Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® EX1632T PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Lexan* EX1632T polycarbonate resin is designed for use in multi-wall sheet or profile extrusion applications. It contains branched polycarbonate resin, release, and UV stabilizer. It is available in a limited number of colors.
Physical Properties Metric English Comments
Density 1.19 g/cc
0.0430 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 6.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
6.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 57.0 MPa
8270 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 61.0 MPa
8850 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 98.8 %
98.8 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 6.3 %
6.3 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.21 GPa
321 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 99.0 MPa
14400 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.37 GPa
344 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 8.00 J/cm
15.0 ft-lb/in
ASTM D256
1.52 J/cm

@Temperature -30.0 °C
2.85 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Dart Drop, Total Energy 74.0 J

@Temperature 23.0 °C
54.6 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 65.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
36.1 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 66.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
36.7 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 140 °C

@Thickness 3.20 mm
284 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 130 °C

@Thickness 3.20 mm
266 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 145 °C
293 °F
Rate B/50; ASTM D1525
147 °C
297 °F
Rate B/120; ISO 306
Flammability, UL94 HB

@Thickness 0.800 mm
HB

@Thickness 0.0315 in
UL 94 by SABIC-IP