SABIC Innovative Plastics LNP THERMOCOMP RF0039S PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RF0039S PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* RF0039S is a compound based on Nylon 66 resin containing 15% Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant, Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 |
| 1.487 g/cc | 0.05372 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.490 % | 0.490 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0089 cm/cm @Time 86400 sec |
0.0089 in/in @Time 24.0 hour |
ISO 294 |
| 0.0090 cm/cm @Time 86400 sec |
0.0090 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0129 cm/cm @Time 86400 sec |
0.0129 in/in @Time 24.0 hour |
ISO 294 |
| 0.013 cm/cm @Time 86400 sec |
0.013 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 98.0 MPa | 14200 psi | ISO 527 |
| 100 MPa | 14500 psi | ASTM D638 | |
| Elongation at Break | 2.9 % | 2.9 % | ISO 527 |
| 3.0 % | 3.0 % | ASTM D638 | |
| Tensile Modulus | 6.06 GPa | 879 ksi | 50 mm/min; ASTM D638 |
| 6.30 GPa | 914 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 160 MPa | 23200 psi | ASTM D790 |
| 164 MPa | 23800 psi | ISO 178 | |
| Flexural Modulus | 5.17 GPa | 750 ksi | ASTM D790 |
| 6.00 GPa | 870 ksi | ISO 178 | |
| Izod Impact, Notched | 0.420 J/cm | 0.787 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.23 J/cm | 9.80 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 38.0 kJ/m² | 18.1 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 5.00 J | 3.69 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 251 °C @Thickness 3.20 mm |
484 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 219 °C | 426 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 226 °C @Thickness 3.20 mm |
439 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Flammability, UL94 | V-0 @Thickness 1.70 mm |
V-0 @Thickness 0.0669 in |
UL 94 by SABIC-IP |