LATI Latamid 6 S/30 PA 6, 30% Glass Bead Reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Bead Filled
Manufacturer LATI
Trade Name Latamid
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latamid 6 S/30 PA 6, 30% Glass Bead Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 6 (PA6) based compound. Glass beads. Very high dimensional stability.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.34 g/cc
0.0484 lb/in³
Linear Mold Shrinkage, Flow 0.0090 - 0.012 cm/cm
0.0090 - 0.012 in/in
Linear Mold Shrinkage, Transverse 0.010 - 0.0125 cm/cm
0.010 - 0.0125 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 20.0 MPa

@Temperature 150 °C
 2900 psi

@Temperature 302 °F
25.0 MPa

@Temperature 120 °C
 3630 psi

@Temperature 248 °F
35.0 MPa

@Temperature 90.0 °C
 5080 psi

@Temperature 194 °F
45.0 MPa

@Temperature 60.0 °C
 6530 psi

@Temperature 140 °F
70.0 MPa

@Temperature 23.0 °C
 10200 psi

@Temperature 73.4 °F
Elongation at Break 4.0 %

@Temperature 23.0 °C
 4.0 %

@Temperature 73.4 °F
10 %

@Temperature 60.0 °C
 10 %

@Temperature 140 °F
15 %

@Temperature 90.0 °C
 15 %

@Temperature 194 °F
20 %

@Temperature 120 °C
 20 %

@Temperature 248 °F
35 %

@Temperature 150 °C
 35 %

@Temperature 302 °F
Elongation at Yield 8.0 %

@Temperature 60.0 °C
 8.0 %

@Temperature 140 °F
12 %

@Temperature 90.0 °C
 12 %

@Temperature 194 °F
12 %

@Temperature 120 °C
 12 %

@Temperature 248 °F
14 %

@Temperature 150 °C
 14 %

@Temperature 302 °F
Tensile Modulus 0.580 GPa

@Temperature 150 °C
 84.1 ksi

@Temperature 302 °F
0.700 GPa

@Temperature 120 °C
 102 ksi

@Temperature 248 °F
1.10 GPa

@Temperature 90.0 °C
 160 ksi

@Temperature 194 °F
2.00 GPa

@Temperature 60.0 °C
 290 ksi

@Temperature 140 °F
4.20 GPa

@Temperature 23.0 °C
 609 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 2.50 J/cm²
11.9 ft-lb/in²
Charpy Impact, Notched 0.300 J/cm²
1.43 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 90.0 °C
194 °F
Deflection Temperature at 0.46 MPa (66 psi) 195 °C
383 °F
Deflection Temperature at 1.8 MPa (264 psi) 85.0 °C
185 °F
Vicat Softening Point 205 °C

@Load 5.00 kg
 401 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 240 - 260 °C
464 - 500 °F
Mold Temperature 70.0 - 100 °C
158 - 212 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
 194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa