SABIC Innovative Plastics Valox® 771 PBT (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® 771 PBT (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
VALOX 771 is a 15% glass and 20% mineral filled, flame retarded injection moulding PBT resin.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.70 g/cc | 1.70 g/cc | ASTM D792 |
| Density | 1.70 g/cc | 0.0614 lb/in³ | ISO 1183 |
| Filler Content | 35 % | 35 % | ASTM D229 |
| Moisture Absorption | 0.0900 % | 0.0900 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.94 % | 0.94 % | ISO 62 |
| Viscosity | 140000 cP | 140000 cP | Melt Viscosity, 260°C, 1500 sec-1; ISO 11443 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | on Tensile Bar; SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.010 cm/cm | 0.0040 - 0.010 in/in | on Tensile Bar; SABIC Method |
| Melt Flow | 20 g/10 min @Load 5.00 kg, Temperature 266 °C |
20 g/10 min @Load 11.0 lb, Temperature 511 °F |
ASTM D1238 |
| Melt Index of Compound | 8.0 g/10 min @Load 5.00 kg, Temperature 250 °C |
8.0 g/10 min @Load 11.0 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
| 16 g/10 min @Load 5.00 kg, Temperature 265 °C |
16 g/10 min @Load 11.0 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 111 | 111 | ISO 2039-2 |
| Hardness, H358/30 | 120 MPa | 17400 psi | ISO 2039-1 |
| Tensile Strength at Break | 85.0 MPa | 12300 psi | Type I, 5 mm/min; ASTM D638 |
| 85.0 MPa | 12300 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 85.0 MPa | 12300 psi | Type I, 5 mm/min; ASTM D638 |
| 85.0 MPa | 12300 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 |
| 2.0 % | 2.0 % | 5 mm/min; ISO 527 | |
| 2.0 % | 2.0 % | Flexural Strain, break, 2 mm/min; ISO 178 | |
| Elongation at Yield | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 |
| 2.0 % | 2.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 9.50 GPa | 1380 ksi | 5 mm/min; ASTM D638 |
| 9.70 GPa | 1410 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 110 MPa | 16000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 120 MPa | 17400 psi | 2 mm/min; ISO 178 | |
| Flexural Yield Strength | 110 MPa | 16000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 120 MPa | 17400 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 7.90 GPa | 1150 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 8.40 GPa | 1220 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.520 J/cm | 0.974 ft-lb/in | ASTM D256 |
| 0.510 J/cm @Temperature -30.0 °C |
0.955 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| 0.520 J/cm @Temperature 0.000 °C |
0.974 ft-lb/in @Temperature 32.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 3.90 J/cm | 7.31 ft-lb/in | ASTM D4812 |
| 3.90 J/cm @Temperature -30.0 °C |
7.31 ft-lb/in @Temperature -22.0 °F |
ASTM D4812 | |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| 5.00 kJ/m² @Temperature 0.000 °C |
2.38 ft-lb/in² @Temperature 32.0 °F |
80*10*4; ISO 180/1A | |
| 5.00 kJ/m² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| 25.0 kJ/m² @Temperature -30.0 °C |
11.9 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | 2.90 J/cm² | 13.8 ft-lb/in² | ISO 179/2C |
| 4.50 J/cm² | 21.4 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| 2.00 J/cm² @Temperature -30.0 °C |
9.52 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| 2.90 J/cm² @Temperature -30.0 °C |
13.8 ft-lb/in² @Temperature -22.0 °F |
ISO 179/2C | |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179/2C | |
| 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| 0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
ISO 179/2C | |
| Taber Abrasion, mg/1000 Cycles | 55 | 55 | CS-17, 1 kg; SABIC Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 22.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
12.5 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 30.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
16.7 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| 30.1 µm/m-°C @Temperature 23.0 - 150 °C |
16.7 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 59.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
32.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | ASTM D257 |
| >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| Dielectric Constant | 3.1 @Frequency 1.00e+6 Hz |
3.1 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.3 @Frequency 50.0 - 60.0 Hz |
3.3 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Dielectric Strength | 20.0 kV/mm @Thickness 3.20 mm |
508 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| 23.0 kV/mm @Thickness 1.60 mm |
584 kV/in @Thickness 0.0630 in |
in oil; IEC 60243-1 | |
| Dissipation Factor | 0.0095 @Frequency 50.0 - 60.0 Hz |
0.0095 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
| 0.0128 @Frequency 1.00e+6 Hz |
0.0128 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Arc Resistance | 180 - 240 sec | 180 - 240 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | >= 175 V | >= 175 V | IEC 60112 |
| 600 V | 600 V | IEC 60112 | |
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 0.000 - 10.0 mm/min | 0.000 - 0.394 in/min | UL 746A |
Users viewing this material also viewed the following:
- NIZHNEKAMSKNEFTEKHIM PP 4340R (EP2Z29G) Propylene and Ethylene Copolymer
- SABIC Innovative Plastics Lexan® OQ2320 PC
- Solvay Specialty Polymers Amodel® AF-1133 V0 Polyphthalamide (PPA) Resin, 33% Glass Reinforced, Dry As Molded
- NanoAmor 95%, OD/ID: 50-80/5-15 nm Aligned Multi-Walled Carbon Nanotubes
- PolyOne Edgetek® ATH-20CF/000 Acetal-Homopolymer, Carbon Fiber Reinforced (discontinued **)
- MRC Polymers MAXTELâ„¢ 600T18-UV TPO, 18% Talc Filled, UV Stabilized
- Wellman Wellamid® GFX1717-BK1 Nylon 66, 43% Glass Fiber Reinforced, Silicone Lubricated
- UBE UBESTA® 3030U Nylon 12 (After Trichloroethylene for 500 hours)
- DuPont Performance Polymers Crastin® 6129 NC010 Polybutylene Terephthalate (PBT) (Unverified Data**)
- Advanced Polymer Alloys Alcryn® 2165 TR Melt Processable Rubber
Copyright © lookpolymers.com All Rights Reserved