- Polymer Property : Tensile Strength, Yield = 13.1 MPa
Polymer Property : Tensile Strength, Yield = 13.1 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 13.1 MPa | 1900 psi | Type IV, 510 mm/min; ASTM D638 |
| PolyOne Geon™ Vinyl Wire & Cable JC404HX Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne |
|||
| Tensile Strength, Yield | 13.1 MPa | 1900 psi | Type IV, 510 mm/min; ASTM D638 |
| PolyOne Geon™ Vinyl Wire & Cable WJKC505L Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications. Provisional Product Information - Physical and Mechanical properties based on initial production.Information provide.. |
|||
| Tensile Strength, Yield | 13.1 MPa | 1900 psi | |
| Resinlab® CYNERGY CA6602 Adhesive Description: The CYNERGY 6600 SERIES are modified to provide greatly reduced odor and frosting of plastics. These products are ideal for bonding dissimilar materials with excellent performance on a .. |
|||
| Tensile Strength, Yield | 13.1 MPa | 1900 psi | ASTM D638 |
| M. Holland Company LL700 LLDPE
(discontinued **) Features: High ESCR (Stress Crack Resist.), Good Flexibility, High FlowUses: Closures, Household GoodsProcessing Method: Injection MoldingInformation provided by M. Holland. |
|||
| Tensile Strength, Yield | 13.1 MPa | 1900 psi | |
| Resinlab® CYNERGY CA6701 Adhesive Description: The CYNERGY 6700 SERIES are modified to provide greatly reduced odor and a further reduction of bloom or frosting of plastics when compared to the 6600 Series. These products are ideal .. |
|||
| Tensile Strength, Yield | 13.1 MPa | 1900 psi | @100% Elongation; ASTM D1414 |
| Greene Tweed CHEMRAZ® SD625 Perfluoroelastomer Chemraz® SD625, a black-colored perfluoroelastomer, offers the broadest chemical resistance of any elastomer, combining the resilience and sealing force of an elastomer with chemical resistance a.. |
|||
| Tensile Strength, Yield | 13.1 MPa | 1900 psi | Elastic; ASTM D412 |
| Multibase Multi-Flex® D 4107 C Black TPE Thermoplastic Elastomer Features: Chemical Resistance, Good Colorability, GoodElasticity, HighElectrically InsulatingFlame RetardantFlexibility, GoodHeat StabilizedOzone ResistantProcessability, GoodUV Resistance, Good I.. |
|||
| Tensile Strength, Yield | 13.1 MPa | 1900 psi | 100%; ASTM D412 |
| Teknor Apex APEX® 3201-90 Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTMUses-Automotive Applications, Non-specific Food Applications, General Purpose, Medical Applications, Modeling.. |
|||
| Tensile Strength, Yield | 13.1 MPa | 1900 psi | ASTM D412 |
| Teknor Apex APEX® 3210-85 Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTMFeatures-Sterilizable, Radiation Uses-Automotive Applications, Connectors, Non-specific Food Applications, Ge.. |
|||
| Tensile Strength, Yield | 13.1 MPa | 1900 psi | ASTM D412 |
| Teknor Apex APEX® 3301-70 Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTM Uses-Automotive Applications, Food Service Applications, General Purpose, Medical Applications, Profiles, To.. |
|||
| Tensile Strength, Yield | 13.1 MPa | 1900 psi | ASTM D412 |
| Teknor Apex APEX® 3310-75 Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTMFeatures-Sterilizable, RadiationUses-Automotive Applications, Food Service Applications, General Purpose, Med.. |
|||
| Tensile Strength, Yield | 13.1 MPa | 1900 psi | Expanded Compound; ASTM D638 |
| Borealis Borcell™ HE1344 High Density Polyethylene Compound for Cellular Insulation of Data Cables Borcell HE1344 is a high-molecular weight, high-density polyethylene (HDPE) insulation compound containing an industry approved non plate-out chemical blowing agent. It contains the required levels.. |
|||
| Tensile Strength, Yield | 13.1 MPa | 1900 psi | Expanded Compound; ASTM D638 |
| Borealis Borcell™ HE1345 High Density Polyethylene Compound for Cellular Insulation of Telephone Singles Borcell HE1345 is a high molecular weight, high-density polyethylene (HDPE) insulation compound containing an industry approved non plate-out chemical blowing agent and contains the required levels .. |
|||
| Tensile Strength, Yield | 13.1 MPa | 1900 psi | Cable - At 2 inch/min; ASTM D638 |
| Borealis Casico™ FR4803 Non-Halogen Flame Retardant Compound for Low Voltage Insulation and Jacketing Borstar FR4803 is a natural, thermoplastic polyolefin compound designed for flame retardant low voltage wire insulation and jacketing. As such, FR4803 offers a unique combination of good extrusion p.. |
|||
| Tensile Strength, Yield | 13.1 MPa | 1900 psi | ASTM D412 |
| Teknor Apex UNIPRENE® 7400-40D Thermoplastic Elastomer Information provided by Teknor Apex Company |
|||
| Tensile Strength, Yield | 13.1 MPa | 1900 psi | 100% Retention, Hot Air Aging, 22 hrs at 70°C |
| Teknor Apex UNIPRENE® 7400-40D Thermoplastic Elastomer Information provided by Teknor Apex Company |
|||
| Tensile Strength, Yield | 13.1 MPa | 1900 psi | 2"/min; ASTM D638 |
| A. Schulman CP810-01 Natural Linear, Low-Density Polyethylene DescriptionCP 810-01 is a linear low-density polyethylene resin with excellent molding characteristics and good low temperature impact. ApplicationCP 810-01 meets the specifications contained in FDA.. |
|||
| Tensile Strength, Yield | 13.1 MPa | 1900 psi | transverse direction; ASTM D882 |
| A. Schulman CP878-01 Natural Linear, Low-Density Polyethylene DescriptionCP 878-01 Natural is a linear low-density polyethylene having good tensile, stiffness, and toughness properties. ApplicationCP 878-01 meets FDA Regulation 21 CFR 177.1520(c)3.1 and 3.2.In.. |
|||
| Tensile Strength, Yield | 13.1 MPa | 1900 psi | Cable - At 2 inch/min; ASTM D638 |
| Borealis Casico™ FR4802 Non-Halogen Flame Retardant Insulation/Jacketing Compound Borstar FR4802 is a natural, thermoplastic polyolefin compound designed for flame retardant low voltage wire insulation and jacketing. As such, FR4802 offers a unique combination of good extrusion p.. |
|||
| Tensile Strength, Yield | 13.1 MPa | 1900 psi | transverse direction; ASTM D882 |
| A. Schulman CP878-01 Natural Linear, Low-Density Polyethylene DescriptionCP 878-01 Natural is a linear low-density polyethylene having good tensile, stiffness, and toughness properties. ApplicationCP 878-01 meets FDA Regulation 21 CFR 177.1520(c)3.1 and 3.2.In.. |
|||
| Tensile Strength, Yield | 13.1 MPa | 1900 psi | |
| TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 120 PHR Iceberg Clay Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
| Tensile Strength, Yield | 13.1 MPa | 1900 psi | 50 mm/min cross speed; ASTM D638 |
| DuPont™ Surlyn® 8660 Ionomer Resin, Sodium Surlyn® 8660 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with sodium ions. The amount of MAA and neu.. |
|||
| Tensile Strength, Yield | 13.1 MPa | 1900 psi | ASTM D-638 |
| Axiall 6730 Moldings & Extrusions Flexible PVC Injection molding compound with good processing characteristics that allow fast cycles and smooth unblemished surfaces on the finished product. Exhibits good weathering and low temperature properti.. |
|||
| Tensile Strength, Yield | 13.1 MPa | 1900 psi | ASTM D-638 |
| Axiall 8730 Moldings & Extrusions Flexible PVC A high quality, profile extrusion compound recommended for those applications where exceptional low temperature performance is required.Information provided by Georgia GulfGeorgia Gulf became Axiall.. |
|||
| Tensile Strength, Yield | 13.1 MPa | 1900 psi | ASTM D-638 |
| Axiall 8758 Moldings & Extrusions Flexible PVC A general purpose extrusion compound recommended for extruded shapes, weatherstrips and flexible gaskets. Formulated for good UV light resistance and low temperature properties.Information provided.. |
|||
| Tensile Strength, Yield | 13.1 MPa | 1900 psi | ASTM D-638 |
| Axiall 8779 Moldings & Extrusions Flexible PVC Non-lead stabilized, general purpose extrusion compound designed for PVC waterstops per Corps of Engineers Specification CRD-C 572-74.Information provided by Georgia GulfGeorgia Gulf became Axiall C.. |
|||
| Tensile Strength, Yield | 13.1 MPa | 1900 psi | |
| TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 90 PHR Hi-Sil 233 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
| Tensile Strength, Yield | 13.1 MPa | 1900 psi | 2"/min; ASTM D638 |
| A. Schulman CP810-01 Natural Linear, Low-Density Polyethylene DescriptionCP 810-01 is a linear low-density polyethylene resin with excellent molding characteristics and good low temperature impact. ApplicationCP 810-01 meets the specifications contained in FDA.. |
|||
| Tensile Strength, Yield | 13.1 MPa | 1900 psi | 500 mm/min (20 in./min.); ASTM D638, Type IV Specimen |
| Eastman D4041-P Polyethylene
(discontinued **) Low-density polyethylene D4041-P is a recommended for use in the boardstock coating industry for applications such as breadboard, cupstock, and liquid packaging board. This resin has low neck-in an.. |
|||