Huntsman IROGRAN® A 78 E 4506 TPU-Polyester
| Category | Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Polyester Grade |
| Manufacturer | Huntsman Corporation |
| Trade Name | IROGRAN® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Huntsman IROGRAN® A 78 E 4506 TPU-Polyester.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Introduction: IROGRAN A 78 E 4506 is a thermoplastic polyester- polyurethane for injection molding and extrusion applications. Additional characteristics of the product are excellent mechanical properties and high tear strength. Performance Features: High production rates Good melt flow Softener-free High oil resistance Dynamically highly loadable Applications: For the production of profiles, spiral hoses, jackets for high pressure hosesInformation provided by Alliance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | Injection molded |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | Injection molded; ASTM D955 |
| Melt Index of Compound | 25 g/10 min @Load 21.6 kg, Temperature 190 °C |
25 g/10 min @Load 47.6 lb, Temperature 374 °F |
MVR, [cm<sup>3</sup>/10 min] |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 80 | 80 | Injection molded parts; ASTM D2240 |
| Hardness, Shore D | 30 | 30 | Injection molded parts; ASTM D2240 |
| Tensile Strength at Break | 50.0 MPa | 7250 psi | Injection molded parts; DIN 53504 |
| Elongation at Break | 700 % | 700 % | Injection molded parts; DIN 53504 |
| 100% Modulus | 0.00440 GPa | 0.638 ksi | Injection molded parts; DIN 53504 |
| 300% Modulus | 0.00800 GPa | 1.16 ksi | Injection molded parts; DIN 53504 |
| Tear Strength | 60.0 kN/m | 342 pli | Injection molded parts; DIN 53515 |
| Abrasion | 25 | 25 | mm<sup>3</sup>, Injection molded; ISO 4649 |
| Compression Set | 21 % @Temperature 22.8 °C, Time 86400 sec |
21 % @Temperature 73.0 °F, Time 24.0 hour |
Injection molded; ASTM D395 |
| 36 % @Temperature 70.0 °C, Time 86400 sec |
36 % @Temperature 158 °F, Time 24.0 hour |
Injection molded; ASTM D395 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 25.0 - 40.0 °C | 77.0 - 104 °F | Extrusion |
| Middle Barrel Temperature | 165 - 190 °C | 329 - 374 °F | Extrusion |
| Nozzle Temperature | 170 - 200 °C | 338 - 392 °F | Extrusion |
| 180 - 200 °C | 356 - 392 °F | Injection | |
| Adapter Temperature | 175 - 195 °C | 347 - 383 °F | Extrusion |
| Die Temperature | 175 - 200 °C | 347 - 392 °F | Extrusion |
| Melt Temperature | 170 - 195 °C | 338 - 383 °F | Injection |
| Mold Temperature | 20.0 - 70.0 °C | 68.0 - 158 °F | Injection |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Heating Zone | 175-195°C | Injection |
Users viewing this material also viewed the following:
- PolyOne Trilliant™ HC HC9820-0030 RS Natural Polyetheretherketone (PEEK)
- Albis Plastics Cellulose Acetate Butyrate B9004 (Odor Mask Added), 10% Plasticizer (discontinued **)
- Saint-Gobain CHR® K100 Polyimide Film Backing Silicone Adhesive Pressure Sensitive Tape
- Teknor Apex Uniprene® UN-2598A Thermoplastic Vulcanizate
- Dow Corning SILASTIC® 24043-V SILICONE RUBBER BLUE
- DuPont™ Tedlar® SP TTR5JSH9 Clear Polyvinyl Fluoride Film
- SABIC Innovative Plastics NORYL EM6100 PPE+PS (Asia Pacific)
- Fainplast Compounds FKA 88/1 Flexible PVC, Flame Retardant Insulation Lead Free
- SK Chemicals SKYTHANE® 375D S series Polyurethane
Copyright © lookpolymers.com All Rights Reserved