- HOME
- POLYMER SEARCH
- Thermoplastic
- Polycarbonate (PC)
- Polycarbonate, Molded
- Network Polymers NPP 808 C2WW
Network Polymers NPP 808 C2WW
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded |
| Manufacturer | Network Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Network Polymers NPP 808 C2WW.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Polycarbonate AlloyInformation provided by Network Polymers Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | 24 hours at 73°F; ASTM D570 |
| Water Absorption at Saturation | 0.35 % | 0.35 % | 73°F; ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 3.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
| 12 g/10 min @Load 3.80 kg, Temperature 230 °C |
12 g/10 min @Load 8.38 lb, Temperature 446 °F |
Procedure A Condition I; ASTM D1238 | |
| 78 g/10 min @Load 1.20 kg, Temperature 300 °C |
78 g/10 min @Load 2.65 lb, Temperature 572 °F |
Procedure A Condition 0; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 55.2 MPa | 8000 psi | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 2.07 GPa | 300 ksi | Tangent (chs speed 0.05 in/min); ASTM D790 |
| Izod Impact, Notched | NB | NB | Reverse Notched 0.125 in bar; ASTM D256 |
| Gardner Impact | >= 36.2 J @Temperature -18.0 °C |
>= 26.7 ft-lb @Temperature -0.400 °F |
ASTM D5420 |
| >= 36.2 J @Temperature -30.0 °C |
>= 26.7 ft-lb @Temperature -22.0 °F |
ASTM D-5420 | |
| >= 36.2 J @Temperature 23.0 °C |
>= 26.7 ft-lb @Temperature 73.4 °F |
ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 77.8 °C | 172 °F | 0.125 in bar, Unannealed/Conditioned 48 hours; ASTM D648 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 1.0 % | 1.0 % | ASTM D1003 |
| Transmission, Visible | 90 % | 90 % | ASTM D1003 |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 65-8452-1 PP-copolymer, with aramid reinforcement, lubricant modified
- Michelman® Michem® Emulsion 43040 Nonionic polypropylene emulsion
- SolVin 367NC Polyvinyl Chloride Low Viscosity Paste
- Teknor Apex Monprene® MP 1061 Thermoplastic Elastomer
- DuPont Elvanol® 70-30 Polyvinyl Alcohol Fully Hydrolyzed General Purpose Grade
- Dow Corning LSPBK27 SILICONE MASTERBATCH BLACK
- ExxonMobil Escorene™ UL 7521 Ethylene Vinyl Acetate Copolymer
- BASF Novolen® 2448 L Polypropylene
- Mo-Sci Corporation GL-0237 Hollow Glass Spheres
Copyright © lookpolymers.com All Rights Reserved