SABIC Innovative Plastics LNP Faradex EX06464 PEI (Asia Pacific)

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP FARADEX
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Faradex EX06464 PEI (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Faradex* EX06464 is a compound based on Polyetherimide resin containing Stainless Steel. Added features of this material include: Electrically Conductive, EMI/RFI Shielding.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Specific Gravity 1.50 g/cc
1.50 g/cc
ASTM D 792
Density 1.46 g/cc
0.0527 lb/in³
ASTM D 792
1.46 g/cc
0.0527 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0055 cm/cm
0.0055 in/in
SABIC Method
0.0055 cm/cm

@Time 86400 sec
0.0055 in/in

@Time 24.0 hour
ASTM D 955
Linear Mold Shrinkage, Transverse 0.0061 cm/cm
0.0061 in/in
SABIC Method
0.0061 cm/cm

@Time 86400 sec
0.0061 in/in

@Time 24.0 hour
ASTM D 955
Melt Flow 8.0 g/10 min

@Load 5.00 kg,
Temperature 360 °C
8.0 g/10 min

@Load 11.0 lb,
Temperature 680 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
10 g/10 min

@Load 6.60 kg,
Temperature 367 °C
10 g/10 min

@Load 14.6 lb,
Temperature 693 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 100 MPa
14500 psi
ISO 527
100 MPa
14500 psi
5 mm/min; ISO 527
109 MPa
15800 psi
ASTM D 638
110 MPa
16000 psi
Type I, 5 mm/min; ASTM D 638
Elongation at Break 3.1 %
3.1 %
ISO 527
3.1 %
3.1 %
5 mm/min; ISO 527
3.2 %
3.2 %
Type I, 5 mm/min; ASTM D 638
3.4 %
3.4 %
ASTM D 638
Tensile Modulus 5.86 GPa
850 ksi
50 mm/min; ASTM D 638
5.90 GPa
856 ksi
1 mm/min; ISO 527
5.97 GPa
866 ksi
5 mm/min; ASTM D 638
Flexural Strength 197 MPa
28600 psi
ISO 178
199 MPa
28900 psi
ASTM D 790
Flexural Yield Strength 198 MPa
28700 psi
1.3 mm/min, 50 mm span; ASTM D 790
200 MPa
29000 psi
2 mm/min; ISO 178
Flexural Modulus 5.40 GPa
783 ksi
ISO 178
5.47 GPa
793 ksi
2 mm/min; ISO 178
5.85 GPa
848 ksi
1.3 mm/min, 50 mm span; ASTM D 790
5.86 GPa
850 ksi
ASTM D 790
Izod Impact, Notched 0.380 J/cm

@Temperature 23.0 °C
0.712 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 4.96 J/cm

@Temperature 23.0 °C
9.29 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature 23.0 °C
2.38 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 33.0 kJ/m²

@Temperature 23.0 °C
15.7 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1U
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 26.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
14.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
27.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
15.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 51.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
28.3 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
53.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
29.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 203 °C
397 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
201 °C

@Thickness 3.20 mm
394 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Vicat Softening Point 180 °C
356 °F
Rate B/120; ISO 306
Flammability, UL94 V-0

@Thickness 0.440 mm
V-0

@Thickness 0.0173 in
UL 94
Electrical Properties Metric English Comments
Volume Resistivity 9.0 ohm-cm
9.0 ohm-cm
ASTM D 257
Surface Resistance 5.0 - 10000 ohm
5.0 - 10000 ohm
ASTM D 257
10000 - 1.00e+6 ohm
10000 - 1.00e+6 ohm
ROA; IEC 60093
Shielding Effectiveness 55 dB

@Thickness 3.00 mm
55 dB

@Thickness 0.118 in
SABIC Method
55 - 65 dB

@Thickness 3.00 mm
55 - 65 dB

@Thickness 0.118 in
SABIC Method