Unitika A1030GFL PA6, 30% Glass Fiber Reinforced, Dry
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Unitika |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unitika A1030GFL PA6, 30% Glass Fiber Reinforced, Dry.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 |
| Water Absorption | 1.3 % @Time 86400 sec |
1.3 % @Time 24.0 hour |
ISO 62 |
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Thickness 3.20 mm |
0.0020 in/in @Thickness 0.126 in |
|
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Thickness 3.20 mm |
0.0070 in/in @Thickness 0.126 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ISO 2039 |
| Tensile Strength at Break | 170 MPa | 24700 psi | ISO 527-1/-2 |
| Elongation at Break | 3.1 % | 3.1 % | ISO 527-1/-2 |
| Tensile Modulus | 9.60 GPa | 1390 ksi | ISO 527-1/-2 |
| Flexural Strength | 250 MPa | 36300 psi | ISO 178 |
| Flexural Modulus | 8.20 GPa | 1190 ksi | ISO 178 |
| Charpy Impact Unnotched | 7.00 J/cm² | 33.3 ft-lb/in² | ISO 179-1 |
| Charpy Impact, Notched | 1.10 J/cm² | 5.23 ft-lb/in² | ISO 179-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 31.0 µm/m-°C | 17.2 µin/in-°F | ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 217 °C | 423 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 203 °C | 397 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+13 ohm-cm | 2.00e+13 ohm-cm | IEC 60093 |
| Dielectric Constant | 3.3 @Frequency 1.00e+6 Hz |
3.3 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 42.1 kV/mm @Thickness 1.00 mm |
1070 kV/in @Thickness 0.0394 in |
IEC 60243-1 |
| Dissipation Factor | 0.022 @Frequency 1.00e+6 Hz |
0.022 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 550 V | 550 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 255 - 265 °C | 491 - 509 °F | |
| Middle Barrel Temperature | 250 - 260 °C | 482 - 500 °F | |
| Front Barrel Temperature | 230 - 240 °C | 446 - 464 °F | |
| Nozzle Temperature | 255 - 265 °C | 491 - 509 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Back Pressure | 3.00 - 5.00 MPa | 435 - 725 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Primary Pressure | 80-90 MPa | |
| Secondary Pressure | 60-80 MPa |
Users viewing this material also viewed the following:
- S&E Specialty Polymers TufTech™ G-4285-405 Black PVC Compound
- Polimeri Europa Greenflex® FC 45 Ethylene Vinyl Acetate Copolymer - Blown Film Extrusion
- Pyrotek Bonded Particle Filtration Media
- PolyOne Elastamax™ EG-9190 Thermoplastic Elastomer (TPE)
- Parker Chomerics CHO-BOND 2165 Polyurethane Sealant
- Teknor Apex APEX® CX 2001-73 Polyvinyl Chloride, Flexible
- A. Schulman PP 1329 Polypropylene Stabilized Copolymer Polypropylene
- Daikin POLYFLON MG-2060 PTFE 30% Graphite Filled Molding Powder
- DuPont™ Kapton® 200HN Polyimide Film, 50 Micron Thickness
- Hippe PF GC 21 Woven Glass Cloth Reinforced Phenolic Resin - Round, Rolled Tube
Copyright © lookpolymers.com All Rights Reserved