- HOME
- POLYMER SEARCH
- Polymer Property : Tensile Strength, Yield = 870 psi
Polymer Property : Tensile Strength, Yield = 870 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 6.00 MPa | 870 psi | ISO 527 |
| Polimeri Europa Greenflex® ML 40 Ethylene Vinyl Acetate Copolymer - Injection Molding Greenflex ML 40 is an ethylene vinyl acetate copolymer (EVA) for injection molding of flexible items. Items produced with Greenflex ML 40 show high elasticity and flexibility.Main Applications: Gr.. |
|||
| Tensile Strength, Yield | 6.00 MPa | 870 psi | -25% change after 72 hours @ 150°C; ASTM D412 |
| Precision Polymer Engineering H50B Epichlorohydrin Peroxide Cured, Epichlorohydrin Rubber, 45-55 °IRHD. Terpolymer of epichlorohydrin, ethylene oxide and an unsaturated monomer. ASTM and ISO designation = GECO.Applications: Excellent resistance t.. |
|||
| Tensile Strength, Yield | 6.00 MPa | 870 psi | -25% change after 72 hours @ 150°C; ASTM D412 |
| Precision Polymer Engineering H60B Epichlorohydrin Peroxide Cured, Epichlorohydrin Rubber, 55-65 °IRHD. Terpolymer of epichlorohydrin, ethylene oxide and an unsaturated monomer. To ASTM D2000 line call-out: M3CH608, A25, B14, EO16, EO36, F17. AS.. |
|||
| Tensile Strength, Yield | 6.00 MPa | 870 psi | -25% change after 70 hours @ 200°C; ASTM D412 |
| Precision Polymer Engineering S60A Silicone Rubber Blue Silicone Rubber, 55-65 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain. Formulated using only those ingredients determined by the United States Fe.. |
|||
| Tensile Strength, Yield | 6.00 MPa | 870 psi | -25% change after 70 hours @ 200°C; ASTM D412 |
| Precision Polymer Engineering S60B Silicone Rubber Black Silicone Rubber, 55-65 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain. Formulated using only those ingredients determined by the United States F.. |
|||
| Tensile Strength, Yield | 6.00 MPa | 870 psi | -25% change after 70 hours @ 225°C; ASTM D412 |
| Precision Polymer Engineering S60Z Silicone Rubber Grey Silicone Rubber, 55-65 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain. Formulated using only those ingredients determined by the United States Fo.. |
|||
| Tensile Strength, Yield | 6.00 MPa | 870 psi | -25% change after 70 hours @ 200°C; ASTM D412 |
| Precision Polymer Engineering S65R Silicone Rubber Low Compression Set, Red Silicone Rubber, 61-70 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain. Formulated using only those ingredients determined by t.. |
|||
| Tensile Strength, Yield | 6.00 MPa | 870 psi | -25% change after 70 hours @ 200°C; ASTM D412 |
| Precision Polymer Engineering S70A Silicone Rubber Blue Silicone Rubber, 66-75 °IRHD.Complies with the formulation guidelines of the FDA. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain.Applications: Excellent .. |
|||
| Tensile Strength, Yield | 6.00 MPa | 870 psi | -25% change after 70 hours @ 200°C; ASTM D412 |
| Precision Polymer Engineering S70G Silicone Rubber Green Silicone Rubber, 66-75 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain. Formulated using only those ingredients determined by the United States F.. |
|||
| Tensile Strength, Yield | 6.00 MPa | 870 psi | -25% change after 70 hours @ 200°C; ASTM D412 |
| Precision Polymer Engineering S72R Silicone Rubber Orange Silicone Rubber, 65-75 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain. Formulated using only those ingredients determined by the United States .. |
|||
| Tensile Strength, Yield | 6.00 MPa | 870 psi | -25% change after 72 hours @ 250°C; ASTM D412 |
| Precision Polymer Engineering V75E Fluoroelastomer Compound Special steam resistant, Green Fluoroelastomer Rubber, 71-80 °IRHD. Copolymer of vinylidene fluoride and hexafluoropropylene. To meet ASTM D2000 line call-out:- M2HK710, A1-10, B38, EF31, EO78, F1.. |
|||
| Tensile Strength, Yield | 6.00 MPa | 870 psi | ASTM D638 |
| Petroquimica Triunfo Tritheva® TN 2007 EVA Copolymer The Tritheva TN 2007 resin is an Ethylene-Vinyl Acetate copolymer (EVA), developed to meet the multi-layer packaging needs where are required high strength, with high toughness, and excellent optica.. |
|||
| Tensile Strength, Yield | 6.00 - 170 MPa | 870 - 24700 psi | Average value: 105 MPa Grade Count:16 |
| Overview of materials for Nylon 6, Glass Filled, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Glass Filled, Impact Grade". Each property range of values reported is minimum and maximum valu.. |
|||
| Tensile Strength, Yield | 6.00 MPa | 870 psi | 200°C for 1,000 hrs |
| Fujipoly Industries Sarcon® 30Q Thin-Film QR Sarcon QR is Fujipolys originally developed High Heat Conductive/Low Hardness Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Information prov.. |
|||
| Tensile Strength, Yield | 6.00 MPa | 870 psi | 150°C for 1,000 hrs |
| Fujipoly Industries Sarcon® 30T Thin-Film TR Sarcon TR is Fujipolys originally developed High Heat Conductive Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Sarcon GTR is a composite of .. |
|||
| Tensile Strength, Yield | 6.00 MPa | 870 psi | 200°C for 1,000 hrs |
| Fujipoly Industries Sarcon® 85U Thin-Film UR Sarcon UR is Fujipolys originally developed High Heat Conductive/Low Hardness Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Information prov.. |
|||
| Tensile Strength, Yield | 6.00 MPa | 870 psi | ISO 527-1, -2 |
| LyondellBasell Hifaxâ„¢ A Thermoplastic Polyolefin Elastomer Description: Hifaxâ„¢ CA 10 A is a thermoplastic polyolefin which has been developed for the extrusion and calendering of soft film and sheet. Thanks to its high rubber content "Hifax" CA 10 A fe.. |
|||
| Tensile Strength, Yield | 6.00 MPa | 870 psi | ASTM D638 |
| A. Schulman POLYFORT™ PX 1040 Information provided by A. Schulman. |
|||
| Tensile Strength, Yield | 6.00 MPa | 870 psi | |
| Trelleborg Commercial Neoprene® C800 Chloroprene CR or Chloroprene is a homopolymer of chloroprene or chlorobutadiene. NEOPRENE®PropertiesExcellent mechanical and abrasion properties even without reinforcing fillers.Reasonable resilience in grade.. |
|||
| Tensile Strength, Yield | 6.00 MPa | 870 psi | ASTM D638 |
| A. Schulman POLYFORT™ PX 1040 Information provided by A. Schulman. |
|||
| Tensile Strength, Yield | 6.00 MPa @Strain 50.0 % |
870 psi @Strain 50.0 % |
|
| Covestro Texin® 185 Urethane Thermoplastic Elastomer Key Features:UnfilledSuitable processing methods:Injection moldingFilm extrusionProfile extrusionSheet extrusionCoatingInformation provided by Bayer Polymers.As of 1 September 2015, Bayer MaterialSc.. |
|||
| Tensile Strength, Yield | 6.00 MPa | 870 psi | |
| BASF Lucalen® A 2920 M Ethylene/Acrylate Copolymer Used in the manufacture of economical composite films of Lucalen and PE-LD, and as a primer for aluminum steel composites.Data was collected by ISO methods and provided by BASF. |
|||
| Tensile Strength, Yield | 6.00 MPa | 870 psi | 50 mm/min |
| Arkema Group Evatane® 1003 VN 4 Ethylene Vinyl Acetate EVA copolymer made by high pressure tubular process. Applications Grade for transparent and thermal agricultural film for greenhouse coverage.ISO data provided by the manufacturer, Arkema. |
|||
| Tensile Strength, Yield | 6.00 MPa | 870 psi | ASTM D638 |
| Arkema Group OREVAC® 9309 EVA Terpolymer OREVAC® is a range of ethylene-vinyl acetate copolymers modified by adjunction of polar groups which, when molten, have excellent adhesive properties to various substrates. They are supplied as fre.. |
|||
| Tensile Strength, Yield | 6.00 MPa | 870 psi | Film Property, 50 µm thickness; ASTM D882 |
| Arkema Group OREVAC® 9309 EVA Terpolymer OREVAC® is a range of ethylene-vinyl acetate copolymers modified by adjunction of polar groups which, when molten, have excellent adhesive properties to various substrates. They are supplied as fre.. |
|||
| Tensile Strength, Yield | 6.00 MPa | 870 psi | |
| Trelleborg Commercial Neoprene® C803 Chloroprene CR or Chloroprene is a homopolymer of chloroprene or chlorobutadiene. NEOPRENE®PropertiesExcellent mechanical and abrasion properties even without reinforcing fillers.Reasonable resilience in grade.. |
|||
| Tensile Strength, Yield | 6.00 MPa @Strain 50.0 % |
870 psi @Strain 50.0 % |
50 mm/min |
| Arkema Group Nakan® FKC 911 S PVC, Soft Extrusion Grade NAKAN FKC 911 S is a soft polyvinyl chloride compound developed for L.S.F. insulation and sheeting - BS 5467.ISO data provided by the manufacturer, Arkema. |
|||
| Tensile Strength, Yield | 6.00 - 47.0 MPa @Temperature -40.0 - 100 °C |
870 - 6820 psi @Temperature -40.0 - 212 °F |
Average value: 26.5 MPa Grade Count:1 |
| Overview of materials for High Density Polyethylene (HDPE), Crosslinkable This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Crosslinkable". Each property range of values reported is minimum and .. |
|||
| Tensile Strength, Yield | 6.00 MPa | 870 psi | ASTM D638 |
| A. Schulman POLYFORT™ PX 1040 Information provided by A. Schulman. |
|||
Copyright © lookpolymers.com All Rights Reserved