Industrial Laminates/Norplex MC603 Paper Base Laminate (discontinued **)

Category	Polymer , Thermoset , Phenolic
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Industrial Laminates/Norplex MC603 Paper Base Laminate (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: MC603 is constructed from electrical grade of kraft paper and a specially modified phenolic resin system, and is designed to be used in tap changers, coil support plates and terminal panels for transformers and their accessories.Thickness Tested: 0.250" and0.500"

Physical Properties	Metric	English	Comments
Specific Gravity	1.35 g/cc	1.35 g/cc
Moisture Absorption at Equilibrium	0.94 % @Thickness 6.35 mm	0.94 % @Thickness 0.250 in

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell M	90 - 110	90 - 110
Tensile Strength, Yield	172 MPa @Thickness 6.35 mm	25000 psi @Thickness 0.250 in	LW
Flexural Strength	138 MPa @Thickness 6.35 mm	20000 psi @Thickness 0.250 in	CW
	172 MPa @Thickness 6.35 mm	25000 psi @Thickness 0.250 in	LW
Compressive Strength	241 MPa @Thickness 6.35 mm	35000 psi @Thickness 0.250 in	Flatwise
Izod Impact, Unnotched	0.454 J/cm @Thickness 6.35 mm	0.850 ft-lb/in @Thickness 0.250 in	CW, E-48/50
	1.87 J/cm @Thickness 6.35 mm	3.50 ft-lb/in @Thickness 0.250 in	LW, E-48/50

Thermal Properties	Metric	English
UL RTI, Electrical	140 °C	284 °F
UL RTI, Mechanical without Impact	130 °C	266 °F
Flammability, UL94	HB	HB

Electrical Properties	Metric	English	Comments
Dielectric Strength	5.91 kV/mm @Thickness 3.17 mm	150 kV/in @Thickness 0.125 in	Condition - A Step/Step
Dielectric Breakdown	6000 V @Thickness 6.35 mm	6000 V @Thickness 0.250 in	D-48/50
	>= 70000 V @Thickness 6.35 mm	>= 70000 V @Thickness 0.250 in	Condition A

Descriptive Properties	Value	Comments
Bond Strength	850 lb	0.5"
Power Factor	0.03	ASTM D150
Thermal Index	130/140°C