Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Charpy Impact, Notched | 0.790 - 3.50 J/cm² | 3.76 - 16.7 ft-lb/in² | Average value: 1.67 J/cm² Grade Count:12 |
Overview of materials for Polybutylene Terephthalate (PBT), 40% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 40% Glass Fiber Filled". Specific grades with glass content between 35.. |
|||
Charpy Impact, Notched | 1.50 - 3.50 J/cm² @Temperature -20.0 - -20.0 °C |
7.14 - 16.7 ft-lb/in² @Temperature -4.00 - -4.00 °F |
Average value: 1.62 J/cm² Grade Count:2 |
Overview of materials for Polycarbonate, Unreinforced, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Unreinforced, Flame Retardant". Each property range of values reported is minimum and max.. |
|||
Charpy Impact, Notched | 0.800 - 3.50 J/cm² @Temperature -30.0 - -20.0 °C |
3.81 - 16.7 ft-lb/in² @Temperature -22.0 - -4.00 °F |
Average value: 1.75 J/cm² Grade Count:13 |
Overview of materials for Polycarbonate/ASA Alloy, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate/ASA Alloy, Unreinforced". Each property range of values reported is minimum and maximum va.. |
|||
Charpy Impact, Notched | 0.200 - 3.50 J/cm² | 0.952 - 16.7 ft-lb/in² | Average value: 0.743 J/cm² Grade Count:54 |
Overview of materials for Polypropylene with 30% Talc Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 30% Talc Filler". Specific grades with primary filler content between 25% and 34% are.. |
|||
Charpy Impact, Notched | 3.00 - 3.50 J/cm² | 14.3 - 16.7 ft-lb/in² | ISO 179 |
Bulk Molding Compounds tetra-DUR F 4306 Bulk Molding Compound Mechanical high grade standard productTypical Applications - Requiring mechanical strength, abrasion resistance, dimensional stability, electrical insulation, electrostatic dissipation (explosion pr.. |