Tra-Con Tra-Bond 342-13ACC Single Component Low Viscosity Epoxy Adhesive
| Category | Polymer , Adhesive , Thermoset , Epoxy |
| Manufacturer | Tra-Con, Inc. |
| Trade Name | Tra-Bond |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Tra-Con Tra-Bond 342-13ACC Single Component Low Viscosity Epoxy Adhesive.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
TRA-BOND 342-13ACC single component, low viscosity epoxy adhesive exhibits high bond strength and excellent thermal shock characteristics. This adhesive may be cured at room temperature in 24 hours or at elevated temperatures. TRA-BOND 342-13ACC adhesive may be used to bond semi-porous materials such as ferrite, where a physical, rather than a chemical, bond is required. Information provided by Tra-Con Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | Mixed |
| Viscosity | 700 cP @Temperature 25.0 °C |
700 cP @Temperature 77.0 °F |
After mixing |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 86 | 86 | |
| Adhesive Bond Strength | 20.7 MPa | 3000 psi | Lap shear, alum to alum, @ 25°C |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.200 W/m-K @Temperature 121 °C |
1.39 BTU-in/hr-ft²-°F @Temperature 250 °F |
|
| Glass Transition Temp, Tg | 99.0 °C | 210 °F | Ultimate Tg |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 9.00e+14 ohm-cm @Temperature 100 °C |
9.00e+14 ohm-cm @Temperature 212 °F |
|
| Dielectric Constant | 4.4 @Frequency 1000 Hz |
4.4 @Frequency 1000 Hz |
|
| Dissipation Factor | 0.0010 @Frequency 1000 Hz |
0.0010 @Frequency 1000 Hz |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 30.0 min @Temperature 120 °C |
0.500 hour @Temperature 248 °F |
|
| 60.0 min @Temperature 95.0 °C |
1.00 hour @Temperature 203 °F |
||
| 120 min @Temperature 65.0 °C |
2.00 hour @Temperature 149 °F |
||
| 1440 min @Temperature 25.0 °C |
24.0 hour @Temperature 77.0 °F |
||
| Shelf Life | 12.0 Month @Temperature -40.0 °C |
12.0 Month @Temperature -40.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Thixotropic Index | 1 | |
| Weight Loss % | 0.85 | At 250°C |
| Working Life hours | 4 | At 25°C |
Users viewing this material also viewed the following:
- LyondellBasell Alathon® L4907 High Density Polyethylene
- Techmer ES Electrablend® POM Acetal
- Spartech 2850-60 PVC for Regulated Applications
- Supreme Petrochem SPEXP 44 Antistatic Polystyrene
- ELASTO UK Dryflex® 660550S SEBS Based Material, Semi-Filled Qualities, 55A Hardness, Natural
- EMS-Griltech Griltex® 9E Copolyester Hotmelt Adhesive (Apparel Interlinings)
- ChevronTexaco HiPerSYN™ ISO 100 Oil
- Arlon R35066R020 0.020" (0.508 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Fainplast Compounds PMP 77 Flexible PVC, Extrusion Modified with PU
Copyright © lookpolymers.com All Rights Reserved