Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 13.1 MPa | 1900 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Wire & Cable JC404HX Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne |
|||
Tensile Strength, Yield | 13.1 MPa | 1900 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Wire & Cable MJF114A Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne |
|||
Tensile Strength, Yield | 13.1 MPa | 1900 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Wire & Cable WJKC505L Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications. Provisional Product Information - Physical and Mechanical properties based on initial production.Information provide.. |
|||
Tensile Strength, Yield | 13.1 MPa | 1900 psi | |
Resinlab® CYNERGY CA6602 Adhesive Description: The CYNERGY 6600 SERIES are modified to provide greatly reduced odor and frosting of plastics. These products are ideal for bonding dissimilar materials with excellent performance on a .. |
|||
Tensile Strength, Yield | 13.1 MPa | 1900 psi | |
Resinlab® CYNERGY CA6702 Adhesive Description: The CYNERGY 6700 SERIES are modified to provide greatly reduced odor and a further reduction of bloom or frosting of plastics when compared to the 6600 Series. These products are ideal .. |
|||
Tensile Strength, Yield | 13.1 MPa | 1900 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Wire & Cable WJCK502L Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications. Provisional Product Information - Physical and Mechanical properties based on initial production.Information provide.. |
|||
Tensile Strength, Yield | 13.1 MPa | 1900 psi | |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 120 PHR Iceberg Clay Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | >= 13.1 MPa | >= 1900 psi | ASTM D-882 |
Saint-Gobain Norton® T-200 Mechanical Grade PTFE Sheet (0.031" thick) Features/Benefits: Outstanding heat and chemical resistance; High dielectric strength; Anti-stick properties; Can be chemically etched for bondability; Applications include laminate release sheets, .. |
|||
Tensile Strength, Yield | 13.1 MPa | 1900 psi | ASTM D412 |
Teknor Apex APEX® 3301-70 Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTM Uses-Automotive Applications, Food Service Applications, General Purpose, Medical Applications, Profiles, To.. |
|||
Tensile Strength, Yield | 13.1 MPa | 1900 psi | ASTM D412 |
Teknor Apex APEX® 3310-75 Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTMFeatures-Sterilizable, RadiationUses-Automotive Applications, Food Service Applications, General Purpose, Med.. |
|||
Tensile Strength, Yield | 13.1 MPa | 1900 psi | ASTM D412 |
Teknor Apex APEX® 90-A41R-70-NT Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTM Uses- Medical Applications, Tubing, Appearance-ClearForms-PelletsProcessing-ExtrusionInformation provided by.. |
|||
Tensile Strength, Yield | 13.1 MPa | 1900 psi | ASTM D412 |
Teknor Apex Flexalloy® 3500-60 Polyvinyl Chloride Elastomer Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTM Features: Ultra High MWUses- Tubing, Pump PartsForms-PelletsProcessing- ExtrusionInformation provided by Te.. |
|||
Tensile Strength, Yield | 13.1 MPa | 1900 psi | Longitudinal |
Saint-Gobain Norton® Fluorglas® Chemfilm® R128/R129 Premium Grade Extruded Full Density PTFE Film (0.005" thick) Description: Full Density Unsintered Tape is used as primary insulation for high-temperature wires, jackets and cables and wall for convoluted hose. It meets the requirements of component insulation.. |
|||
Tensile Strength, Yield | 13.1 MPa | 1900 psi | Expanded Compound; ASTM D638 |
Borealis Borcell™ HE1344 High Density Polyethylene Compound for Cellular Insulation of Data Cables Borcell HE1344 is a high-molecular weight, high-density polyethylene (HDPE) insulation compound containing an industry approved non plate-out chemical blowing agent. It contains the required levels.. |
|||
Tensile Strength, Yield | 13.1 MPa | 1900 psi | transverse direction; ASTM D882 |
A. Schulman CP878-01 Natural Linear, Low-Density Polyethylene DescriptionCP 878-01 Natural is a linear low-density polyethylene having good tensile, stiffness, and toughness properties. ApplicationCP 878-01 meets FDA Regulation 21 CFR 177.1520(c)3.1 and 3.2.In.. |
|||
Tensile Strength, Yield | 13.1 MPa | 1900 psi | Cable - At 2 inch/min; ASTM D638 |
Borealis Casico™ FR4803 Non-Halogen Flame Retardant Compound for Low Voltage Insulation and Jacketing Borstar FR4803 is a natural, thermoplastic polyolefin compound designed for flame retardant low voltage wire insulation and jacketing. As such, FR4803 offers a unique combination of good extrusion p.. |
|||
Tensile Strength, Yield | 13.1 MPa | 1900 psi | ASTM D412 |
Teknor Apex UNIPRENE® 7400-40D Thermoplastic Elastomer Information provided by Teknor Apex Company |
|||
Tensile Strength, Yield | 13.1 MPa | 1900 psi | 100% Retention, Hot Air Aging, 22 hrs at 70°C |
Teknor Apex UNIPRENE® 7400-40D Thermoplastic Elastomer Information provided by Teknor Apex Company |
|||
Tensile Strength, Yield | 13.1 MPa | 1900 psi | 2"/min; ASTM D638 |
A. Schulman CP810-01 Natural Linear, Low-Density Polyethylene DescriptionCP 810-01 is a linear low-density polyethylene resin with excellent molding characteristics and good low temperature impact. ApplicationCP 810-01 meets the specifications contained in FDA.. |
|||
Tensile Strength, Yield | 13.1 MPa | 1900 psi | transverse direction; ASTM D882 |
A. Schulman CP878-01 Natural Linear, Low-Density Polyethylene DescriptionCP 878-01 Natural is a linear low-density polyethylene having good tensile, stiffness, and toughness properties. ApplicationCP 878-01 meets FDA Regulation 21 CFR 177.1520(c)3.1 and 3.2.In.. |
|||
Tensile Strength, Yield | 13.1 MPa | 1900 psi | 2"/min; ASTM D638 |
A. Schulman CP810-01 Natural Linear, Low-Density Polyethylene DescriptionCP 810-01 is a linear low-density polyethylene resin with excellent molding characteristics and good low temperature impact. ApplicationCP 810-01 meets the specifications contained in FDA.. |
|||
Tensile Strength, Yield | 13.1 MPa | 1900 psi | transverse direction; ASTM D882 |
A. Schulman CP878-01 Natural Linear, Low-Density Polyethylene DescriptionCP 878-01 Natural is a linear low-density polyethylene having good tensile, stiffness, and toughness properties. ApplicationCP 878-01 meets FDA Regulation 21 CFR 177.1520(c)3.1 and 3.2.In.. |
|||
Tensile Strength, Yield | 13.1 MPa | 1900 psi | Cable - At 2 inch/min; ASTM D638 |
Borealis Casico™ FR4802 Non-Halogen Flame Retardant Insulation/Jacketing Compound Borstar FR4802 is a natural, thermoplastic polyolefin compound designed for flame retardant low voltage wire insulation and jacketing. As such, FR4802 offers a unique combination of good extrusion p.. |
|||
Tensile Strength, Yield | 13.1 MPa | 1900 psi | |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 90 PHR Hi-Sil 233 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 13.1 MPa | 1900 psi | |
Dow LDPE 5004IM Low Density Polyethylene DOW LDPE 5004IM resin is a broad molecular weight distribution homopolymer designed to offer good impact strength and rigidity with high ESCR. This resin has good processability over a wide range of.. |
|||
Tensile Strength, Yield | 13.1 MPa | 1900 psi | ASTM D-638 |
Axiall 50897 Moldings & Extrusions Flexible PVC Migration resistant, flexible PVC compound recommended for injection molding and extrusion applications.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||
Tensile Strength, Yield | 13.1 MPa | 1900 psi | ASTM D-638 |
Axiall 8779 Moldings & Extrusions Flexible PVC Non-lead stabilized, general purpose extrusion compound designed for PVC waterstops per Corps of Engineers Specification CRD-C 572-74.Information provided by Georgia GulfGeorgia Gulf became Axiall C.. |
|||
Tensile Strength, Yield | 13.1 MPa | 1900 psi | ASTM D-638 |
Axiall 19840 Wire & Cable Flexible PVC 105°C rated insulation suitable for 1/64 wall. Recommended for AWM applications.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||
Tensile Strength, Yield | 13.1 MPa | 1900 psi | 2"/min; ASTM D638 |
A. Schulman CP810-01 Natural Linear, Low-Density Polyethylene DescriptionCP 810-01 is a linear low-density polyethylene resin with excellent molding characteristics and good low temperature impact. ApplicationCP 810-01 meets the specifications contained in FDA.. |
|||
Tensile Strength, Yield | 13.1 MPa | 1900 psi | ASTM D-638 |
Axiall 18752 Wire & Cable Flexible PVC Electrical grade extrusion compound with excellent low temperature performance. Maximum service temperature of 105°CInformation provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 20.. |