Polimeri Europa SINKRAL C443 ABS, Heat Stabilized (discontinued **)

Category	Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Polimeri Europa SINKRAL C443 ABS, Heat Stabilized (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Symbol according to ISO 1043-1: ABS Grade designation according to ISO 2580-ABS 1,MG,105-08-25-20 Medium heat injection moulding grade. The availability of different industrial processes to manufacture ABS has permitted the development of SINKRAL C443, which provides an excellent balance between thermal and mechanical properties. Typical applications for this grade are automotive interior parts such as trim and central consoles.Unfilled. Suitable for Injection Molding, Sheet Extrusion, Thermoforming. Supplied as pellets. Contains lubricant and release agent.ISO data. Information provided by EnichemPolimeri Europa now has Enichem's plastics businesses. This grade is no longer in the product line.

Physical Properties	Metric	English	Comments
Density	1.04 g/cc	0.0376 lb/in³
Water Absorption	1.0 %	1.0 %
Moisture Absorption at Equilibrium	0.20 %	0.20 %	Humidity Absorption
Melt Flow	6.0 g/10 min @Load 10.0 kg, Temperature 220 °C	6.0 g/10 min @Load 22.0 lb, Temperature 428 °F	cm³/10 min

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	38.0 MPa	5510 psi	50 mm/min
Elongation at Break	30 %	30 %	Nominal
Elongation at Yield	3.0 %	3.0 %	50 mm/min
Tensile Modulus	2.20 GPa	319 ksi	1 mm/min
Charpy Impact Unnotched	NB	NB
	16.0 J/cm² @Temperature -30.0 °C	76.1 ft-lb/in² @Temperature -22.0 °F
Charpy Impact, Notched	1.80 J/cm²	8.57 ft-lb/in²
	0.900 J/cm² @Temperature -30.0 °C	4.28 ft-lb/in² @Temperature -22.0 °F

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	90.0 µm/m-°C @Temperature 20.0 °C	50.0 µin/in-°F @Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi)	98.0 °C	208 °F
Deflection Temperature at 1.8 MPa (264 psi)	85.0 °C	185 °F
Vicat Softening Point	103 °C	217 °F	50°C/hr; 50N
Glass Transition Temp, Tg	112 °C	234 °F	10°C/min test
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in
	HB @Thickness 3.10 mm	HB @Thickness 0.122 in

Electrical Properties	Metric	English
Electrical Resistivity	1.00e+15 ohm-cm	1.00e+15 ohm-cm
Surface Resistance	1.00e+14 ohm	1.00e+14 ohm
Dielectric Constant	2.8 @Frequency 100 Hz	2.8 @Frequency 100 Hz
	2.9 @Frequency 1e+6 Hz	2.9 @Frequency 1e+6 Hz
Dielectric Strength	30.0 kV/mm	762 kV/in
Dissipation Factor	0.0090 @Frequency 1e+6 Hz	0.0090 @Frequency 1e+6 Hz
	0.010 @Frequency 100 Hz	0.010 @Frequency 100 Hz
Comparative Tracking Index	600 V	600 V