LATI Kelon® A FR H2 CET/35-V2 PA 66, 35% Mineral Reinforced, Flame Retardant, Heat Stabilized

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Mineral Filled
Manufacturer LATI
Trade Name Kelon® A
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Kelon® A FR H2 CET/35-V2 PA 66, 35% Mineral Reinforced, Flame Retardant, Heat Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 66 (PA66) based compound. Heat stabilized. Mineral filler. UL94 V-2 classified, with brominated flame retardants, PBB/PBDE free.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.57 g/cc
0.0567 lb/in³
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
Linear Mold Shrinkage, Transverse 0.0060 - 0.0075 cm/cm
0.0060 - 0.0075 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 20.0 MPa

@Temperature 150 °C
 2900 psi

@Temperature 302 °F
25.0 MPa

@Temperature 120 °C
 3630 psi

@Temperature 248 °F
35.0 MPa

@Temperature 90.0 °C
 5080 psi

@Temperature 194 °F
55.0 MPa

@Temperature 60.0 °C
 7980 psi

@Temperature 140 °F
70.0 MPa

@Temperature 23.0 °C
 10200 psi

@Temperature 73.4 °F
Elongation at Break 1.5 %

@Temperature 23.0 °C
 1.5 %

@Temperature 73.4 °F
2.5 %

@Temperature 60.0 °C
 2.5 %

@Temperature 140 °F
7.0 %

@Temperature 90.0 °C
 7.0 %

@Temperature 194 °F
15 %

@Temperature 120 °C
 15 %

@Temperature 248 °F
25 %

@Temperature 190 °C
 25 %

@Temperature 374 °F
Elongation at Yield 6.0 %

@Temperature 90.0 °C
 6.0 %

@Temperature 194 °F
10 %

@Temperature 120 °C
 10 %

@Temperature 248 °F
>= 10 %

@Temperature 150 °C
 >= 10 %

@Temperature 302 °F
Tensile Modulus 1.60 GPa

@Temperature 150 °C
 232 ksi

@Temperature 302 °F
2.10 GPa

@Temperature 120 °C
 305 ksi

@Temperature 248 °F
3.80 GPa

@Temperature 90.0 °C
 551 ksi

@Temperature 194 °F
7.30 GPa

@Temperature 60.0 °C
 1060 ksi

@Temperature 140 °F
9.50 GPa

@Temperature 23.0 °C
 1380 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 2.50 J/cm²

@Temperature 23.0 °C
 11.9 ft-lb/in²

@Temperature 73.4 °F
2.50 J/cm²

@Temperature -20.0 °C
 11.9 ft-lb/in²

@Temperature -4.00 °F
Charpy Impact, Notched 0.200 J/cm²

@Temperature -20.0 °C
 0.952 ft-lb/in²

@Temperature -4.00 °F
0.300 J/cm²

@Temperature 23.0 °C
 1.43 ft-lb/in²

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 125 °C
257 °F
Deflection Temperature at 0.46 MPa (66 psi) 210 °C
410 °F
Deflection Temperature at 1.8 MPa (264 psi) 165 °C
329 °F
Vicat Softening Point 200 °C

@Load 5.00 kg
 392 °F

@Load 11.0 lb
Flammability, UL94 V-2

@Thickness 3.00 mm
 V-2

@Thickness 0.118 in
V-2

@Thickness 1.50 mm
 V-2

@Thickness 0.0591 in
V-2

@Thickness 0.750 mm
 V-2

@Thickness 0.0295 in
Oxygen Index 28 %
28 %
Glow Wire Test 960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 GWFI/GWT
960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V
A solution
Processing Properties Metric English Comments
Melt Temperature 270 - 290 °C
518 - 554 °F
Mold Temperature 70.0 - 100 °C
158 - 212 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
 194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa