Total PPC 3666 Polypropylene, Heterophasic Copolymer, Extrusion

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Extrusion Grade
Manufacturer	Total Atofina
Trade Name	PPC
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Total PPC 3666 Polypropylene, Heterophasic Copolymer, Extrusion.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Polypropylene PPC 3666 is a heterophasic copolymer with a Melt Flow index of 1.5 g/10 min. This resin offers an outstanding processability in combination with good melt strength and excellent mechanical properties.Polypropylene PPC 3666 has been especially developed for the extrusion of corrugated cardboard. It offers an excellent performance as well in other applications, include sheet and film extrusion and thermoforming.Information provided by Total Petrochemicals.

Physical Properties	Metric	English	Comments
Specific Gravity	0.905 g/cc	0.905 g/cc	ISO 1183
Bulk Density	0.525 g/cc	0.0190 lb/in³	ISO 1183
Melt Flow	1.5 g/10 min @Load 2.16 kg, Temperature 230 °C	1.5 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	77	77	ISO 2039-2
Tensile Strength, Yield	24.0 MPa	3480 psi	ISO 527-2
Elongation at Yield	11 %	11 %	ISO 527-2
Tensile Modulus	1.30 GPa	189 ksi	ISO 527-2
Flexural Modulus	1.20 GPa	174 ksi	ISO 178
Izod Impact, Notched (ISO)	7.00 kJ/m² @Temperature -20.0 °C	3.33 ft-lb/in² @Temperature -4.00 °F	ISO 180
	>= 50.0 kJ/m² @Temperature 23.0 °C	>= 23.8 ft-lb/in² @Temperature 73.4 °F	ISO 180
Charpy Impact, Notched	0.800 J/cm² @Temperature -20.0 °C	3.81 ft-lb/in² @Temperature -4.00 °F	ISO 179
	>= 5.00 J/cm² @Temperature 23.0 °C	>= 23.8 ft-lb/in² @Temperature 73.4 °F	ISO 179

Thermal Properties	Metric	English	Comments
Melting Point	165 °C	329 °F	ISO 3146
Deflection Temperature at 0.46 MPa (66 psi)	92.0 °C	198 °F	120°C per hour; ISO 752
Deflection Temperature at 1.8 MPa (264 psi)	50.0 °C	122 °F	120°C per hour; ISO 752
Vicat Softening Point	60.0 °C @Load 5.10 kg	140 °F @Load 11.2 lb	50°C per hour; ISO 306
	130 °C @Load 1.02 kg	266 °F @Load 2.25 lb	50°C per hour; ISO 306