Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 68.9 MPa | 10000 psi | ASTM D412 |
1065D Polyurethane-based Biomedical Elastomer |
|||
Tensile Strength, Ultimate | 68.9 MPa | 10000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
PolyOne Edgetek® BB-20GF/000 PC/ABS Blend, Glass Filled
(discontinued **) Description/Features:Glass Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation. |
|||
Tensile Strength, Ultimate | 68.9 - 138 MPa | 10000 - 20000 psi | Average value: 115 MPa Grade Count:15 |
Overview of materials for Polyetherimide (PEI), 10% Glass Fiber This property data is a summary of similar materials in the MatWeb database for the category "Polyetherimide, 10% Glass Fiber". Specific grades with glass content between 5% and 14% are included. Ea.. |
|||
Tensile Strength, Ultimate | 68.9 - 108 MPa | 10000 - 15700 psi | Average value: 82.2 MPa Grade Count:13 |
Overview of materials for Polysulfone, 10% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polysulfone, 10% Glass Fiber Reinforced". Specific grades with glass content between 5% and 14% are incl.. |
|||
Tensile Strength, Ultimate | 68.9 - 207 MPa | 10000 - 30000 psi | Average value: 116 MPa Grade Count:10 |
Overview of materials for Nylon 66, Mineral Filled, NCG Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Mineral Filled, NCG Fiber Filled". Each property range of values reported is minimum and maxim.. |
|||
Tensile Strength, Ultimate | 68.9 MPa | 10000 psi | ASTM D638 |
Techmer ES Plaslube® J-50/10/SI/2 Polycarbonate, 10% GFR, 2% Silicone |
|||
Tensile Strength, Ultimate | 68.9 MPa | 10000 psi | ASTM D638 |
Techmer ES Plaslube® NY-1/TF/13/SI/2 Nylon 66, 13% PTFE, 2% Silicone Plaslube polytetrafluoroethylene (PTFE) lubricated nylon 66 grades offer the best wear and friction properties of any unreinforced, lubricated nylon compounds, making them ideal materials for bearin.. |
|||
Tensile Strength, Ultimate | 68.9 MPa | 10000 psi | |
Cotronics Duralco™ 4540 Machinable Epoxy Patches, fills, seals, and repairs with outstanding adhesion, ductility, thermal conductivity and shock resistance.Corrosion Resistance: excellent resistance to chemicals and solventsApplications: .. |
|||
Tensile Strength, Ultimate | 68.9 MPa | 10000 psi | Crosswise; ASTM D638 |
Bedford Plastics Glass Reinforced FR Polyester Flat Sheet, 3/16" to 1/4" Flame retardant grade; see details in the property table.Pultrusion results in the production and supply of one of the worlds strongest and most durable products available today. The pultruded prod.. |
|||
Tensile Strength, Ultimate | 68.9 MPa | 10000 psi | Crosswise; ASTM D638 |
Bedford Plastics Glass Reinforced FR Polyester Flat Sheet, 3/8" to 1" Flame retardant grade; see details in the property table.Pultrusion results in the production and supply of one of the worlds strongest and most durable products available today. The pultruded prod.. |
|||
Tensile Strength, Ultimate | 68.9 MPa | 10000 psi | Crosswise; ASTM D638 |
Bedford Plastics Glass Reinforced Vinylester Flat Sheet, 3/16" to 1/4" Flame retardant grade; see details in the property table.Pultrusion results in the production and supply of one of the worlds strongest and most durable products available today. The pultruded prod.. |
|||
Tensile Strength, Ultimate | 68.9 MPa | 10000 psi | Crosswise; ASTM D638 |
Bedford Plastics Glass Reinforced Polyester Flat Sheet, 3/8" to 1" Pultrusion results in the production and supply of one of the worlds strongest and most durable products available today. The pultruded products feature:High StrengthCorrosion Resistant to many che.. |
|||
Tensile Strength, Ultimate | 68.9 MPa | 10000 psi | |
3M Scotch-Weld™ 2214 Regular Epoxy Adhesive 3M™ Scotch-Weld™ Adhesive 2214 Regular is an aluminum filled general purpose product for use in applications where high strength bonds are needed in a temperature range of -53-121°C.One part 250°.. |
|||
Tensile Strength, Ultimate | 68.9 MPa | 10000 psi | |
Parylene Coating Services C Poly (P-Xylylene) Monomer is monochloro para-xylylene. Parylene C is recommended where excellent barrier protection is needed. It can be used up to 125°C where oxygen is present.Parylene is a generic name for poly-.. |
|||
Tensile Strength, Ultimate | 68.9 - 233 MPa | 10000 - 33800 psi | Average value: 176 MPa Grade Count:81 |
Overview of materials for Polyphthalamide (PPA), 30% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, 30% Glass Fiber Reinforced". Specific grades with glass content between 25% and 34% are.. |