Polymer Property : Film Tensile Strength at Break, TD = 8700 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, TD	60.0 MPa	8700 psi	ASTM D882
Honeywell Aegisâ„¢ H155ZP Nylon 6 Extrusion Grade Homopolymer Film Description: Aegis H155ZP is a high viscosity, nylon 6 film extrusion grade homopolymer for cast or blown film. It conforms to Food and Drugs Administration requirements of 21 CFR 177.1500 as well a..
Film Tensile Strength at Break, TD	60.0 MPa	8700 psi	ISO 527-3
Borealis Borstar® FB1460 HDPE for Film Borstar FB1460 is a high-density polyethylene film grade, which combines superior physical properties with excellent processability. Due to the high density, the material properties are best utiliz..
Film Tensile Strength at Break, TD	60.0 MPa	8700 psi	ASTM D882
ExxonMobil Exceed™ 1023CA Metallocene Polyethylene Resin (European Grade) Product Description: Exceed 1023CA is a metallocene ethylene-hexene copolymers. The slightly higher stiffness of Exceed 1023CA makes it easier to process on certain filling machinery, whilst still k..
Film Tensile Strength at Break, TD	60.0 MPa	8700 psi	ISO 527-3
EMS-Grivory Grivory® BM 17 PA* Product description: Grilon BM 17 natural is a medium viscosity multi-polyamide with a low melting point. Grilon BM 17 natural has the following features: High flexibility and toughnessVery good ori..
Film Tensile Strength at Break, TD	60.0 MPa	8700 psi	ISO 527-3
EMS-Grivory Grivory® CA 6 E PA* Product description: Grilon CA 6 E is a non-extracted copolyamide with a low melting point. Grilon CA 6 E characterizes itself through the following properties Very high flexibility and toughnessVer..
Film Tensile Strength at Break, TD	60.0 MPa	8700 psi	ASTM D882
Braskem Flexus® 9200 Blown Film Extrusion Polyethylene Description: Flexus 9200 is a LLDPE hexene copolymer produced through metallocene catalyst which presents excellent impact and puncture strength, beyond a differential sealing performance comparing ..
Film Tensile Strength at Break, TD	60.0 MPa	8700 psi	ASTM D882
Ashley Polymers Ashlene® 850 Nylon 6 This is an extrusion grade Nylon 6 resin suitable for both coextrusion and blown film applications. It has excellent melt stability and very high melt strength. It also has excellent grease resist..
Film Tensile Strength at Break, TD	60.0 - 100 MPa	8700 - 14500 psi	Average value: 80.0 MPa Grade Count:5
Overview of materials for Nylon 6, Extruded This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Extruded". Each property range of values reported is minimum and maximum values of appropriate ..
Film Tensile Strength at Break, TD	60.0 MPa	8700 psi	ISO 527-3
EMS-Grivory Grivory® BM 20 SBG PA* Product description: Grilon BM 20 SBG is a lactam free multipolyamide. Grilon BM 20 SBG has the following features: Lactam freeGood transparency and glossGood flexibility and toughnessVery good ther..