Asia International Enterprise (Hong Kong) 3010F Polybutylene terephthalate

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer Asia Int'l Enterprise (Hong Kong) Limited
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Asia International Enterprise (Hong Kong) 3010F Polybutylene terephthalate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Asia International Enterprise (Hong Kong) Ltd.
Physical Properties Metric English Comments
Specific Gravity 1.30 g/cc

@Temperature 23.0 °C
1.30 g/cc

@Temperature 73.4 °F
ASTM D792
Filler Content 0.00 %
0.00 %
Linear Mold Shrinkage 0.011 - 0.018 cm/cm
0.011 - 0.018 in/in
ASTM D955
Melt Flow 25 g/10 min

@Load 2.16 kg,
Temperature 250 °C
25 g/10 min

@Load 4.76 lb,
Temperature 482 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 60.8 MPa
8820 psi
5mm/min; ASTM D638
Elongation at Break 20 %
20 %
5mm/min; ASTM D638
Flexural Strength 98.1 MPa
14200 psi
2.8mm/min; ASTM D790
Flexural Modulus 2.75 GPa
398 ksi
2.8mm/min; ASTM D790
Izod Impact, Notched 0.392 J/cm

@Thickness 3.17 mm,
Temperature 23.0 °C
0.735 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 80.0 °C
176 °F
ASTM D648
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
Processing Properties Metric English Comments
Middle Barrel Temperature 225 - 245 °C
437 - 473 °F
Cylinder Temperature
Mold Temperature 40.0 - 80.0 °C
104 - 176 °F
Drying Temperature 100 - 120 °C
212 - 248 °F
Dry Time 3 - 5 hour
3 - 5 hour