Ascend Performance Materials Vydyne® R515 Nylon 66, 15% Glass Reinforced, DAM

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled
Manufacturer Ascend Performance Materials (formerly Solutia)
Trade Name VYDYNE®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ascend Performance Materials Vydyne® R515 Nylon 66, 15% Glass Reinforced, DAM.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Vydyne® R515 is general-purpose, 15% glass-fiber reinforced PA66 resin. Availability:Asia PacificEuropeNorth AmericaFiller/Reinforcement:Glass Fiber, 15% Filler by WeightAdditive:Lubricant Features: Gasoline ResistanceGood Chemical ResistanceGood FlowGood Mold ReleaseGrease ResistantHeat StabilizedHigh RigidityHigh StrengthLubricatedOil ResistantSolvent ResistantUses:Automotive Under the HoodGearsHousingsPower/Other ToolsAppearance: Natural ColorForms: PelletsProcessing Method: Injection MoldingInformation provided by Ascend Performance Materials.
Physical Properties Metric English Comments
Density 1.24 g/cc
0.0448 lb/in³
ISO 1183
Water Absorption 1.0 %

@Time 86400 sec
 1.0 %

@Time 24.0 hour
 ISO 62
Moisture Absorption at Equilibrium 2.2 %
2.2 %
50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0050 cm/cm

@Diameter 2.00 mm
 0.0050 in/in

@Diameter 0.0787 in
 ISO 294-4
Linear Mold Shrinkage, Transverse 0.010 cm/cm

@Diameter 2.00 mm
 0.010 in/in

@Diameter 0.0787 in
 ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength, Yield 120 MPa
17400 psi
ISO 527-2
Elongation at Break 3.0 %
3.0 %
ISO 527-2
Tensile Modulus 6.60 GPa
957 ksi
ISO 527-2
Flexural Strength 170 MPa
24700 psi
ISO 178
Flexural Modulus 5.90 GPa
856 ksi
ISO 178
Poissons Ratio 0.40
0.40
ISO 527-2
Izod Impact, Notched (ISO) 5.70 kJ/m²

@Temperature -30.0 °C
 2.71 ft-lb/in²

@Temperature -22.0 °F
 ISO 180
6.60 kJ/m²

@Temperature 23.0 °C
 3.14 ft-lb/in²

@Temperature 73.4 °F
 ISO 180
Charpy Impact Unnotched 3.20 J/cm²

@Temperature -30.0 °C
 15.2 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
3.90 J/cm²

@Temperature 23.0 °C
 18.6 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eU
Charpy Impact, Notched 0.600 J/cm²

@Temperature -30.0 °C
 2.86 ft-lb/in²

@Temperature -22.0 °F
 ISO 179
0.600 J/cm²

@Temperature 23.0 °C
 2.86 ft-lb/in²

@Temperature 73.4 °F
 ISO 179
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 3.00 µm/m-°C

@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C
 1.67 µin/in-°F

@Thickness 0.0787 in,
Temperature 73.4 - 131 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 11.0 µm/m-°C

@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C
 6.11 µin/in-°F

@Thickness 0.0787 in,
Temperature 73.4 - 131 °F
 ISO 11359-2
Melting Point 260 °C
500 °F
ISO 11357-3
Deflection Temperature at 0.46 MPa (66 psi) 258 °C
496 °F
Unannealed; ISO 75-2/B
Deflection Temperature at 1.8 MPa (264 psi) 241 °C
466 °F
Unannealed; ISO 75-2/A
UL RTI, Electrical 120 °C

@Thickness 0.750 mm
 248 °F

@Thickness 0.0295 in
 UL 746
120 °C

@Thickness 1.50 mm
 248 °F

@Thickness 0.0591 in
 UL 746
120 °C

@Thickness 3.00 mm
 248 °F

@Thickness 0.118 in
 UL 746
UL RTI, Mechanical with Impact 85.0 °C

@Thickness 0.750 mm
 185 °F

@Thickness 0.0295 in
 UL 746
85.0 °C

@Thickness 1.50 mm
 185 °F

@Thickness 0.0591 in
 UL 746
105 °C

@Thickness 3.00 mm
 221 °F

@Thickness 0.118 in
 UL 746
UL RTI, Mechanical without Impact 115 °C

@Thickness 0.750 mm
 239 °F

@Thickness 0.0295 in
 UL 746
120 °C

@Thickness 1.50 mm
 248 °F

@Thickness 0.0591 in
 UL 746
120 °C

@Thickness 3.00 mm
 248 °F

@Thickness 0.118 in
 UL 746
Flammability, UL94 HB

@Thickness 0.750 mm
 HB

@Thickness 0.0295 in
HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
HB

@Thickness 3.00 mm
 HB

@Thickness 0.118 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm

@Thickness 0.750 mm
 1.00e+13 ohm-cm

@Thickness 0.0295 in
 IEC 60093
Dielectric Strength 24.0 kV/mm

@Thickness 1.00 mm
 610 kV/in

@Thickness 0.0394 in
 IEC 60243
Arc Resistance 120 - 179 sec

@Thickness 3.00 mm
 120 - 179 sec

@Thickness 0.118 in
 ASTM D495
Comparative Tracking Index 600 V

@Thickness 3.00 mm
 600 V

@Thickness 0.118 in
 IEC 60112
Hot Wire Ignition, HWI 7.0 - 14 sec

@Thickness 0.750 mm
 7.0 - 14 sec

@Thickness 0.0295 in
 UL 746
7.0 - 14 sec

@Thickness 1.50 mm
 7.0 - 14 sec

@Thickness 0.0591 in
 UL 746
7.0 - 14 sec

@Thickness 3.00 mm
 7.0 - 14 sec

@Thickness 0.118 in
 UL 746
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 0.750 mm
 >= 120 arcs

@Thickness 0.0295 in
 UL 746
>= 120 arcs

@Thickness 1.50 mm
 >= 120 arcs

@Thickness 0.0591 in
 UL 746
>= 120 arcs

@Thickness 3.00 mm
 >= 120 arcs

@Thickness 0.118 in
 UL 746
High Voltage Arc-Tracking Rate, HVTR 10.1 - 25.4 mm/min
0.398 - 1.00 in/min
UL 746
Processing Properties Metric English Comments
Rear Barrel Temperature 280 - 310 °C
536 - 590 °F
Middle Barrel Temperature 280 - 310 °C
536 - 590 °F
Front Barrel Temperature 280 - 310 °C
536 - 590 °F
Nozzle Temperature 280 - 310 °C
536 - 590 °F
Melt Temperature 285 - 305 °C
545 - 581 °F
Mold Temperature 65.0 - 95.0 °C
149 - 203 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 4.00 hour
4.00 hour
Descriptive Properties Value Comments
Suggested Max Regrind 25 %