SABIC Innovative Plastics SABIC PPCOMPOUND 37T1020 PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | SABIC PPCOMPOUND |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics SABIC PPCOMPOUND 37T1020 PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SABIC® PPcompound 37T1020 is a general purpose, talc filled, heat stabilized copolymer polypropylene compound. This compound exhibits high impact and high flow, and is suitable for injection molding applications. The IMDS ID is 16161338.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 |
| Melt Flow | 13 g/10 min @Load 2.16 kg, Temperature 230 °C |
13 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 71 | 71 | ISO 868 |
| Tensile Strength at Break | 17.0 MPa | 2470 psi | Type I, 50 mm/min; ASTM D638 |
| 25.0 MPa | 3630 psi | 50 mm/min, 1A; ISO 527 | |
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | Type I, 50 mm/min; ASTM D638 |
| 28.0 MPa | 4060 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 32.8 % | 32.8 % | Type I, 50 mm/min; ASTM D638 |
| 45 % | 45 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 3.5 % | 3.5 % | 50 mm/min; ISO 527 |
| 3.7 % | 3.7 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 2.45 GPa | 355 ksi | 50 mm/min; ASTM D638 |
| 2.75 GPa | 399 ksi | 1 mm/min; ISO 527 | |
| Flexural Modulus | 2.35 GPa | 341 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.83 GPa | 410 ksi | 2 mm/min, 64mm span; ISO 178 | |
| Izod Impact, Notched | 0.510 J/cm | 0.955 ft-lb/in | 63.5*12.7*3.2mm, Cut; ASTM D256 |
| Izod Impact, Unnotched | 8.50 J/cm | 15.9 ft-lb/in | 63.5*12.7*3.2mm, Cut; ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4mm, Cut; ISO 180/1A |
| 1.00 kJ/m² @Temperature -30.0 °C |
0.476 ft-lb/in² @Temperature -22.0 °F |
80*10*4mm, Cut; ISO 180/1A | |
| 3.00 kJ/m² @Temperature 0.000 °C |
1.43 ft-lb/in² @Temperature 32.0 °F |
80*10*4mm, Cut; ISO 180/1A | |
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | 80*10*4mm, Cut; ISO 179/1eA |
| 0.100 J/cm² @Temperature -30.0 °C |
0.476 ft-lb/in² @Temperature -22.0 °F |
80*10*4mm, Cut; ISO 179/1eA | |
| Dart Drop, Total Energy | 3.00 J @Temperature 23.0 °C |
2.21 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak, 6.6 m/s; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 66.0 µm/m-°C @Temperature -30.0 - 100 °C |
36.7 µin/in-°F @Temperature -22.0 - 212 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 128 µm/m-°C @Temperature -30.0 - 100 °C |
71.1 µin/in-°F @Temperature -22.0 - 212 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | 80*10*4mm, Cut; ISO 75-1&2 |
| 116 °C @Thickness 3.20 mm |
241 °F @Thickness 0.126 in |
ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 69.0 °C | 156 °F | 80*10*4mm, Cut; ISO 75-1&2 |
| 60.0 °C @Thickness 3.20 mm |
140 °F @Thickness 0.126 in |
ASTM D648 | |
| Vicat Softening Point | 145 °C | 293 °F | 10N, 50°C/hr; ISO 306 |
Users viewing this material also viewed the following:
- MV Labs W850 (NH4)2WO4 Ammonium tungstate, ortho
- SABIC Innovative Plastics Lexan® LCG2007 PC (Asia Pacific)
- Nitriflex NP-2130 Powdered Nitrile
- Microcell Composite Company CELLAMP® 5000 Pellets
- Schott N-LASF9 Glass
- Total PPH 10042 Polypropylene, Homopolymer
- Total PPH 7069 Polypropylene, Homopolymer
- CMW® ELKONITE® 5W3 Tungsten Copper material ASTM B702, Class C, infiltrated
- Victrex® PEEK 450G903 Black Polyetheretherketone, Unreinforced
Copyright © lookpolymers.com All Rights Reserved