- Unitika B2040G33 PA66, 33% Glass Fiber Reinforced, Dry
Unitika B2040G33 PA66, 33% Glass Fiber Reinforced, Dry
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Unitika |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unitika B2040G33 PA66, 33% Glass Fiber Reinforced, Dry.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.7 % | 1.7 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 3.20 mm |
0.0030 in/in @Thickness 0.126 in |
|
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Thickness 3.20 mm |
0.0080 in/in @Thickness 0.126 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ISO 2039 |
| Tensile Strength at Break | 170 MPa | 24700 psi | ISO 527-1/-2 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-1/-2 |
| Tensile Modulus | 10.0 GPa | 1450 ksi | ISO 527-1/-2 |
| Flexural Strength | 260 MPa | 37700 psi | ISO 178 |
| Flexural Modulus | 9.00 GPa | 1310 ksi | ISO 178 |
| Charpy Impact Unnotched | 7.50 J/cm² | 35.7 ft-lb/in² | ISO 179-1 |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 40.0 µm/m-°C | 22.2 µin/in-°F | ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ISO 75-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 60093 |
| Dielectric Constant | 3.5 @Frequency 1.00e+6 Hz |
3.5 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 35.0 kV/mm @Thickness 1.00 mm |
889 kV/in @Thickness 0.0394 in |
IEC 60243-1 |
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
IEC 60250 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable MJF114A Polyvinyl Chloride, Flexible (PVC, Flexible)
- PolyOne OnFlex™ S KG 70A-3S2019 Thermoplastic Elastomer (TPE)
- Shamrock Technologies Fluoro T® 815 Thermoplastic Grade PTFE Additive
- Cosmic Plastics CP7318 Short Glass Fiber Filled Diallyl Phthalate Molding Compound
- Hexcel® HexWeb® ACG®-1/4 Honeycomb Aluminum Commercial Grade
- Hexcel® HexWeb® CFC™-20-1/8-6.0 Composite Flooring Honeycomb Core
- Fainplast Compounds R 211 Rigid PVC, Extrusion
- Axiall 8644 Moldings & Extrusions Flexible PVC
- Barlog Plastics KEBAFLEX E D 40.1 TPE-V, Shore D40
- 3M FM113 Indoor UL Recognized Brushed Silver Polyester Label Products
Copyright © lookpolymers.com All Rights Reserved