LATI Kelon® A H CEG/40 PA 66, Glass/Mineral Reinforced, Heat Stabilized

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass/Mineral Filled
Manufacturer LATI
Trade Name Kelon® A
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Kelon® A H CEG/40 PA 66, Glass/Mineral Reinforced, Heat Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 66 (PA66) based compound. Heat stabilized. Glass fibers / Mineral filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.49 g/cc
0.0538 lb/in³
Linear Mold Shrinkage, Flow 0.0080 - 0.011 cm/cm
0.0080 - 0.011 in/in
Linear Mold Shrinkage, Transverse 0.010 - 0.013 cm/cm
0.010 - 0.013 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 25.0 MPa

@Temperature 150 °C
 3630 psi

@Temperature 302 °F
35.0 MPa

@Temperature 120 °C
 5080 psi

@Temperature 248 °F
45.0 MPa

@Temperature 90.0 °C
 6530 psi

@Temperature 194 °F
70.0 MPa

@Temperature 60.0 °C
 10200 psi

@Temperature 140 °F
90.0 MPa

@Temperature 23.0 °C
 13100 psi

@Temperature 73.4 °F
Elongation at Break 2.9 %

@Temperature 23.0 °C
 2.9 %

@Temperature 73.4 °F
3.5 %

@Temperature 60.0 °C
 3.5 %

@Temperature 140 °F
6.5 %

@Temperature 90.0 °C
 6.5 %

@Temperature 194 °F
8.0 %

@Temperature 120 °C
 8.0 %

@Temperature 248 °F
12 %

@Temperature 150 °C
 12 %

@Temperature 302 °F
Tensile Modulus 2.60 GPa

@Temperature 150 °C
 377 ksi

@Temperature 302 °F
3.70 GPa

@Temperature 120 °C
 537 ksi

@Temperature 248 °F
4.10 GPa

@Temperature 90.0 °C
 595 ksi

@Temperature 194 °F
5.00 GPa

@Temperature 60.0 °C
 725 ksi

@Temperature 140 °F
6.60 GPa

@Temperature 23.0 °C
 957 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 2.50 J/cm²
11.9 ft-lb/in²
Charpy Impact, Notched 0.350 J/cm²
1.67 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 125 °C
257 °F
Deflection Temperature at 0.46 MPa (66 psi) 240 °C
464 °F
Deflection Temperature at 1.8 MPa (264 psi) 180 °C
356 °F
Vicat Softening Point 230 °C

@Load 5.00 kg
 446 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 280 - 310 °C
536 - 590 °F
Mold Temperature 80.0 - 100 °C
176 - 212 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
 194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa