Unitika A3030N-2 PA6, 30% Mineral Reinforced, Conditioned
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Mineral Filled |
| Manufacturer | Unitika |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unitika A3030N-2 PA6, 30% Mineral Reinforced, Conditioned.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.9 % | 1.9 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm @Thickness 3.20 mm |
0.0070 in/in @Thickness 0.126 in |
|
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Thickness 3.20 mm |
0.0080 in/in @Thickness 0.126 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 49.0 MPa | 7110 psi | ISO 527-1/-2 |
| Elongation at Break | 13 % | 13 % | ISO 527-1/-2 |
| Tensile Modulus | 2.00 GPa | 290 ksi | ISO 527-1/-2 |
| Flexural Strength | 52.0 MPa | 7540 psi | ISO 178 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ISO 178 |
| Charpy Impact Unnotched | 5.20 J/cm² | 24.7 ft-lb/in² | ISO 179-1 |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | ISO 179-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 60.0 µm/m-°C | 33.3 µin/in-°F | ISO 11359-2 |
| Flammability, UL94 | V-2 @Thickness 0.850 mm |
V-2 @Thickness 0.0335 in |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PH 49 GF 25 PP, 25% glass fibre, mod. of mech. properties
- PolyOne Versalloy™ HC 9210-70N Thermoplastic Elastomer (TPE)
- Total LDPE LA 0710 Low Density Polyethylene - Extrusion Coating
- Cresset Powers Cress-Alon™ NF3020 2% Nano Clay Loaded, 3.0 r.v. Film Grade Nylon 6, 50% RH
- 3M 4466W Double Coated Polyethylene Foam Tape
- Arlon 55560R030 0.030" (0.762 mm) Uncured Silicone Rubber with Fiberglass Substrate
- DuPont Performance Polymers Minlon® 11C140 NC010 Nylon 66 (Unverified Data**)
- Fainplast Compounds PM 5840 Flexible PVC, Extrusion
- Solvay RHODAPEX® ES-2 Surfactant
- DSM Arnitel® PM581 Polyether Ester Elastomer (European and Asian Grade)
Copyright © lookpolymers.com All Rights Reserved