Fujipoly Industries Sarcon® 85U Thin-Film UR

Category Polymer , Thermoset , Silicone
Manufacturer Fujipoly Industries
Trade Name Sarcon®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Fujipoly Industries Sarcon® 85U Thin-Film UR.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Sarcon UR is Fujipolys originally developed High Heat Conductive/Low Hardness Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Information provided by Fujipoly Industries
Mechanical Properties Metric English Comments
Hardness, Shore A 79
79
ASTM D2240
83
83
150°C for 1,000 hrs; ASTM D2240
85
85
60°C for 500 hrs with 95% RH; ASTM D2240
86
86
200°C for 1,000 hrs; ASTM D2240
Tensile Strength, Yield 2.588 MPa
375.4 psi
3.882 MPa
563.0 psi
60°C for 500 hrs with 95% RH
4.00 MPa
580 psi
150°C for 1,000 hrs
6.00 MPa
870 psi
200°C for 1,000 hrs
Elongation at Yield 47 %
47 %
150°C for 1,000 hrs
50 %
50 %
200°C for 1,000 hrs
83 %
83 %
60°C for 500 hrs with 95% RH
110 %
110 %
Tear Strength 0.700 kN/m
3.99 pli
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 182 °C
360 °F
Minimum Service Temperature, Air -60.0 °C
-76.0 °F
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Volume Resistivity 2.00e+13 ohm-cm
2.00e+13 ohm-cm
60°C for 500 hrs with 95% RH
1.00e+15 ohm-cm
1.00e+15 ohm-cm
1.10e+15 ohm-cm
1.10e+15 ohm-cm
150°C for 1,000 hrs
1.20e+16 ohm-cm
1.20e+16 ohm-cm
200°C for 1,000 hrs
Dielectric Constant 5.13

@Frequency 1000 Hz
 5.13

@Frequency 1000 Hz
 After 1000 hrs at 200°C
5.14

@Frequency 50 Hz
 5.14

@Frequency 50 Hz
 After 1000 hrs at 200°C
5.15

@Frequency 50 Hz
 5.15

@Frequency 50 Hz
 After 1000 hrs at 150°C
5.15

@Frequency 1000 Hz
 5.15

@Frequency 1000 Hz
 After 1000 hrs at 150°C
5.15

@Frequency 1e+6 Hz
 5.15

@Frequency 1e+6 Hz
 After 1000 hrs at 200°C
5.16

@Frequency 1e+6 Hz
 5.16

@Frequency 1e+6 Hz
 After 1000 hrs at 150°C
5.34

@Frequency 1e+6 Hz
 5.34

@Frequency 1e+6 Hz
5.34

@Frequency 1000 Hz
 5.34

@Frequency 1000 Hz
5.35

@Frequency 50 Hz
 5.35

@Frequency 50 Hz
5.51

@Frequency 1e+6 Hz
 5.51

@Frequency 1e+6 Hz
 After 500 hrs at 60°C with 95% RH
5.72

@Frequency 1000 Hz
 5.72

@Frequency 1000 Hz
 After 500 hrs at 60°C with 95% RH
6.03

@Frequency 50 Hz
 6.03

@Frequency 50 Hz
 After 500 hrs at 60°C with 95% RH
Dielectric Strength 16.0 kV/mm
406 kV/in
AC 60 Hz
16.0 kV/mm
406 kV/in
200°C for 1,000 hrs
16.0 kV/mm
406 kV/in
60°C for 500 hrs with 95% RH
17.0 kV/mm
432 kV/in
150°C for 1,000 hrs
Dielectric Breakdown 11000 V
11000 V
Withstand Voltage [V/min]; AC 60 Hz
Dissipation Factor 0.00070

@Frequency 50 Hz
 0.00070

@Frequency 50 Hz
 After 1000 hrs at 150°C
0.00070

@Frequency 1000 Hz
 0.00070

@Frequency 1000 Hz
 After 1000 hrs at 150°C
0.00070

@Frequency 1e+6 Hz
 0.00070

@Frequency 1e+6 Hz
 After 1000 hrs at 150°C
0.00070

@Frequency 1000 Hz
 0.00070

@Frequency 1000 Hz
 After 1000 hrs at 200°C
0.00070

@Frequency 1e+6 Hz
 0.00070

@Frequency 1e+6 Hz
 After 1000 hrs at 200°C
0.0010

@Frequency 1e+6 Hz
 0.0010

@Frequency 1e+6 Hz
0.0011

@Frequency 50 Hz
 0.0011

@Frequency 50 Hz
 After 1000 hrs at 200°C
0.0013

@Frequency 1000 Hz
 0.0013

@Frequency 1000 Hz
0.0025

@Frequency 50 Hz
 0.0025

@Frequency 50 Hz
0.0056

@Frequency 1e+6 Hz
 0.0056

@Frequency 1e+6 Hz
 After 500 hrs at 60°C with 95% RH
0.0194

@Frequency 1000 Hz
 0.0194

@Frequency 1000 Hz
 After 500 hrs at 60°C with 95% RH
0.0521

@Frequency 50 Hz
 0.0521

@Frequency 50 Hz
 After 500 hrs at 60°C with 95% RH
Descriptive Properties Value Comments
Color Grey
Thermal Impedance 0.56°C/W
FTM P-3010; ASTM D5470