Teijin Panlite® L-1250Z100 Transparent and Weather Resistant grade Polycarbonate Resin

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded
Manufacturer Teijin
Trade Name Panlite®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Teijin Panlite® L-1250Z100 Transparent and Weather Resistant grade Polycarbonate Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Conforms to SAE regulations. It is an injection molding grade that has normal fluidity and weather resistance and is bluish-tinted to exhibit clear color.Applications:Components of mechanical, electric, electronic, medical, safety and industrial equipment that need clear transparency, heat resistance and weather resistanceInformation provided by Teijin Chemicals Ltd.
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Water Absorption 0.20 %
0.20 %
in water, 23°C, 24h; ISO 62
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm

@Thickness 4.00 mm
 0.0050 - 0.0070 in/in

@Thickness 0.157 in
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm

@Thickness 4.00 mm
 0.0050 - 0.0070 in/in

@Thickness 0.157 in
Melt Flow 9.6 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 9.6 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 61.0 MPa
8850 psi
50mm/min; ISO 527
Elongation at Break >= 50 %
>= 50 %
50mm/min; ISO 527
Elongation at Yield 6.0 %
6.0 %
50mm/min; ISO 527
Tensile Modulus 2.40 GPa
348 ksi
1mm/min; ISO 527
Flexural Strength 93.0 MPa
13500 psi
2mm/min; ISO 178
Flexural Modulus 2.35 GPa
341 ksi
2mm/min; ISO 178
Charpy Impact Unnotched NB
NB
ISO 179
Charpy Impact, Notched 7.60 J/cm²
36.2 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
CTE, linear 70.0 µm/m-°C

@Temperature 20.0 °C
 38.9 µin/in-°F

@Temperature 68.0 °F
 ISO 11359
CTE, linear, Transverse to Flow 70.0 µm/m-°C

@Temperature 20.0 °C
 38.9 µin/in-°F

@Temperature 68.0 °F
 ISO 11359
Deflection Temperature at 0.46 MPa (66 psi) 142 °C
288 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 129 °C
264 °F
ISO 75
Vicat Softening Point 149 °C
300 °F
50°C/hr, 50N; ISO 306
UL RTI, Electrical 125 °C

@Thickness 1.47 mm
 257 °F

@Thickness 0.0579 in
 UL 746B
UL RTI, Mechanical with Impact 115 °C

@Thickness 1.47 mm
 239 °F

@Thickness 0.0579 in
 UL 746B
UL RTI, Mechanical without Impact 125 °C

@Thickness 1.47 mm
 257 °F

@Thickness 0.0579 in
 UL 746B
Flammability, UL94 HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
V-2

@Thickness 0.400 mm
 V-2

@Thickness 0.0157 in
Optical Properties Metric English Comments
Refractive Index 1.585
1.585
ASTM D542
Transmission, Visible 88 %

@Thickness 3.00 mm
 88 %

@Thickness 0.118 in
 ASTM D1003
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
Dielectric Constant 3.0

@Frequency 1e+6 Hz
 3.0

@Frequency 1e+6 Hz
 IEC 60250
3.1

@Frequency 100 Hz
 3.1

@Frequency 100 Hz
 IEC 60250
Dielectric Strength 30.0 kV/mm
762 kV/in
IEC 60243
Dissipation Factor 0.0010

@Frequency 100 Hz
 0.0010

@Frequency 100 Hz
 IEC 60250
0.0090

@Frequency 1e+6 Hz
 0.0090

@Frequency 1e+6 Hz
 IEC 60250
Comparative Tracking Index 250 V
250 V
IEC 60112