PolyOne Edgetek® ET3500-5002 BK Acrylonitrile Styrene Acrylate + PC (ASA+PC)

Category Polymer , Thermoplastic , ASA Polymer , Polycarbonate (PC)
Manufacturer PolyOne Corporation
Trade Name Edgetek®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Edgetek® ET3500-5002 BK Acrylonitrile Styrene Acrylate + PC (ASA+PC).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
The Edgetek™ Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for elevated service temperature environments, high-modulus / structural materials for load-bearing and high-strength applications and flame-retardant products. These compounds are based on select engineering thermoplastic resins that are compounded with reinforcing additives such as carbon fiber, glass fiber and glass beads.Information provided by PolyOne
Physical Properties Metric English Comments
Density 1.23 g/cc

@Temperature 23.0 °C
0.0444 lb/in³

@Temperature 73.4 °F
±0.02; ISO 1183
Water Absorption 0.15 %
0.15 %
@ 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0010 - 0.0020 cm/cm
0.0010 - 0.0020 in/in
ASTM D955
Melt Flow 17 - 22 g/10 min

@Load 2.16 kg,
Temperature 300 °C
17 - 22 g/10 min

@Load 4.76 lb,
Temperature 572 °F
ISO 1133
Melt Index of Compound 13 - 16 g/10 min

@Load 21.6 kg,
Temperature 300 °C
13 - 16 g/10 min

@Load 47.6 lb,
Temperature 572 °F
cm³/10min; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 100 MPa

@Thickness 4.00 mm,
Temperature 23.0 °C
14500 psi

@Thickness 0.157 in,
Temperature 73.4 °F
Injection Molded; ISO 527-2/50
Elongation at Break 2.2 %

@Thickness 4.00 mm,
Temperature 23.0 °C
2.2 %

@Thickness 0.157 in,
Temperature 73.4 °F
Injection Molded; ISO 527-2/50
Tensile Modulus 5.90 GPa

@Thickness 4.00 mm,
Temperature 23.0 °C
856 ksi

@Thickness 0.157 in,
Temperature 73.4 °F
Injection Molded; ISO 527-2/1
Charpy Impact Unnotched 3.70 J/cm²

@Temperature 23.0 °C
17.6 ft-lb/in²

@Temperature 73.4 °F
Injection Molded; ISO 179
Charpy Impact, Notched 0.800 J/cm²

@Temperature 23.0 °C
3.81 ft-lb/in²

@Temperature 73.4 °F
Injection Molded; ISO 179
Thermal Properties Metric English Comments
Flammability, UL94 HB
HB
UL 94
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
ASTM D257
Surface Resistance >= 1.00e+14 ohm
>= 1.00e+14 ohm
ASTM D257
Processing Properties Metric English Comments
Melt Temperature 280 - 320 °C
536 - 608 °F
Mold Temperature 82.0 - 110 °C
180 - 230 °F
Drying Temperature 120 °C
248 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Descriptive Properties Value Comments
Features Low Warpage
Filler / Reinforcement Glass Fiber Reinforcement, 12% Filler by Weight
Forms Pellets
Generic Material ASA+PC
Generic Name Acrylonitrile Styrene Acrylate + PC (ASA+PC)
Regional Availability Europe
RoHS Compliance RoHS Compliant