Polymer Property : Tensile Strength, Ultimate = 82.7 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	40.0 - 82.7 MPa	5800 - 12000 psi	Average value: 57.6 MPa Grade Count:28
Overview of materials for Acetal Copolymer, Aramid Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, Aramid Fiber Filled". Each property range of values reported is minimum and maximum va..
Tensile Strength, Ultimate	25.0 - 82.7 MPa	3630 - 12000 psi	Average value: 60.5 MPa Grade Count:4
Overview of materials for Nylon 6, Stainless Steel Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Stainless Steel Filled". Each property range of values reported is minimum and maximum values o..
Tensile Strength, Ultimate	55.0 - 82.7 MPa	7980 - 12000 psi	Average value: 65.2 MPa Grade Count:11
Overview of materials for Nylon 612, Aramid Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 612, Aramid Fiber Filled". Each property range of values reported is minimum and maximum values of..
Tensile Strength, Ultimate	58.6 - 82.7 MPa	8500 - 12000 psi	Average value: 66.4 MPa Grade Count:4
Overview of materials for Nylon 11 with 10% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Nylon 11 with 10% Glass Fiber Filler". Specific grades with glass content between 5% and 14% are includ..
Tensile Strength, Ultimate	62.1 - 82.7 MPa	9000 - 12000 psi
Bulk Molding Compounds BMC 685 Mineral Filled, Glass Fiber Reinforced Polyester Compound BMC 685 molding compound is a mineral filled, glass fiber-reinforced polyester compound suitable for compression, transfer and stuffer injection molding It is characterized by good moldability, oil ..
Tensile Strength, Ultimate	62.1 - 82.7 MPa	9000 - 12000 psi
Bulk Molding Compounds BMC 695 Vinyl Ester Molding Compound BMC 695 vinyl ester molding compound is a mineral filled glass fiber-reinforced vinyl ester compound suitable for compression and injection molding It is characterized by good moldability, oil and s..
Tensile Strength, Ultimate	68.9 - 82.7 MPa	10000 - 12000 psi
Bulk Molding Compounds BMC 810 General Purpose Molding Compound BMC 810 is a general purpose, very high strength compound suitable for compression, transfer and stuffer injection molding. It is characterized by excellent flow and controlled reactivity and is wel..