Raschig Group EPOXIDUR® 3582 EP Epoxy

Category Polymer , Thermoset , Epoxy , Epoxy, Molded, Glass Fiber Filler , Filled/Reinforced Thermoset
Manufacturer Raschig Group
Trade Name EPOXIDUR®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Raschig Group EPOXIDUR® 3582 EP Epoxy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Glass-fiber reinforced and inorganically filled epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures. Molding compound with a broad spectrum of applications. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS).Processing: Injection and compression moldingInformation provided by the Raschig Group
Physical Properties Metric English Comments
Specific Gravity 1.90 - 2.00 g/cc
1.90 - 2.00 g/cc
ISO 1183
Apparent Bulk Density 0.700 - 1.00 g/cc
0.0253 - 0.0361 lb/in³
ISO 60
Water Absorption <= 0.100 %

@Temperature 23.0 °C,
Time 86400 sec
<= 0.100 %

@Temperature 73.4 °F,
Time 24.0 hour
ISO 62
Linear Mold Shrinkage 0.0030 - 0.0050 cm/cm
0.0030 - 0.0050 in/in
(longitudinal) Injection and Compression; ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength, Yield 60.0 - 80.0 MPa
8700 - 11600 psi
Injection and Compression; ISO 527
Modulus of Elasticity 15.0 - 18.0 GPa
2180 - 2610 ksi
Injection and Compression; ISO 527
Flexural Strength 180 - 210 MPa
26100 - 30500 psi
Injection and Compression; ISO 178
Flexural Modulus 20.0 - 23.0 GPa
2900 - 3340 ksi
Injection and Compression; ISO 178
Compressive Strength 200 - 250 MPa
29000 - 36300 psi
ISO 604
Charpy Impact Unnotched 1.20 - 1.60 J/cm²

@Temperature 23.0 °C
5.71 - 7.61 ft-lb/in²

@Temperature 73.4 °F
Injection and Compression; ISO 179/ 1eU
Charpy Impact, Notched 0.400 - 0.700 J/cm²

@Temperature 23.0 °C
1.90 - 3.33 ft-lb/in²

@Temperature 73.4 °F
Injection and Compression; ISO 179/ 1eA
Thermal Properties Metric English Comments
CTE, linear 15.0 - 20.0 µm/m-°C

@Temperature 50.0 - 150 °C
8.33 - 11.1 µin/in-°F

@Temperature 122 - 302 °F
ISO 11359-2
Thermal Conductivity 0.400 - 0.600 W/m-K
2.78 - 4.16 BTU-in/hr-ft²-°F
ASTM E1461
Deflection Temperature at 1.8 MPa (264 psi) >= 200 °C
>= 392 °F
Injection and Compression; ISO 75-A
Deflection Temperature at 8.0 MPa 180 - 200 °C
356 - 392 °F
Injection and Compression; ISO 75-C
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Shrinkage <= 0.0500 %

@Temperature 110 °C,
Time 605000 sec
<= 0.0500 %

@Temperature 230 °F,
Time 168 hour
ISO 2577
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 - 1.00e+16 ohm-cm
1.00e+15 - 1.00e+16 ohm-cm
IEC 60093
Surface Resistance 1.00e+14 - 1.00e+15 ohm
1.00e+14 - 1.00e+15 ohm
IEC 60093
Dielectric Constant 4.0 - 6.0

@Frequency 100 Hz
4.0 - 6.0

@Frequency 100 Hz
IEC 60250
4.0 - 6.0

@Frequency 1.00e+6 Hz
4.0 - 6.0

@Frequency 1.00e+6 Hz
IEC 60250
Dielectric Strength 20.0 - 30.0 kV/mm
508 - 762 kV/in
IEC 60243-1
Dissipation Factor 0.010 - 0.020

@Frequency 100 Hz
0.010 - 0.020

@Frequency 100 Hz
IEC 60250
0.020 - 0.040

@Frequency 1.00e+6 Hz
0.020 - 0.040

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index >= 250 V
>= 250 V
CTI; IEC 60112
Processing Properties Metric English Comments
Shelf Life 6.00 Month

@Temperature <=20.0 °C
6.00 Month

@Temperature <=68.0 °F
Descriptive Properties Value Comments
Arc Resistance 4 Stufe
ASTM D495
Glow wire flammability test 900/1
IEC 60695 2-12
Glow wire ignitability test 900/1
IEC 60695 2-13
Water Absorption <10 mg
24h/23°C; ISO 62