Polymer Property : Compressive Strength = 241 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Compressive Strength	241 MPa @Thickness 6.35 mm	35000 psi @Thickness 0.250 in	Flatwise
Industrial Laminates/Norplex MC603 Paper Base Laminate (discontinued **) Description: MC603 is constructed from electrical grade of kraft paper and a specially modified phenolic resin system, and is designed to be used in tap changers, coil support plates and terminal pa..
Compressive Strength	241 MPa @Thickness 12.7 mm	35000 psi @Thickness 0.500 in	ASTM D695
Industrial Laminates/Norplex NP325 Cotton Fabric Description: Linen phenolic laminate with graphite added as a solid lubricant. Linen substrate provides better machining and wear resistance than NP315.Thickness Tested: 0.062", 0.125" and 0.500".
Compressive Strength	241 MPa @Thickness 12.7 mm	35000 psi @Thickness 0.500 in	ASTM D695
Industrial Laminates/Norplex NP342 Cotton Fabric Description: Fine weave canvas phenolic material with fabric construction weight intermediate to NP310 and NP320. Designed for better machining than grade NP310 and lower cost than NP320.Thickness T..
Compressive Strength	241 MPa @Thickness 12.7 mm	35000 psi @Thickness 0.500 in	ASTM D695
Industrial Laminates/Norplex NP344 Cotton Fabric Description: Fine weave canvas laminate with high temperature phenolic resin and molybdenum disulfide lubricant. Good machining properties and low coefficient of thermal expansion. Better machining ..
Compressive Strength	241 MPa @Thickness 12.7 mm	35000 psi @Thickness 0.500 in	ASTM D695
Industrial Laminates/Norplex NP600 Paper Base Laminate Description: A paper-base laminate with low phenolic resin content for hard, flat surfaces. This material is most commonly used for drill entry material in the PCB industry. Thickness Tested: 0.062"..
Compressive Strength	241 MPa @Thickness 12.7 mm	35000 psi @Thickness 0.500 in	ASTM D695
Industrial Laminates/Norplex NP602 Paper Base Laminate Description: A paper-base laminate with low phenolic resin content for hard, flat surfaces. It is typically hot punched for numerous low voltage, less than 250 volts, electrical applications.Thickne..
Compressive Strength	241 MPa @Thickness 12.7 mm	35000 psi @Thickness 0.500 in	ASTM D695
Industrial Laminates/Norplex NP605 Paper Base Laminate Description: A paper-base laminate with low phenolic resin content for hard, flat surfaces. This material is normally used in the printed circuit board industry as a backup for the drilling operatio..
Compressive Strength	241 MPa @Thickness 12.7 mm	35000 psi @Thickness 0.500 in	ASTM D695
Industrial Laminates/Norplex NP610 Paper Base Laminate Description: Phenolic paper based grade for mechanical applications. Good tensile, compressive and flexural strength. Primarily a machining material, but may be hot punched up to .093" thick.Thickne..
Compressive Strength	241 MPa	35000 psi	ASTM D695
Greene Tweed ArlonÂ® 1163 PEEK, Glass Filled ArlonÂ® is a tough, high-temperature, semi-crystalline, thermoplastic presenting a unique combination of mechanical, thermal, chemical and electrical properties. Greene, Tweed uses several proprie..
Compressive Strength	241 MPa	35000 psi
Haysite ETR-FR-C Glass Reinforced Polyester Sheet, Electrical Grade (GPO3) ETR-FR-C meets NEMA GPO-3 requirements and exceeds NEMA in dielectric strength, arc resistance, and track resistance. This U.L. recognized grade is highly flame retardant and low smoke generating. E..
Compressive Strength	241 MPa	35000 psi	ASTM D695
Haysite HCR-125 Vinyl Ester Sheet, Corrosion Resistant HCR-125 is a corrosion resistant vinyl ester sheet created by impregnating fiber glass mat, synthetic surface veil, and inert additives with Derkane 470 resin and catalyst. A compression molded pro..
Compressive Strength	241 MPa	35000 psi	ASTM D695
Sumitomo Bakelite DurezÂ® 32245 Phenolic, Compression Grade Durez 32245 Black Phenolic is a two-stage glass fiber and mineral filled special purpose molding compound. It is especially designed for applications requiring high strength and dimensional stabilit..
Compressive Strength	241 MPa	35000 psi	ASTM D695
Sumitomo Bakelite DurezÂ® 32245 Phenolic, Injection Grade Durez 32245 Black Phenolic is a two-stage glass fiber and mineral filled special purpose molding compound. It is especially designed for applications requiring high strength and dimensional stabilit..
Compressive Strength	241 MPa	35000 psi	ASTM D695
Sumitomo Bakelite SumikonÂ® PM-9610 Glass-Filled Phenolic, Compression Grade SumikonÂ PM-9610 is a two stage glass fiber and mineral filled black phenolic special purpose molding compound. It is especially designed for applications requiring high strength and higher dimens..
Compressive Strength	241 MPa	35000 psi	ASTM D695
Sumitomo Bakelite SumikonÂ® PM-9610 Glass-Filled Phenolic, Injection Grade SumikonÂ PM-9610 is a two stage glass fiber and mineral filled black phenolic special purpose molding compound. It is especially designed for applications requiring high strength and higher dimens..
Compressive Strength	241 MPa	35000 psi
Cosmic Plastics CP7311 Epoxy Molding Compound Data provided by the manufacturer.
Compressive Strength	241 MPa	35000 psi
Cosmic Plastics E4905 Mineral Filled Epoxy Molding Compound, Encapsulated Grade Data provided by the manufacturer.
Compressive Strength	241 MPa	35000 psi
Cosmic Plastics E4920 Mineral Filled Epoxy Molding Compound, Encapsulated Grade Data provided by the manufacturer.
Compressive Strength	241 MPa	35000 psi	45° stress angle
Cytec Cyply® 1002 Epoxy Fiberglass Composite, Unidirectional CYPLY® 1002 is a cured epoxy composite material based on a unique non-woven parallel filament construction. This type of construction minimizes filament stress abrasion that can shorten fatigue li..
Compressive Strength	241 MPa @Temperature 23.0 °C	35000 psi @Temperature 73.4 °F	ASTM D695
DuPont Performance Polymers Rynite® 830ER NC010 PET Rynite® 830ER is 30% glass reinforced with excellent high temperature dielectric properties. Class H (180C).Information provided by DuPont Performance Polymers
Compressive Strength	241 MPa	35000 psi	ASTM D695
Sumitomo Bakelite North America RX® 647 Fiberglass Reinforced Phenolic RX 643 is a fiberglass reinforced, ammonia-free, phenolic resole compound, with good dimensional stability and good strength at elevated temperatures. Meets ASTM D-5948 Type GPI-10. RX 647 is a fibe..