LATI Laril 13 G/20 PPOm, 20% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, 20% Glass Filled
Manufacturer LATI
Trade Name Laril
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Laril 13 G/20 PPOm, 20% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Modified Polyphenylene Oxide (PPOm) based compound. Glass fibers. Low thermal expansion coefficient. Good thermal properties.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.22 g/cc
0.0441 lb/in³
Linear Mold Shrinkage, Flow 0.0040 - 0.0065 cm/cm
0.0040 - 0.0065 in/in
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 25.0 MPa

@Temperature 120 °C
 3630 psi

@Temperature 248 °F
45.0 MPa

@Temperature 90.0 °C
 6530 psi

@Temperature 194 °F
60.0 MPa

@Temperature 60.0 °C
 8700 psi

@Temperature 140 °F
80.0 MPa

@Temperature 23.0 °C
 11600 psi

@Temperature 73.4 °F
Elongation at Break 2.5 %

@Temperature 23.0 °C
 2.5 %

@Temperature 73.4 °F
2.5 %

@Temperature 60.0 °C
 2.5 %

@Temperature 140 °F
2.5 %

@Temperature 90.0 °C
 2.5 %

@Temperature 194 °F
4.0 %

@Temperature 120 °C
 4.0 %

@Temperature 248 °F
Elongation at Yield 1.7 %

@Temperature 120 °C
 1.7 %

@Temperature 248 °F
1.8 %

@Temperature 90.0 °C
 1.8 %

@Temperature 194 °F
2.0 %

@Temperature 60.0 °C
 2.0 %

@Temperature 140 °F
Tensile Modulus 4.20 GPa

@Temperature 120 °C
 609 ksi

@Temperature 248 °F
5.80 GPa

@Temperature 90.0 °C
 841 ksi

@Temperature 194 °F
6.30 GPa

@Temperature 23.0 °C
 914 ksi

@Temperature 73.4 °F
6.30 GPa

@Temperature 60.0 °C
 914 ksi

@Temperature 140 °F
Charpy Impact Unnotched 2.50 J/cm²

@Temperature 23.0 °C
 11.9 ft-lb/in²

@Temperature 73.4 °F
2.50 J/cm²

@Temperature -20.0 °C
 11.9 ft-lb/in²

@Temperature -4.00 °F
Charpy Impact, Notched 0.500 J/cm²

@Temperature -20.0 °C
 2.38 ft-lb/in²

@Temperature -4.00 °F
0.600 J/cm²

@Temperature 23.0 °C
 2.86 ft-lb/in²

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 120 °C
248 °F
Deflection Temperature at 0.46 MPa (66 psi) 135 °C
275 °F
Deflection Temperature at 1.8 MPa (264 psi) 125 °C
257 °F
Vicat Softening Point 140 °C

@Load 5.00 kg
 284 °F

@Load 11.0 lb
Oxygen Index 25 %
25 %
Electrical Properties Metric English Comments
Comparative Tracking Index 225 V
225 V
A solution
Processing Properties Metric English Comments
Melt Temperature 270 - 290 °C
518 - 554 °F
Mold Temperature 80.0 - 90.0 °C
176 - 194 °F
Drying Temperature 80.0 - 90.0 °C

@Time 10800 sec
 176 - 194 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa