Overview of materials for Polycarbonate/ASA Alloy, Unreinforced

Category Polymer , Thermoplastic , ASA Polymer , Polycarbonate (PC) , Polycarbonate/ASA Alloy, Unreinforced
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polycarbonate/ASA Alloy, Unreinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate/ASA Alloy, Unreinforced". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.10 - 1.24 g/cc
0.0397 - 0.0448 lb/in³
Average value: 1.15 g/cc Grade Count:67
Water Absorption 0.200 - 0.900 %
0.200 - 0.900 %
Average value: 0.384 % Grade Count:11
Moisture Absorption at Equilibrium 0.150 - 1.00 %
0.150 - 1.00 %
Average value: 0.272 % Grade Count:26
Water Absorption at Saturation 0.600 - 1.00 %
0.600 - 1.00 %
Average value: 0.751 % Grade Count:19
Viscosity 138000 - 138000 cP

@Temperature 260 - 260 °C
138000 - 138000 cP

@Temperature 500 - 500 °F
Average value: 229000 cP Grade Count:1
275000 - 275000 cP

@Temperature 260 - 260 °C
275000 - 275000 cP

@Temperature 500 - 500 °F
Average value: 229000 cP Grade Count:1
275000 - 275000 cP

@Shear Rate 1000 - 1000 1/s
275000 - 275000 cP

@Shear Rate 1000 - 1000 1/s
Average value: 229000 cP Grade Count:1
Linear Mold Shrinkage 0.00300 - 0.00900 cm/cm
0.00300 - 0.00900 in/in
Average value: 0.00557 cm/cm Grade Count:55
Linear Mold Shrinkage, Transverse 0.00500 - 0.00700 cm/cm
0.00500 - 0.00700 in/in
Average value: 0.00600 cm/cm Grade Count:8
Melt Flow 0.700 - 53.5 g/10 min
0.700 - 53.5 g/10 min
Average value: 18.2 g/10 min Grade Count:66
Mechanical Properties Metric English Comments
Hardness, Rockwell R 102 - 116
102 - 116
Average value: 110 Grade Count:16
Hardness, H358/30 63.0 - 98.0 MPa
9140 - 14200 psi
Average value: 86.3 MPa Grade Count:3
Ball Indentation Hardness 95.0 - 120 MPa
13800 - 17400 psi
Average value: 109 MPa Grade Count:7
Tensile Strength, Ultimate 39.0 - 68.0 MPa
5660 - 9860 psi
Average value: 52.0 MPa Grade Count:43
Tensile Strength, Yield 45.5 - 66.0 MPa
6600 - 9570 psi
Average value: 57.9 MPa Grade Count:59
Elongation at Break 5.00 - 160 %
5.00 - 160 %
Average value: 64.8 % Grade Count:46
Elongation at Yield 3.00 - 130 %
3.00 - 130 %
Average value: 6.03 % Grade Count:45
Modulus of Elasticity 2.02 - 3.10 GPa
293 - 450 ksi
Average value: 2.52 GPa Grade Count:36
Flexural Yield Strength 60.0 - 100 MPa
8700 - 14500 psi
Average value: 85.4 MPa Grade Count:49
Flexural Modulus 1.89 - 2.96 GPa
274 - 430 ksi
Average value: 2.47 GPa Grade Count:58
Poissons Ratio 0.280 - 0.360
0.280 - 0.360
Average value: 0.332 Grade Count:5
Shear Modulus 0.900 - 0.980 GPa
131 - 142 ksi
Average value: 0.940 GPa Grade Count:5
Izod Impact, Notched 0.0300 - 14.1 J/cm
0.0562 - 26.5 ft-lb/in
Average value: 4.68 J/cm Grade Count:54
0.500 - 7.20 J/cm

@Temperature -30.0 - 0.000 °C
0.937 - 13.5 ft-lb/in

@Temperature -22.0 - 32.0 °F
Average value: 2.37 J/cm Grade Count:26
0.374 - 0.374 J/cm

@Temperature -30.0 - -30.0 °C
0.701 - 0.701 ft-lb/in

@Temperature -22.0 - -22.0 °F
Average value: 2.37 J/cm Grade Count:1
0.374 - 0.374 J/cm

@Thickness 3.17 - 3.17 mm
0.701 - 0.701 ft-lb/in

@Thickness 0.125 - 0.125 in
Average value: 2.37 J/cm Grade Count:1
Izod Impact, Notched (ISO) 7.00 - 125 kJ/m²
3.33 - 59.5 ft-lb/in²
Average value: 35.4 kJ/m² Grade Count:27
3.00 - 47.0 kJ/m²

@Temperature -30.0 - 0.000 °C
1.43 - 22.4 ft-lb/in²

@Temperature -22.0 - 32.0 °F
Average value: 15.1 kJ/m² Grade Count:26
Charpy Impact Unnotched 1000 J/cm²
4760 ft-lb/in²
Grade Count:7
999.9 - 999.9 J/cm²

@Temperature -30.0 - -30.0 °C
4759 - 4759 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Grade Count:7
Charpy Impact, Notched 0.900 - 12.8 J/cm²
4.28 - 60.9 ft-lb/in²
Average value: 4.09 J/cm² Grade Count:36
0.800 - 3.50 J/cm²

@Temperature -30.0 - -20.0 °C
3.81 - 16.7 ft-lb/in²

@Temperature -22.0 - -4.00 °F
Average value: 1.75 J/cm² Grade Count:13
Dart Drop, Total Energy 7.00 - 50.0 J
5.16 - 36.9 ft-lb
Average value: 37.2 J Grade Count:14
10.0 - 33.0 J

@Temperature -30.0 - -30.0 °C
7.38 - 24.3 ft-lb

@Temperature -22.0 - -22.0 °F
Average value: 21.0 J Grade Count:9
Puncture Energy 45.0 - 45.0 J

@Temperature -30.0 - -30.0 °C
33.2 - 33.2 ft-lb

@Temperature -22.0 - -22.0 °F
Average value: 45.0 J Grade Count:1
Thermal Properties Metric English Comments
CTE, linear 62.0 - 100 µm/m-°C
34.4 - 55.6 µin/in-°F
Average value: 74.0 µm/m-°C Grade Count:33
CTE, linear, Transverse to Flow 62.0 - 95.0 µm/m-°C
34.4 - 52.8 µin/in-°F
Average value: 74.6 µm/m-°C Grade Count:25
Thermal Conductivity 0.170 - 0.250 W/m-K
1.18 - 1.74 BTU-in/hr-ft²-°F
Average value: 0.201 W/m-K Grade Count:11
Maximum Service Temperature, Air 90.0 - 115 °C
194 - 239 °F
Average value: 107 °C Grade Count:6
Hot Ball Pressure Test 85.0 - 130 °C
185 - 266 °F
Average value: 105 °C Grade Count:9
Deflection Temperature at 0.46 MPa (66 psi) 90.0 - 132 °C
194 - 270 °F
Average value: 113 °C Grade Count:44
Deflection Temperature at 1.8 MPa (264 psi) 80.0 - 122 °C
176 - 252 °F
Average value: 97.2 °C Grade Count:54
Vicat Softening Point 96.0 - 146 °C
205 - 295 °F
Average value: 119 °C Grade Count:60
UL RTI, Electrical 50.0 - 90.0 °C
122 - 194 °F
Average value: 70.0 °C Grade Count:4
UL RTI, Mechanical with Impact 50.0 - 90.0 °C
122 - 194 °F
Average value: 70.0 °C Grade Count:4
UL RTI, Mechanical without Impact 50.0 - 90.0 °C
122 - 194 °F
Average value: 70.0 °C Grade Count:4
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+12 - 6.20e+15 ohm-cm
1.00e+12 - 6.20e+15 ohm-cm
Average value: 1.58e+15 ohm-cm Grade Count:11
Surface Resistance 1.00e+10 - 2.40e+16 ohm
1.00e+10 - 2.40e+16 ohm
Average value: 5.49e+15 ohm Grade Count:13
Dielectric Constant 3.00 - 3.40
3.00 - 3.40
Average value: 3.09 Grade Count:6
Dielectric Strength 27.1 - 38.0 kV/mm
688 - 965 kV/in
Average value: 33.3 kV/mm Grade Count:9
Dissipation Factor 0.00600 - 0.0175
0.00600 - 0.0175
Average value: 0.0102 Grade Count:10
Comparative Tracking Index 225 - 600 V
225 - 600 V
Average value: 378 V Grade Count:8