SABIC Innovative Plastics Valox® IQ325 PBT (Asia Pacific)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Valox®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Valox® IQ325 PBT (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PBT resin, using chemically recycled post consumer PET Bottles.
Physical Properties Metric English Comments
Specific Gravity 1.34 g/cc
1.34 g/cc
ASTM D792
Density 1.34 g/cc
0.0484 lb/in³
ISO 1183
Moisture Absorption 0.0700 %
0.0700 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.16 %
0.16 %
ISO 62
Linear Mold Shrinkage, Flow 0.016 - 0.024 cm/cm

@Thickness 3.20 mm
0.016 - 0.024 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 23 g/10 min

@Load 2.16 kg,
Temperature 250 °C
23 g/10 min

@Load 4.76 lb,
Temperature 482 °F
ASTM D1238
Melt Index of Compound 21 g/10 min

@Load 2.16 kg,
Temperature 250 °C
21 g/10 min

@Load 4.76 lb,
Temperature 482 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 29.0 MPa
4210 psi
Type I, 50 mm/min; ASTM D638
50.0 MPa
7250 psi
50 mm/min; ISO 527
Tensile Strength, Yield 55.0 MPa
7980 psi
50 mm/min; ISO 527
56.0 MPa
8120 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 14.4 %
14.4 %
50 mm/min; ISO 527
282.4 %
282.4 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 3.0 %
3.0 %
50 mm/min; ISO 527
3.2 %
3.2 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.03 GPa
294 ksi
1 mm/min; ISO 527
2.85 GPa
413 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 80.0 MPa
11600 psi
2 mm/min; ISO 178
84.0 MPa
12200 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.43 GPa
352 ksi
2 mm/min; ISO 178
2.56 GPa
371 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.500 J/cm
0.937 ft-lb/in
ASTM D256
0.460 J/cm

@Temperature -30.0 °C
0.862 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
80*10*4; ISO 180/1A
2.00 kJ/m²

@Temperature -30.0 °C
0.952 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 0.500 J/cm²
2.38 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 61.0 J

@Temperature 23.0 °C
45.0 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 78.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
43.3 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
78.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
43.3 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 81.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
45.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
81.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
45.0 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 48.0 °C
118 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
49.0 °C

@Thickness 3.20 mm
120 °F

@Thickness 0.126 in
unannealed; ASTM D648
58.0 °C

@Thickness 6.40 mm
136 °F

@Thickness 0.252 in
unannealed; ASTM D648
Vicat Softening Point 161 °C
322 °F
Rate B/50; ASTM D1525
165 °C
329 °F
Rate B/120; ISO 306
172 °C
342 °F
Rate B/50; ISO 306