Unitika A3130HR-25 PA6, 25% Mineral Reinforced, Dry

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Mineral Filled
Manufacturer Unitika
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Unitika A3130HR-25 PA6, 25% Mineral Reinforced, Dry.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Unitika Ltd.
Physical Properties Metric English Comments
Density 1.33 g/cc
0.0480 lb/in³
ISO 1183
Water Absorption 1.4 %

@Time 86400 sec
 1.4 %

@Time 24.0 hour
 ISO 62
Moisture Absorption at Equilibrium 2.1 %
2.1 %
50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0060 - 0.010 cm/cm

@Thickness 3.20 mm
 0.0060 - 0.010 in/in

@Thickness 0.126 in
Linear Mold Shrinkage, Transverse 0.0060 - 0.010 cm/cm

@Thickness 3.20 mm
 0.0060 - 0.010 in/in

@Thickness 0.126 in
Mechanical Properties Metric English Comments
Hardness, Rockwell R 119
119
ISO 2039
Tensile Strength at Break 70.0 MPa
10200 psi
ISO 527-1/-2
Elongation at Break 3.5 %
3.5 %
ISO 527-1/-2
Tensile Modulus 5.40 GPa
783 ksi
ISO 527-1/-2
Flexural Strength 108 MPa
15700 psi
ISO 178
Flexural Modulus 4.20 GPa
609 ksi
ISO 178
Charpy Impact Unnotched 5.20 J/cm²
24.7 ft-lb/in²
ISO 179-1
Charpy Impact, Notched 0.300 J/cm²
1.43 ft-lb/in²
ISO 179-1
Thermal Properties Metric English Comments
CTE, linear 50.0 µm/m-°C
27.8 µin/in-°F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 195 °C
383 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 111 °C
232 °F
ISO 75-1/-2
Flammability, UL94 HB

@Thickness 0.750 mm
 HB

@Thickness 0.0295 in