BASF Capron® 8202 NL Nylon 6 (DAM)  (discontinued **)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Capron® 8202 NL Nylon 6 (DAM)  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by BASF Corporation.Capron® is no longer a part of the BASF standard line. The BASF nylon products have been consolidated in the Ultramid ® line.
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
ISO 1183
Water Absorption 1.6 %
1.6 %
24 hr.; ISO 62
9.5 %
9.5 %
ISO 62
Moisture Absorption at Equilibrium 2.7 %
2.7 %
23°C/50% R.H.; ISO 62
Viscosity Measurement 48
48
Formic Acid; ASTM D789
Linear Mold Shrinkage 0.012 cm/cm
0.012 in/in
MD; ASTM Test
Mechanical Properties Metric English Comments
Hardness, Rockwell R 119
119
ASTM D785
Tensile Strength at Break 75.0 MPa
10900 psi
0.2 in/min; ASTM D638
Tensile Strength, Yield 79.0 MPa
11500 psi
50 mm/min; ISO 527
79.0 MPa
11500 psi
2 in/min; ASTM D638
25.0 MPa

@Temperature 120 °C
3630 psi

@Temperature 248 °F
ASTM D638
25.0 MPa

@Temperature 120 °C
3630 psi

@Temperature 248 °F
ISO 527
35.0 MPa

@Temperature 80.0 °C
5080 psi

@Temperature 176 °F
ASTM D638
35.0 MPa

@Temperature 80.0 °C
5080 psi

@Temperature 176 °F
ISO 527
125 MPa

@Temperature -40.0 °C
18100 psi

@Temperature -40.0 °F
ASTM D638
125 MPa

@Temperature -40.0 °C
18100 psi

@Temperature -40.0 °F
ISO 527
Elongation at Break 25 %
25 %
50 mm/min; Nominal; ISO 527
55 %
55 %
2 in/min; ASTM D638
Elongation at Yield 4.0 %
4.0 %
50 mm/min; ISO 527
4.0 %
4.0 %
2 in/min; ASTM D638
36 %

@Temperature 120 °C
36 %

@Temperature 248 °F
ASTM D638
42 %

@Temperature 80.0 °C
42 %

@Temperature 176 °F
ASTM D638
Modulus of Elasticity 0.360 GPa

@Temperature 120 °C
52.2 ksi

@Temperature 248 °F
ISO 527
0.485 GPa

@Temperature 80.0 °C
70.3 ksi

@Temperature 176 °F
ISO 527
Tensile Modulus 3.10 GPa
450 ksi
1 mm/min; ISO 527
Flexural Strength 110 MPa
16000 psi
ASTM D790
20.0 MPa

@Temperature 120 °C
2900 psi

@Temperature 248 °F
ASTM D790
20.0 MPa

@Temperature 93.0 °C
2900 psi

@Temperature 199 °F
ASTM D790
30.0 MPa

@Temperature 65.0 °C
4350 psi

@Temperature 149 °F
ASTM D790
170 MPa

@Temperature -40.0 °C
24700 psi

@Temperature -40.0 °F
ASTM D790
Flexural Modulus 2.83 GPa
410 ksi
ASTM D790
0.305 GPa

@Temperature 120 °C
44.2 ksi

@Temperature 248 °F
ASTM D790
0.350 GPa

@Temperature 93.0 °C
50.8 ksi

@Temperature 199 °F
ASTM D790
0.500 GPa

@Temperature 65.0 °C
72.5 ksi

@Temperature 149 °F
ASTM D790
3.01 GPa

@Temperature -40.0 °C
437 ksi

@Temperature -40.0 °F
ASTM D790
Izod Impact, Notched 0.600 J/cm
1.12 ft-lb/in
ASTM D256
0.500 J/cm

@Temperature -40.0 °C
0.937 ft-lb/in

@Temperature -40.0 °F
ASTM D256
Thermal Properties Metric English Comments
CTE, linear 83.0 µm/m-°C

@Temperature 20.0 °C
46.1 µin/in-°F

@Temperature 68.0 °F
ASTM E831
Melting Point 220 °C
428 °F
10 K/min
220 °C
428 °F
ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 178 °C
352 °F
ISO 75
178 °C
352 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 60.0 °C
140 °F
ISO 75
65.0 °C
149 °F
ASTM D648
Descriptive Properties Value Comments
Additive Unfilled
Color Natural
Commercial Status (March 2007) Active America
FDA 21 CFR 177.1500
Form Pellets
Impact Modified No
Injection molding Processable
Primary Processing Technique Film Extrusion