Polymers Ashlene® E126WO PET Polyester, 30% Glass Reinforced PET Polyester with 30% glass reinforcement, flame retardant, natural. Note: Colors will modify properties.Data provided by the manufacturer
Flexural Modulus	7.90 GPa	1150 ksi	ISO 178
BASF Ultramid® S3EG6 Balance 30% Glass Filled PA 610 (Dry) Description: BASF supplies polyamide 610 for processing by injection molding under the trade name Ultramid® Balance which is produced by polycondensation of hexamethylene diamine and sebacic acid. ..
Flexural Modulus	7.90 GPa	1150 ksi	ISO 178
BASF Ultramid® S3WG6 Balance 30% Glass Filled PA 610 (Dry) Description: BASF supplies polyamide 610 for processing by injection molding under the trade name Ultramid® Balance which is produced by polycondensation of hexamethylene diamine and sebacic acid. ..
Flexural Modulus	7.90 GPa	1150 ksi	ASTM D790
Chem Polymer Chemlon 233 G Nylon 6, 33% Glass Fiber Reinforced A 33% glass fiber reinforced nylon 6 offering excellent high temperature performance, dimensional stability, tensile strength and impact resistance.Data provided by the manufacturer, Chem Polymer.
Flexural Modulus	7.90 GPa	1150 ksi	ASTM D790
Chem Polymer Durlex 730 G PBT, 30% Glass Fiber Reinforced A lubricated 30% glass reinforced PBT offering a balance of dimensional stability, tensile strength and high temperature performance.Data provided by the manufacturer, Chem Polymer.
Flexural Modulus	7.90 GPa	1150 ksi	ASTM D790
A. Schulman ComAlloy Hiloy® 616 Nylon 6, Mineral Reinforced Data provided by the manufacturer, ComAlloy International Company.40% Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Flexural Modulus	7.90 GPa	1150 ksi	ASTM D790
Ashley Polymers Ashlene® 520-33G Nylon 66, 33% Glass Reinforced Nylon 66, 33% glass reinforced resin. Also available with Heat Stabilized and/or UV Stabilized.Data provided by the manufacturer
Flexural Modulus	7.90 GPa	1150 ksi	ISO 178
Polyplastics Duracon® GH-25 Acetal Co-polymer (POM), GF 25% reinforced, High strength, High rigidity DURACON® is a crystalline thermoplastic acetal copolymer. The primary raw material trioxane, a trimer of formaldehyde.The thermoplastic adopts a copolymer structure in which polyoxymethylene (-C-O)..