Unitika A1025NO PA6, Flame Retardant, Conditioned
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced, Flame Retardant |
| Manufacturer | Unitika |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unitika A1025NO PA6, Flame Retardant, Conditioned.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 |
| Water Absorption | 1.2 % @Time 86400 sec |
1.2 % @Time 24.0 hour |
ISO 62 |
| Moisture Absorption at Equilibrium | 1.9 % | 1.9 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.011 cm/cm @Thickness 3.20 mm |
0.011 in/in @Thickness 0.126 in |
|
| Linear Mold Shrinkage, Transverse | 0.015 cm/cm @Thickness 3.20 mm |
0.015 in/in @Thickness 0.126 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 97 | 97 | ISO 2039 |
| Tensile Strength at Break | 41.0 MPa | 5950 psi | ISO 527-1/-2 |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527-1/-2 |
| Tensile Modulus | 1.80 GPa | 261 ksi | ISO 527-1/-2 |
| Flexural Strength | 60.0 MPa | 8700 psi | ISO 178 |
| Flexural Modulus | 1.50 GPa | 218 ksi | ISO 178 |
| Charpy Impact Unnotched | 5.10 J/cm² | 24.3 ft-lb/in² | ISO 179-1 |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 100 µm/m-°C | 55.6 µin/in-°F | ISO 11359-2 |
| Flammability, UL94 | V-0 @Thickness 0.840 mm |
V-0 @Thickness 0.0331 in |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Flexible Y126 White 317 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Polykemi AB POLYfill PPH GF5020 PB Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled
- Nilit FRIANYL C73 TFGV1530 Nylon 6.6/6 for injection molding, 15% PTFE lubricated, 30% glass fiber reinforced
- Henkel Hysol EA 9309.3NA Paste Adhesive System
- SABIC Innovative Plastics LNP STAT-KON DE0026E PC (Europe-Africa-Middle East)
- Techmer ES HiFill® PA6 GF30 L 30% Glass Filled
- Shuman 720H Black ABS
- BASF Heligoen® Blue 6989 F Color Additive
- ATI Allvac® Nickelvac® 23 UNS N08020 Specialty Steel
- Ineos H13Z-00 Polypropylene Homopolymer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved