Polymer Property : Flexural Strength = 98.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Strength 98.0 MPa
14200 psi
ISO 178
Nilit FRIANYL A63 HH-KV15 Nylon 6.6 for injection molding, 15% glass ball reinforced
Nylon 6.6 for injection molding, heat and hydrolysis stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Flexural Strength 98.0 MPa
14200 psi
ISO 178
SABIC Innovative Plastics LNP COLORCOMP DX04401H PC
LNP* COLORCOMP* DX04401H is an unfilled Polycarbonate. Added feature of this grade is: Healthcare.
Flexural Strength 98.0 MPa
14200 psi
ASTM D790
LG Chemical LUCEL EC-610B Electrically Conductive POM, 10% Carbon Black Filled
LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m..
Flexural Strength 98.0 MPa
14200 psi
ASTM D790
Kolon SPESIN® KP212V0BLK Flame Retardant PBT Compound Resin
Flame retardant, BLACKApplications: ConnectorsInformation provided by API-Kolon.
Flexural Strength 98.0 MPa
14200 psi
ASTM D790
Kolon SPESIN® KP513MT25 G/F Reinforced PBT Alloy Resin
High flow, dimensionally stableApplications: Head lamp bezelsInformation provided by API-Kolon.
Flexural Strength 98.0 MPa
14200 psi
ASTM D790
LG Chemical LUPOS GP-2106F General Purpose ABS, 10% Glass Fiber Reinforced, Weather Resistant, Flame Retardant
LUPOS resins are glass fiber reinforced styrene copolymers. LUPOS have improved strength, rigidity and dimensional stability. They offer excellent heat resistance, minimal mold shrinkage and have ..
Flexural Strength 98.0 MPa
14200 psi
ISO 178
Lucite International Diakon® Frost 902 51 Acrylic Polymer
Information provided by Lucite International
Flexural Strength 98.0 MPa
14200 psi
ASTM D790
LG Chemical LUPOY GP-1006F General Purpose Modified PC, Unreinforced, Weather Resistant, Flame Retardant
Among the characteristics of LUPOY polycarbonate resins are excellent mechanical properties, high heat resistance, high impact strength, and dimensional stability.Applications:Automotive: Automotive..
Flexural Strength 98.0 MPa
14200 psi
ASTM D790
SABIC Innovative Plastics LNP STAT-KON DX96717C PC
LNP STAT-KON* DX96717C is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive, Flame Retardant.
Flexural Strength 98.0 MPa
14200 psi
ISO 178
SABIC Innovative Plastics LNP STAT-KON DX96717C PC
LNP STAT-KON* DX96717C is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive, Flame Retardant.
Flexural Strength 98.0 MPa
14200 psi
ISO 178
SABIC Innovative Plastics LNP THERMOCOMP AX04518 ABS
LNP* THERMOCOMP* AX04518 is a compound based on ABS resin containing proprietary filler(s).
Flexural Strength 98.0 MPa
14200 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP CF008 PS
LNP* THERMOCOMP* CF008 is a compound based on Polystyrene resin containing 40% Glass Fiber.
Flexural Strength 98.0 MPa
14200 psi
ISO 178
Styrolution PS 147F GPPS
Styrolution PS 147F is a highly transparent GPPS grade. It gives excellent mechanical and heat resistance properties while providing with easy processability and short cycle time.Medium FlowEasy pro..
Flexural Strength 98.0 MPa
14200 psi
2.0 mm/min; ISO 178
Styron CALIBREâ„¢ 2061-15 Polycarbonate Resin
Overview: CALIBREâ„¢ 2061-15 resin is suitable for steam and ethylene oxide sterilization required by the health care industry. CALIBRE 2061-15 provides excellent heat resistance, impact strength..
Flexural Strength 98.0 MPa
14200 psi
3-point, 2.0 mm/min; ISO 178
Styron CALIBREâ„¢ 2091-15 Polycarbonate Resin
Overview: CALIBREâ„¢ MEGARADâ„¢ 2091 Polycarbonate Resins are designed for single use medical devices (SUDs) that require gamma and electron-beam irradiation and an accelerated schedule for de..
Flexural Strength 98.0 MPa
14200 psi
3-point, 2.0 mm/min; ISO 178
Styron CALIBREâ„¢ MEGARAD 2081-15 Polycarbonate Resin
Overview: CALIBREâ„¢ MEGARAD 2081-15 Polycarbonate resin provides end-users of radiation sterilized medical devices a color closer to the water-clear look of the natural resin. When exposed to hi..
Flexural Strength 98.0 MPa
14200 psi
ISO 178
SABIC Innovative Plastics LNP STAT-KON DD0009PC PC
LNP STAT-KON* DD0009PC is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material include: Electrically Conductive, Flame Retardant.
Flexural Strength 98.0 MPa
14200 psi
ISO 178
SABIC Innovative Plastics LNP STAT-KON DX04462C PC (Asia Pacific)
LNP* STAT-KON* DX04462C is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material include: Clean Compounding System.
Flexural Strength 98.0 MPa
14200 psi
3-point, 2.0 mm/min; ISO 178
Styron CALIBREâ„¢ MEGARAD 2081-HD-15 2 Polycarbonate Resin
Overview: CALIBREâ„¢ MEGARAD 2081 HD-15 2 polycarbonate resin provides end-users of radiation sterilized medical devices a color closer to the water-clear look of the natural resin. When exposed ..
Flexural Strength 98.0 MPa
14200 psi
ISO 178
SABIC Innovative Plastics LNP Thermocomp OF002A PPS (Asia Pacific)
LNP* Thermocomp* OF002A is a compound based on Polyphenylene Sulfide resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region.
Flexural Strength 98.0 MPa
14200 psi
ASTM D790
Plenco 4548 Phenolic, Granular, Transfer Molded
PLENCO 04548 is a heat resistant mineral filled phenolic molding compound, offering fast cure rates and hot rigidity. Type ASTM 5948 CFG, and UL recognized under component file E40654. 04548 is avai..
Flexural Strength 98.0 MPa
14200 psi
ISO 178
Polyplastics Duranex® 2016 Polybutylene Terephthalate (PBT), Standard, FR, UL approved regrind 50%
DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers ..
Flexural Strength 98.0 MPa
14200 psi
ISO 178
Polyram RamTough PZ726 Polycarbonate, Impact Modified, UV Stabilized
An impact modified, UV stabilized polycarbonate for injection molding applications.Information provided by Polyram.
Flexural Strength 98.0 MPa
14200 psi
ASTM D790
Toyobo VYLOPET® EMC407 Non-Reinforced
Applications: Iron's heat insulation plateChair framesHousingsFeatures: WarpagelessImproved processabilityHigh fluidityGood appearanceInformation provided by Toyobo.
Flexural Strength 98.0 MPa
14200 psi
2 mm/min; ISO 178
Covestro Makrolon® 2407 MAS070 Polycarbonate
Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• General purpose• Low..
Flexural Strength 98.0 MPa
14200 psi
2 mm/min; ISO 178
Covestro Makrolon® 3107 MAS167 Polycarbonate
Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• General purpose• Hig..
Flexural Strength 98.0 MPa
14200 psi
2 mm/min; ISO 178
Covestro Makrolon® FU1007 Polycarbonate
Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Furniture applications..
Flexural Strength 98.0 MPa

@Temperature 300 °C
14200 psi

@Temperature 572 °F
Advanced Ceramics ZEMAT® ACL 2090 - Zero Expansion Glass-Ceramic
“Zero Expansion” glass-ceramic is a transparent material now in production for applications requiring ultra-low thermal expansion. The primary crystal phase is a s-eucryptite (Li2OAl2O32SiO2) soli..
Flexural Strength 98.0 MPa
14200 psi
ASTM D790
LG Chemical LUPOY SR-3108F High Flow Modified PC, 10% Mineral Fillers, High Reflectivity, Flame Retardant
Among the characteristics of LUPOY polycarbonate resins are excellent mechanical properties, high heat resistance, high impact strength, and dimensional stability.Applications:Automotive: Automotive..
Flexural Strength 98.0 MPa
14200 psi
ISO 178
Polyplastics Duracon® HP270X Acetal Co-polymer (POM), High stiffness, High flow
DURACON® is a crystalline thermoplastic acetal copolymer. The primary raw material trioxane, a trimer of formaldehyde.The thermoplastic adopts a copolymer structure in which polyoxymethylene (-C-O)..