Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Compressive Strength | 241 MPa @Thickness 6.35 mm |
35000 psi @Thickness 0.250 in |
Flatwise |
Industrial Laminates/Norplex MC603 Paper Base Laminate
(discontinued **) Description: MC603 is constructed from electrical grade of kraft paper and a specially modified phenolic resin system, and is designed to be used in tap changers, coil support plates and terminal pa.. |
|||
Compressive Strength | 241 MPa @Thickness 12.7 mm |
35000 psi @Thickness 0.500 in |
ASTM D695 |
Industrial Laminates/Norplex NP325 Cotton Fabric Description: Linen phenolic laminate with graphite added as a solid lubricant. Linen substrate provides better machining and wear resistance than NP315.Thickness Tested: 0.062", 0.125" and 0.500". |
|||
Compressive Strength | 241 MPa @Thickness 12.7 mm |
35000 psi @Thickness 0.500 in |
ASTM D695 |
Industrial Laminates/Norplex NP342 Cotton Fabric Description: Fine weave canvas phenolic material with fabric construction weight intermediate to NP310 and NP320. Designed for better machining than grade NP310 and lower cost than NP320.Thickness T.. |
|||
Compressive Strength | 241 MPa @Thickness 12.7 mm |
35000 psi @Thickness 0.500 in |
ASTM D695 |
Industrial Laminates/Norplex NP344 Cotton Fabric Description: Fine weave canvas laminate with high temperature phenolic resin and molybdenum disulfide lubricant. Good machining properties and low coefficient of thermal expansion. Better machining .. |
|||
Compressive Strength | 241 MPa @Thickness 12.7 mm |
35000 psi @Thickness 0.500 in |
ASTM D695 |
Industrial Laminates/Norplex NP600 Paper Base Laminate Description: A paper-base laminate with low phenolic resin content for hard, flat surfaces. This material is most commonly used for drill entry material in the PCB industry. Thickness Tested: 0.062".. |
|||
Compressive Strength | 241 MPa @Thickness 12.7 mm |
35000 psi @Thickness 0.500 in |
ASTM D695 |
Industrial Laminates/Norplex NP602 Paper Base Laminate Description: A paper-base laminate with low phenolic resin content for hard, flat surfaces. It is typically hot punched for numerous low voltage, less than 250 volts, electrical applications.Thickne.. |
|||
Compressive Strength | 241 MPa @Thickness 12.7 mm |
35000 psi @Thickness 0.500 in |
ASTM D695 |
Industrial Laminates/Norplex NP605 Paper Base Laminate Description: A paper-base laminate with low phenolic resin content for hard, flat surfaces. This material is normally used in the printed circuit board industry as a backup for the drilling operatio.. |
|||
Compressive Strength | 241 MPa @Thickness 12.7 mm |
35000 psi @Thickness 0.500 in |
ASTM D695 |
Industrial Laminates/Norplex NP610 Paper Base Laminate Description: Phenolic paper based grade for mechanical applications. Good tensile, compressive and flexural strength. Primarily a machining material, but may be hot punched up to .093" thick.Thickne.. |
|||
Compressive Strength | 241 MPa | 35000 psi | ASTM D695 |
Greene Tweed Arlon® 1163 PEEK, Glass Filled Arlon® is a tough, high-temperature, semi-crystalline, thermoplastic presenting a unique combination of mechanical, thermal, chemical and electrical properties. Greene, Tweed uses several proprie.. |
|||
Compressive Strength | 241 MPa | 35000 psi | |
Haysite ETR-FR-C Glass Reinforced Polyester Sheet, Electrical Grade (GPO3) ETR-FR-C meets NEMA GPO-3 requirements and exceeds NEMA in dielectric strength, arc resistance, and track resistance. This U.L. recognized grade is highly flame retardant and low smoke generating. E.. |
|||
Compressive Strength | 241 MPa | 35000 psi | ASTM D695 |
Haysite HCR-125 Vinyl Ester Sheet, Corrosion Resistant HCR-125 is a corrosion resistant vinyl ester sheet created by impregnating fiber glass mat, synthetic surface veil, and inert additives with Derkane 470 resin and catalyst. A compression molded pro.. |
|||
Compressive Strength | 241 MPa | 35000 psi | ASTM D695 |
Sumitomo Bakelite Durez® 32245 Phenolic, Compression Grade Durez 32245 Black Phenolic is a two-stage glass fiber and mineral filled special purpose molding compound. It is especially designed for applications requiring high strength and dimensional stabilit.. |
|||
Compressive Strength | 241 MPa | 35000 psi | ASTM D695 |
Sumitomo Bakelite Durez® 32245 Phenolic, Injection Grade Durez 32245 Black Phenolic is a two-stage glass fiber and mineral filled special purpose molding compound. It is especially designed for applications requiring high strength and dimensional stabilit.. |
|||
Compressive Strength | 241 MPa | 35000 psi | ASTM D695 |
Sumitomo Bakelite Sumikon® PM-9610 Glass-Filled Phenolic, Compression Grade Sumikon PM-9610 is a two stage glass fiber and mineral filled black phenolic special purpose molding compound. It is especially designed for applications requiring high strength and higher dimens.. |
|||
Compressive Strength | 241 MPa | 35000 psi | ASTM D695 |
Sumitomo Bakelite Sumikon® PM-9610 Glass-Filled Phenolic, Injection Grade Sumikon PM-9610 is a two stage glass fiber and mineral filled black phenolic special purpose molding compound. It is especially designed for applications requiring high strength and higher dimens.. |
|||
Compressive Strength | 241 MPa | 35000 psi | |
Cosmic Plastics CP7311 Epoxy Molding Compound Data provided by the manufacturer. |
|||
Compressive Strength | 241 MPa | 35000 psi | |
Cosmic Plastics E4905 Mineral Filled Epoxy Molding Compound, Encapsulated Grade Data provided by the manufacturer. |
|||
Compressive Strength | 241 MPa | 35000 psi | |
Cosmic Plastics E4920 Mineral Filled Epoxy Molding Compound, Encapsulated Grade Data provided by the manufacturer. |
|||
Compressive Strength | 241 MPa | 35000 psi | 45° stress angle |
Cytec Cyply® 1002 Epoxy Fiberglass Composite, Unidirectional CYPLY® 1002 is a cured epoxy composite material based on a unique non-woven parallel filament construction. This type of construction minimizes filament stress abrasion that can shorten fatigue li.. |
|||
Compressive Strength | 241 MPa @Temperature 23.0 °C |
35000 psi @Temperature 73.4 °F |
ASTM D695 |
DuPont Performance Polymers Rynite® 830ER NC010 PET Rynite® 830ER is 30% glass reinforced with excellent high temperature dielectric properties. Class H (180C).Information provided by DuPont Performance Polymers |
|||
Compressive Strength | 241 MPa | 35000 psi | ASTM D695 |
Sumitomo Bakelite North America RX® 647 Fiberglass Reinforced Phenolic RX 643 is a fiberglass reinforced, ammonia-free, phenolic resole compound, with good dimensional stability and good strength at elevated temperatures. Meets ASTM D-5948 Type GPI-10. RX 647 is a fibe.. |