- Polymer Property : Flexural Modulus = 5.90 GPa
Polymer Property : Flexural Modulus = 5.90 GPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Modulus | 5.90 GPa @Temperature 23.0 °C |
856 ksi @Temperature 73.4 °F |
ISO 178 |
| Polykemi AB POLYblend 85FS GF20 PC/ABS-Blend, Glass Fiber reinforced Information provided by Polykemi AB |
|||
| Flexural Modulus | 5.90 GPa | 856 ksi | ASTM D790 |
| LG Chemical LUCEL MR-320 Low Warpage POM, 20% Mineral Filled LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m.. |
|||
| Flexural Modulus | 5.90 GPa | 856 ksi | 1.3 mm/min; ASTM D790 |
| Lavergne VYPET VNT 615 FR PET 15% Glass Reinforced, Flame Retardant Vypet VNT 615 FR is a 15% fiberglass reinforced flame retardant PET injection molding compound designed for electrical and structural applications.Features: Flame retardant; UL yellow card file E216.. |
|||
| Flexural Modulus | 5.90 GPa | 856 ksi | cond., 2 mm/min; ISO 178-A |
| Lanxess Durethan® BKV 35 H3.0 000000 Nylon 6, Glass Fiber Reinforced PA 6, 35% glass fibers, injection molding, heat-aging stabilizedInformation provided by LANXESS. |
|||
| Flexural Modulus | 5.90 GPa | 856 ksi | 2 mm/min, 64mm span; ISO 178 |
| SABIC Innovative Plastics SABIC STAMAX 30YM243 PP SABIC® STAMAX 30YM243 is a 30% long glass fiber reinforced UV stabilized polypropylene. The glass fibers are chemically coupled to the PP matrix, resulting in high stiffness and strength. The IMD.. |
|||
| Flexural Modulus | 5.90 GPa | 856 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP SFL36 PA12 (Europe-Africa-Middle East) LNP* LUBRICOMP* SFL36 is a compound based on PA 12 resin containing Glass Fiber, PTFE. Added features include: Internally Lubricated. |
|||
| Flexural Modulus | 5.90 GPa | 856 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Valox® 412 PBT (Europe-Africa-Middle East) VALOX 412 is 20% glass reinforced PBT injection moulding resin. Applications: Spotlights, appliance housings and handles. |
|||
| Flexural Modulus | 5.90 GPa | 856 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP STAT-KON PFD04ES PA 6 (Europe-Africa-Middle East) LNP* STATKON* PFD04ES is a compound based on PA 6 resin containing Carbon Powder, Glass Fiber. Added features include: Electrically Conductive, Easy Molding, Heat Stabilized. |
|||
| Flexural Modulus | 5.90 GPa | 856 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP STAT-KON PFD04S PA 6 (Europe-Africa-Middle East) LNP* Statkon* PFD04S is a compound based on PA 6 resin containing Glass Fiber, Carbon Powder. Added features include: Electrically Conductive, Heat Stabilized. |
|||
| Flexural Modulus | 5.90 GPa | 856 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP STAT-KON PX93058 PA 6 (Europe-Africa-Middle East) LNP*STATKON*PX93058 is a compound based on PA 6 resin containing Carbon Powder, Glass Fiber. Added features include: Electrically Conductive, Easy Molding, Heat Stabilized. |
|||
| Flexural Modulus | 5.90 GPa | 856 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP THERMOCOMP JF004 PES (Europe-Africa-Middle East) LNP* Thermocomp* JF004 is a compound based on Polyethersulfone resin containing Glass Fiber. |
|||
| Flexural Modulus | 5.90 GPa | 856 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP Thermocomp PFB139E PA 6 (Europe-Africa-Middle East) LNP* THERMOCOMP* PFB139E is a compound based on PA 6 resin containing Glass Fiber, Glass Bead, Flame Retardant. Added features include; Flame Retardant, Easy Molding.This data was supplied by SABIC-.. |
|||
| Flexural Modulus | 5.90 GPa | 856 ksi | ISO 178 |
| SABIC Innovative Plastics LNP THERMOCOMP RF0029S PA 66 LNP* THERMOCOMP* RF0029S is a compound based on Nylon 66 resin containing 10% Glass Fiber. Added features of this material include: Flame Retardant, Heat Stabilized. |
|||
| Flexural Modulus | 5.90 GPa | 856 ksi | 2 mm/min; ISO 178 |
| Sax Polymers SAXAMID 226F4 Nylon 6.6, 20% Glass Fiber SAXAMID 226F4 is a polyamide 6.6 injection-molding-grade reinforced with 20% glass fibers.Information provided by SAX Polymers |
|||
| Flexural Modulus | 5.90 GPa | 856 ksi | ISO 178 |
| Solvay TECHNYL® A 218HP V30 Black 21N PA66, 30% glass fiber, Conditioned Provisional datasheet - Product in developmentDescription: Polyamide 66, reinforced with 30% of glass fiber, heat stabilized, for injection molding.Available in: EuropeProduct Applications: TECHNYLÂ.. |
|||
| Flexural Modulus | 5.90 GPa | 856 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| SABIC Innovative Plastics Noryl GFN1420V PPE+PS (Asia Pacific) Noryl* GFN1420V resin is a high flow blend of polyphenylene ether (PPE) and polystyrene (PS) resin that contains 20 % glass reinforcement. The resin is suitable for injection molding and is designe.. |
|||
| Flexural Modulus | 5.90 GPa | 856 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| SABIC Innovative Plastics Noryl GFN1420V PPE+PS (Europe-Africa-Middle East) Noryl* GFN1420V resin is a high flow blend of polyphenylene ether (PPE) and polystyrene (PS) resin that contains 20 % glass reinforcement. The resin is suitable for injection molding and is designe.. |
|||
| Flexural Modulus | 5.90 GPa | 856 ksi | DAM; ISO 178 |
| DuPont Performance Polymers Minlon® 73M40 NC010 Nylon 6
(Unverified Data**) 40% Mineral Reinforced Polyamide 6 Minlon 73M40 NC010 is a 40% mineral reinforced heat stabilized polyamide 6 resin for injection molding. It has isotropic properties and low warpage.Information pro.. |
|||
| Flexural Modulus | 5.90 GPa | 856 ksi | ISO 178 |
| Ascend Performance Materials Vydyne® R515 Nylon 66, 15% Glass Reinforced, DAM Vydyne® R515 is general-purpose, 15% glass-fiber reinforced PA66 resin. Availability:Asia PacificEuropeNorth AmericaFiller/Reinforcement:Glass Fiber, 15% Filler by WeightAdditive:Lubricant Features.. |
|||
| Flexural Modulus | 5.90 GPa | 856 ksi | ISO 178 |
| Ascend Performance Materials Vydyne® R515H Nylon 66, 15% Glass Reinforced, DAM Vydyne® R515H is general-purpose, heat-stabilized, hydrolysis-resistant, 15% glass-fiber reinforced PA66 resin. Available in natural it is specifically designed to maximize the retention of physica.. |
|||
| Flexural Modulus | 5.90 GPa | 856 ksi | ASTM D790 |
| A. Schulman ComAlloy Hiloy® 113 Polypropylene, Glass Reinforced, Chemically Coupled Data provided by the manufacturer, ComAlloy International Company.30% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Flexural Modulus | 5.90 GPa | 856 ksi | Dry; ASTM D790 |
| Asahi Kasei Leona® CR301 Nylon 66 Suitable for a switch insulator. Low abrasion and superior electrical properties.Applications:Sliding switch insulators Information provided by Asahi Kasei |
|||
| Flexural Modulus | 5.90 GPa | 856 ksi | dry; ISO 178 |
| DSM Novamid® 1013PL1 NAT PA6-MX Injection Molding |
|||
| Flexural Modulus | 5.90 GPa | 856 ksi | At 2 mm/min; ISO 178 |
| Borealis Xmod™ K65G3 30% Glass Fiber Reinforced Polypropylene Compound Xmod K65G3 is a 30% glass fiber reinforced grade intended for injection molding. Xmod K65G3 has been developed especially for the car industry, to be used UTB parts. Xmod K65G3 offers good balance.. |
|||
| Flexural Modulus | 5.90 GPa | 856 ksi | ASTM D790 |
| LATI LASULF G/20 20% Glass Reinforced Polysulfone (PSU)
(Unverified Data**) Description: Lasulf products are composed of polysulfone (PSU). They feature good thermal and mechanical properties such as excellent toughness, even at low temperatures, excellent dimensional stabi.. |
|||
| Flexural Modulus | 5.90 GPa | 856 ksi | ASTM D790 |
| PolyOne Lubri-Tech™ MP-30GF/15T Modified PPO - 30% Glass Fiber - 15% PTFE
(discontinued **) Data provided by PolyOne. |
|||
| Flexural Modulus | 5.90 GPa | 856 ksi | ASTM D790 |
| Adell BJ-17 Nylon 6, 35% Glass Reinforced; High Impact Data provided by Adell Plastics, Inc. |
|||
| Flexural Modulus | 5.90 GPa | 856 ksi | ASTM D790 |
| Adell ER-16 Homopolymer Polypropylene, 30% Glass Reinforced Data provided by Adell Plastics, Inc. |
|||