Polymer Property : Tensile Strength, Yield = 8700 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	35.0 - 60.0 MPa	5080 - 8700 psi	Compression; ISO 527
Raschig Group 2567 AMC Glass fiber-reinforced and inorganically filled polyester molding compound (UP) in various colors. Outstanding mechanical strength similar to BMC/SMC, very good electrical isolation properties and ..
Tensile Strength, Yield	35.0 - 60.0 MPa	5080 - 8700 psi	Compression; ISO 527
Raschig Group 2568 AMC Glass fiber-reinforced polyester molding compound. Very good mechanical strength, very good electrical properties and dimensional stability, heat resistant up to 500°C for short time - usable for s..
Tensile Strength, Yield	35.0 - 60.0 MPa	5080 - 8700 psi	Compression; ISO 527
Raschig Group 5553 DAP Glass-fiber reinforced diallyl phthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensiona..
Tensile Strength, Yield	50.0 - 60.0 MPa	7250 - 8700 psi	Injection; ISO 527
Raschig Group AMPLA® 7500 melamine-modified polyester Organically and inorganically filled melamine modified Polyester molding compound. Low post-shrinkage, very good electrical values, excellent heat resistance, very good sliding behavior and wear sta..
Tensile Strength, Yield	40.0 - 60.0 MPa	5800 - 8700 psi	Compression; ISO 527
Raschig Group MELOPLAS® 182 MF Wood flour-reinforced and inorganically filled, phenol-modified MF molding compound (MPF) in dark colors. Improved dimensional stability and electrical properties as compared with MP 180, high surf..
Tensile Strength, Yield	45.0 - 60.0 MPa	6530 - 8700 psi	Compression; ISO 527
Raschig Group MELOPLAS® 2500 MF Cellulose-reinforced MF molding compound in white and colored shades. Very good electrical properties, high surface hardness, good abrasion- and UV-stability, very good resistance to chemicals - al..
Tensile Strength, Yield	35.0 - 60.0 MPa	5080 - 8700 psi	Compression; ISO 527
Raschig Group RALUPOL® 4385 UP Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, very high arc resistance, very high mechanical values. This product meets the allowed upper limits for heavy..
Tensile Strength, Yield	35.0 - 60.0 MPa	5080 - 8700 psi	Compression; ISO 527
Raschig Group RALUPOL® 4806 UP Glass-fiber reinforced polyester molding compound. Very low mold shrinkage and post-shrinkage, very good mechanical strength, very good electrical values, better performance values compared to UP 80..
Tensile Strength, Yield	35.0 - 60.0 MPa	5080 - 8700 psi	Compression; ISO 527
Raschig Group SURAPLAST 54 UPA Glass fiber reinforced polyester molding compound. Minimal mold shrinkage and post-shrinkage, very good arc resistance, very good mechanical strength. This product meets the allowed upper limits for..
Tensile Strength, Yield	50.0 - 60.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C	7250 - 8700 psi @Thickness 0.0787 in, Temperature 73.4 °F	Type IV, 50 mm/min; ASTM D638
Solvay Specialty Polymers Solef® 6008 Polyvinylidene Fluoride (PVDF) (Unverified Data**) Solef® 6008 PVDF homopolymer is a low-viscosity PVDF resin and is typically processed by injection molding.Information provided by Solvay Specialty Polymers.
Tensile Strength, Yield	50.0 - 60.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C	7250 - 8700 psi @Thickness 0.0787 in, Temperature 73.4 °F	Type IV, 50 mm/min; ASTM D638
Solvay Specialty Polymers Solef® 6010 Polyvinylidene Fluoride (PVDF) (Unverified Data**) Solef® 6010 PVDF homopolymer has medium viscosity and is typically processed by extrusion.Information provided by Solvay Specialty Polymers.
Tensile Strength, Yield	50.0 - 60.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C	7250 - 8700 psi @Thickness 0.0787 in, Temperature 73.4 °F	Type IV, 50 mm/min; ASTM D638
Solvay Specialty Polymers Solef® 6012 Polyvinylidene Fluoride (PVDF) (Unverified Data**) Solef® 6012 PVDF homopolymer is a high-viscosity PVDF resin and is typically processed by extrusion or compression molding.Information provided by Solvay Specialty Polymers.
Tensile Strength, Yield	56.0 - 60.0 MPa	8120 - 8700 psi	50 mm/min; ASTM D638
Solvay Specialty Polymers Solef® 3108/0903 Anti-static PVDF Compound (discontinued **) Key features of this grade: Anti-static, Formulated. Recommended processing is injection. Available as granules.General information about SOLEF® PVDF: SOLEF® PVDF is a fluorinated semi-crystall..
Tensile Strength, Yield	45.0 - 60.0 MPa	6530 - 8700 psi	ISO-DIS 527
Schwartz Technical Plastics LAMIGAMIDÂ® 400 Cast Polyamide 6, Elastomer Modified, Dry Application: gear-wheels, chain-wheels, hydrocyclones, housings, outrigger floatsInformation provided by Schwartz Technical Plastics GmbH
Tensile Strength, Yield	40.0 - 60.0 MPa	5800 - 8700 psi	ISO-DIS 527
Schwartz Technical Plastics LAMINEXÂ® 2101 Cotton Fabric, Phenolic Resin Impregnated Application: bearing segments and prismatic bearingsInformation provided by Schwartz Technical Plastics GmbH
Tensile Strength, Yield	40.0 - 60.0 MPa	5800 - 8700 psi	ISO-DIS 527
Schwartz Technical Plastics LAMINEXÂ® 2141 Cotton Fabric, Phenolic Resin Impregnated, MoS2 Filled Application: bearing segments and prismatic bearingsInformation provided by Schwartz Technical Plastics GmbH
Tensile Strength, Yield	50.0 - 60.0 MPa @Thickness 2.00 mm	7250 - 8700 psi @Thickness 0.0787 in	50 mm/min; ASTM D638
Solvay Specialty Polymers SolefÂ® 1006 Polyvinylidene Fluoride (PVDF) SolefÂ® 1006 PVDF is a very low viscosity homopolymer resin mainly used in injection molding or in multifilament extrusion.Features: Homopolymer; Low ViscosityUses: General PurposeAdditional Prope..
Tensile Strength, Yield	50.0 - 60.0 MPa @Thickness 2.00 mm	7250 - 8700 psi @Thickness 0.0787 in	50 mm/min; ASTM D638
Solvay Specialty Polymers SolefÂ® 6010 Polyvinylidene Fluoride (PVDF) SolefÂ® 6010 PVDF homopolymer has medium viscosity and is typically processed by extrusion.Features: Homopolymer; Medium ViscosityAdditional Properties: Crystallization Heat - ASTM D3417 54.0 to 6..
Tensile Strength, Yield	50.0 - 60.0 MPa @Thickness 2.00 mm	7250 - 8700 psi @Thickness 0.0787 in	50 mm/min; ASTM D638
Solvay Specialty Polymers SolefÂ® 6012 Polyvinylidene Fluoride (PVDF) SolefÂ® 6012 PVDF homopolymer is a high-viscosity PVDF resin and is typically processed by extrusion or compression molding.Features: High Viscosity; HomopolymerAdditional Properties: Crystallizat..
Tensile Strength, Yield	45.0 - 60.0 MPa @Thickness 2.00 mm	6530 - 8700 psi @Thickness 0.0787 in	50 mm/min; ASTM D638
Solvay Specialty Polymers SolefÂ® 9007 Polyvinylidene Fluoride (PVDF) SolefÂ® 9007 PVDF homopolymer has low viscosity and is used in film extrusion and injection molding.Features: Homopolymer; Low ViscosityAdditional Properties: Crystallization Heat - ASTM D3418 53...
Tensile Strength, Yield	50.0 - 60.0 MPa	7250 - 8700 psi	Typical
ATI Allegheny Ludlum AL 20™ Plate Specialty Steel The N08020 alloy has been available for many years and has found applications in many environments, such as in chlorides and in sulfuric and sulfurous acids.Although AL 20 alloy was developed for im..
Tensile Strength, Yield	50.0 - 60.0 MPa	7250 - 8700 psi	ISO 527
Beijing Ranger Chem BLUESTAR® 1084 PBT Can be used directly for spinning, and producing color concentrates. It can also be used for production after reinforcement & compounding.Information provided by Beijing Ranger Chemical Co.
Tensile Strength, Yield	50.0 - 60.0 MPa	7250 - 8700 psi	ISO 527
Beijing Ranger Chem BLUESTAR® 1110 PBT Can be used directly for spinning, or it can be used after reinforcement & compounding. It can also be used to produce cable sheath through tackificationInformation provided by Beijing Ranger Chemic..
Tensile Strength, Yield	45.0 - 60.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C	6530 - 8700 psi @Thickness 0.0787 in, Temperature 73.4 °F	Type IV, 50 mm/min; ASTM D638
Solvay Specialty Polymers Solef® 9007 Polyvinylidene Fluoride (PVDF) (Unverified Data**) Solef® 9007 PVDF homopolymer has low viscosity and is used in film extrusion and injection molding.Information provided by Solvay Specialty Polymers.
Tensile Strength, Yield	45.0 - 60.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C	6530 - 8700 psi @Thickness 0.0787 in, Temperature 73.4 °F	Type IV, 50 mm/min; ASTM D638
Solvay Specialty Polymers Solef® 9009 Polyvinylidene Fluoride (PVDF) (discontinued **) Solef® 9009 PVDF homopolymer has low/medium viscosity and is used in film extrusion and injection molding.Information provided by Solvay Specialty Polymers.
Tensile Strength, Yield	45.0 - 60.0 MPa	6530 - 8700 psi	Compression; ISO 527
Raschig Group MELOPLAS® 180 MF Wood flour-reinforced, phenol-modified MF molding compound (MPF) in dark colors. High surface hardness, good mechanical strength and electrical properties, good heat resistance. Self-extinguishing ..
Tensile Strength, Yield	50.0 - 60.0 MPa	7250 - 8700 psi	ISO 527
Beijing Ranger Chem BLUESTAR® 1120 PBT Can be used directly to produce cable sheathInformation provided by Beijing Ranger Chemical Co.
Tensile Strength, Yield	28.0 - 60.0 MPa	4060 - 8700 psi	Average value: 42.2 MPa Grade Count:17
Overview of materials for Acrylic, Impact Modified, Molded This property data is a summary of similar materials in the MatWeb database for the category "Acrylic, Impact Modified, Molded". Each property range of values reported is minimum and maximum values ..
Tensile Strength, Yield	13.8 - 60.0 MPa	2000 - 8700 psi	Average value: 29.2 MPa Grade Count:76
Overview of materials for Polypropylene with 40% Talc Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 40% Talc Filler". Specific grades with primary filler content between 35% and 44% are..
Tensile Strength, Yield	35.0 - 60.0 MPa	5080 - 8700 psi	Average value: 55.8 MPa Grade Count:6
Overview of materials for Polytrimethylene Terephthalate (PTT) This property data is a summary of similar materials in the MatWeb database for the category "Polytrimethylene Terephthalate (PTT)". Each property range of values reported is minimum and maximum val..