Solvay TECHNYL® A 230 V13 PA66, 13% glass fiber, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® A 230 V13 PA66, 13% glass fiber, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Modified polyamide 66, reinforced with 13% of glass fiber, with improved impact resistance, for injection molding.Available in: Europe and North AmericaProduct Applications: In addition to primary polyamide properties, TECHNYL® A230 V13 offers a very good rigidity / impact resistance compromise. This grade is used in the automotive industry, such as: belt covers, fasteners. This product is available in natural, black, grey, and in colors on request.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183/A |
| Water Absorption | 0.75 % @Temperature 23.0 °C, Time 86400 sec |
0.75 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage | 0.0085 cm/cm | 0.0085 in/in | Isotropy |
| Linear Mold Shrinkage, Flow | 0.0085 cm/cm | 0.0085 in/in | |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527 Type 1A |
| Tensile Strength, Yield | 100 MPa | 14500 psi | ISO 527 type 1 A |
| Elongation at Break | 100 % | 100 % | ISO 527 Type 1A |
| Tensile Modulus | 5.50 GPa | 798 ksi | ISO 527 Type 1A |
| Flexural Modulus | 4.20 GPa | 609 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | ISO 180/1eA |
| Charpy Impact Unnotched | 6.50 J/cm² | 30.9 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C @Temperature 23.0 - 85.0 °C |
27.8 µin/in-°F @Temperature 73.4 - 185 °F |
ISO 11359 |
| Melting Point | 263 °C | 505 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 225 °C | 437 °F | ISO 75/Af |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
1210 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 3.5 | 3.5 | IEC 60250 |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | IEC 60243 |
| Dissipation Factor | 0.010 | 0.010 | IEC 60250 |
| Comparative Tracking Index | 525 V | 525 V | Solution B; IEC 60112 |
| 600 V | 600 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 260 - 270 °C | 500 - 518 °F | |
| Front Barrel Temperature | 280 - 290 °C | 536 - 554 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 270-280°C |
Users viewing this material also viewed the following:
- Quadrant EPP Ertalyte® TX PET + solid lubricant, extruded (ISO Data)
- Polykemi AB SCANMID 6 B12^ NH9 Nylon 6, Flame Retardant, Halogen Free
- Resinlab® RC8075 Anaerobic Retaining Compound
- Iran Petrochemical (PCC) X 30 S Polypropylene Film
- Techmer ES HiFill® HDPE E GF40 40% Glass Filled
- Solvay TECHNYL® A 216 NATURAL FA PA66, DRY
- A. Schulman POLYFLAM™ FPP 1007E Talc Filled Homopolymer Polypropylene
- A. Schulman POLYFORT™ PP 2268UX Heat Resistant Polypropylene
- ExxonMobil Santoprene® 8211-75 Thermoplastic Elastomer
- Barlog Plastics KEBAFORM C 8027 POM Copolymer, 30% mineral reinforced
Copyright © lookpolymers.com All Rights Reserved